Composite high polymer material

A technology of composite polymers and parts by weight, applied in the field of functional materials, can solve the problems of difficult wide application, limited effect, single function, etc., and achieve the effect of simple and easy preparation method, good thermal insulation effect, and high mechanical strength

Inactive Publication Date: 2017-05-31
吴中区穹窿山天仲高分子材料技术研究所
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Traditional thermal insulation materials are mainly to reduce the thermal conductivity and conductivity coefficient. However, the existing domestic thermal insulation coatings on the market have problems such as single function, limited effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Example 1: Preparation of composite polymer material.

[0014] The composite polymer material of this embodiment includes the following components: butyl rubber (molar content of isoprene 1%) 50 kg, styrene-butadiene rubber (molar content of styrene 20%) 5 kg, nitrile rubber (molar content of acrylonitrile 40 kg) %) 5kg, tributyltin chloride 5kg, melamine 3kg, magnesium phosphate 4kg, liquid paraffin 2kg, dimethicone 0.1kg and zinc stearate 1kg.

Embodiment 2

[0015] Example 2: Preparation of composite polymer material.

[0016] The composite polymer material of this embodiment includes the following components: butyl rubber (molar content of isoprene 2%) 80 kg, styrene-butadiene rubber (molar content of styrene 30%) 10 kg, nitrile rubber (molar content of acrylonitrile 30 kg) %) 10kg, tributyltin chloride 8kg, melamine 5kg, magnesium phosphate 6kg, liquid paraffin 5kg, dimethicone 0.5kg and zinc stearate 5kg.

Embodiment 3

[0017] Example 3: Preparation of composite polymer material.

[0018] The composite polymer material of this embodiment includes the following components: butyl rubber (molar content of isoprene 30%) 60 kg, styrene-butadiene rubber (molar content of styrene 30%) 6 kg, nitrile rubber (molar content of acrylonitrile 30 kg) %) 6kg, tributyltin chloride 6kg, melamine 3.5kg, magnesium phosphate 4.5kg, liquid paraffin 3kg, dimethicone 0.2kg and zinc stearate 2kg.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a composite high polymer material. Specifically, the composite high polymer material provided by the invention comprises the following components in parts by weight: 50-80 parts of butyl rubber, 5-10 parts of styrene-butadiene rubber, 5-10 parts of butadiene-acrylonitrile rubber, 5-8 parts of tributyltin chloride, 3-5 parts of melamine, 4-6 parts of magnesium phosphate, 2-5 parts of liquid paraffin, 0.1-0.5 part of dimethyl silicone oil and 1-5 parts of zinc stearate. The composite high polymer material provided by the invention is energy-saving and environment-friendly, high in mechanical strength, high in temperature resistance and good in thermal insulating effect, is not added with any harmful ingredients in a production process, achieves non-toxic, harmless, clean and environment-friendly effects, has a simple and feasible preparation method and is suitable for industrial production.

Description

technical field [0001] The invention belongs to the field of functional materials, and relates to a composite polymer material. Background technique [0002] Traditional thermal insulation materials are mainly based on reducing thermal conductivity and conductivity. However, the existing domestic thermal insulation coatings on the market have problems such as single function, limited effect and short validity period, which are difficult to be widely used. Although imported composite coatings have good effects, However, the price is high, which increases the production cost and is not conducive to large-scale application. SUMMARY OF THE INVENTION [0003] In view of the above situation, the object of the present invention is to provide a composite polymer material. [0004] In order to achieve the above object, the present invention adopts the following technical solutions: [0005] A composite polymer material, comprising the following components in parts by weight: 50-8...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/22C08L9/06C08L9/02C08K13/02C08K5/57C08K5/098C08K3/32C08K5/3492
CPCC08L23/22C08L2201/08C08L2205/02C08L2205/035C08L9/06C08L9/02C08K13/02C08K5/57C08K5/098C08K2003/326C08K5/34922
Inventor 周春毅
Owner 吴中区穹窿山天仲高分子材料技术研究所
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap