A kind of highly wear-resistant nitrile rubber composite cable material and preparation method thereof

A technology of composite cable material and nitrile rubber, applied in rubber insulators, organic insulators, etc., can solve the problems of general physical and mechanical properties, poor wear resistance, and easy to wear

Active Publication Date: 2018-12-04
贵州安众成电线电缆有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] 2. General physical and mechanical properties
[0006] 4. Good water resistance and low air permeability
However, the modified nitrile rubber cable material still has the disadvantage of poor wear resistance, and is easily subject to wear during use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of highly wear-resistant nitrile rubber composite cable material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] High wear-resistant nitrile rubber composite cable material, made of the following components in parts by weight: 100 parts of nitrile rubber, 4 parts of accelerator M, 2.5 parts of antioxidant 1068, 12 parts of antimony trioxide, white carbon 11 parts of black, 1.3 parts of coupling agent A151, 8 parts of dioctyl adipate, 1.1 parts of sulfur, 2.5 parts of antioxidant ODA, 8 parts of modified composite zirconia, 4 parts of zinc oxide, and 2 parts of stearic acid.

[0033] The preparation method of this nitrile rubber composite cable material comprises the following steps:

[0034] (1) Add cerium nitrate hexahydrate to zirconium nitrate trihydrate, stir until evenly mixed, then add citric acid, stir for 30 minutes and heat to 60°C, continue stirring for 5 hours, let stand for 1 hour, place in an oven to dry, Transfer to a high-temperature furnace and heat up to 900°C, calcining for 5 hours, and passing through a 100-mesh sieve after grinding to obtain composite zirconia,...

Embodiment 2

[0039] High wear-resistant nitrile rubber composite cable material, made of the following components in parts by weight: 100 parts of nitrile rubber, 4.4 parts of accelerator M, 2.3 parts of antioxidant 1068, 10 parts of antimony trioxide, white carbon 13 parts of black, 1.5 parts of coupling agent A151, 10 parts of dioctyl adipate, 1.3 parts of sulfur, 2.7 parts of antioxidant ODA, 7 parts of modified composite zirconia, 4 parts of zinc oxide, 2 parts of stearic acid.

[0040] The preparation method of this nitrile rubber composite cable material is the same as that of Example 1.

Embodiment 3

[0042] High wear-resistant nitrile rubber composite cable material, made of the following components in parts by weight: 100 parts of nitrile rubber, 4.2 parts of accelerator M, 2.1 parts of antioxidant 1068, 8 parts of antimony trioxide, white carbon 15 parts of black, 1.1 parts of coupling agent A151, 6 parts of dioctyl adipate, 1.5 parts of sulfur, 2.9 parts of antioxidant ODA, 7.5 parts of modified composite zirconia, 4 parts of zinc oxide, and 2 parts of stearic acid.

[0043] The preparation method of this nitrile rubber composite cable material is the same as that of Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a high-wear-resistance nitrile rubber composite cable material. The high-wear-resistance nitrile rubber composite cable material is prepared from components in parts by weight as follows: 100 parts of nitrile rubber, 4-5 parts of an accelerant, 2-2.5 parts of an antioxidant, 8-13 parts of a fire retardant, 10-15 parts of filler, 1.5-2 parts of a coupling agent, 5-10 parts of a plasticizer, 1-1.5 parts of a vulcanizing agent, 2.5-3 parts of an anti-aging agent, 6-8 parts of modified compound zirconia, 4 parts of zinc oxide and 2 parts of stearic acid. The invention further provides a preparation method of the nitrile rubber composite cable material. The wear resistance of the nitrile rubber composite cable material is very high.

Description

technical field [0001] The invention relates to a cable material, in particular to a highly wear-resistant nitrile rubber composite cable material and a preparation method thereof. Background technique [0002] Nitrile rubber is polymerized from butadiene and acrylonitrile, and can be divided into general-purpose nitrile rubber and special nitrile rubber according to uses. Nitrile rubber has the following properties: [0003] 1. Excellent oil resistance and solvent resistance, the higher the acrylonitrile content, the better the oil resistance [0004] 2. General physical and mechanical properties [0005] 3. Good heat resistance [0006] 4. Good water resistance and low air permeability [0007] 5. It can be mixed with other rubber or plastic to improve the performance of the rubber. [0008] Nitrile rubber can be used alone or mixed with polyvinyl chloride plastic to make oil-resistant electrical insulation sheaths, such as motor lead wires, oil and mine cables, and m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L9/02C08K13/06C08K9/00C08K9/04C08K9/10C08K3/22H01B3/28
CPCC08K3/22C08K3/2279C08K9/00C08K9/04C08K9/10C08K13/06C08K2003/2213C08K2003/2244C08L2201/02C08L2203/202H01B3/28C08L9/02
Inventor 叶青
Owner 贵州安众成电线电缆有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap