A kind of preparation technology of metal glaze carpet tile and metal glaze carpet tile

A preparation process and metal glaze technology, applied in the field of carpet tiles, can solve the problems of poor wear resistance, easy pollution, easy slippage, etc., and achieve the effect of strong paving integrity

Active Publication Date: 2020-02-11
欧阳琦
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Therefore, the technical problem to be solved by the present invention is to overcome the fact that the carpet tiles in the prior art use a single method for glaze decoration, and the single pattern is difficult to achieve the intimate experience brought by the simulated carpet, and it is easy to slip, has poor wear resistance, and is easy to wear. Pollution, easy warping and deformation defects, thereby providing a preparation process for metal glazed carpet tiles and metal glazed carpet tiles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation technology of metal glaze carpet tile and metal glaze carpet tile
  • A kind of preparation technology of metal glaze carpet tile and metal glaze carpet tile

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The raw materials used in this embodiment are composed as follows:

[0033] Components in parts by weight of the bottom glaze: SiO 2 56.58 parts; Al 2 o 3 9.42 parts; Fe 2 o 3 0.01 parts; Ti 2 O 0.01 parts; CaO 5.83 parts; MgO 5.04 parts; K 2 O 9.89 parts; N a2 O 8.79 copies; LOI 5.08 copies.

[0034] Metallic glaze includes components in parts by weight: 40 parts of potassium feldspar; 8 parts of kaolin; 12 parts of lithium feldspar; 15 parts of quartz; 2 parts of vanadium pentoxide; 17 parts of manganese oxide; 4 parts of copper oxide; 1 part of nickel oxide parts; 1 part of fluorite powder.

[0035] Components in parts by weight included in raw materials for adobe of carpet tiles: SiO 2 69.35 parts; Al 2 o 3 17.8 parts; Fe 2 o 3 0.89 parts; TiO 0.09 parts; CaO 0.28 parts; MgO 3.04 parts; K 2 O 3.57 parts; N a2 O 4.84 copies; LOI 4.2 copies.

[0036] Mix the billet with the raw materials and send it to the ball mill for 16 hours and mix it evenly, ...

Embodiment 2

[0041] The raw materials used in this embodiment are composed as follows:

[0042] The bottom glaze includes the following components by weight: SiO 2 50 copies; Al 2 o 3 15 parts; Fe 2 o 3 0.001 parts; Ti 2 O 0.002 parts; CaO 8 parts; MgO 2 parts; K 2 O 5 parts; N a2 O15 copies; LOI 5 copies;

[0043] The metal glaze comprises the following components by weight: 30 parts of potassium feldspar; 7 parts of kaolin; 9 parts of lithium feldspar; 15 parts of quartz; 4 parts of vanadium pentoxide; 10 parts of manganese oxide; 1 part of copper oxide; parts; 0.5 parts of fluorite powder.

[0044] The raw materials for the adobe of carpet tiles include the following components by weight: SiO 2 90 copies; Al 2 o 3 10 parts; Fe 2 o 3 0.5 parts; Ti 2 O 2 parts; CaO 3 parts; MgO 1 part; K 2 O 1 part; N a2 O 8 copies; LOI 9 copies.

[0045] Mix the billet with the raw materials and send them to the ball mill for 12 hours and mix them evenly, then remove iron and sieve...

Embodiment 3

[0050] The raw materials used in this embodiment are composed as follows:

[0051] The bottom glaze includes the following components by weight: SiO 2 60 copies; Al 2 o 3 5 parts; Fe 2 o 3 0.002 parts; Ti 2 O 0.001 part; CaO 1 part; MgO 9 parts; K 2 O 15 parts; N a2 O 5 copies; LOI 1 copy;

[0052] The metallic glaze comprises the following components by weight: 60 parts of potassium feldspar; 13 parts of kaolin; 8 parts of lithium feldspar; 20 parts of quartz; 1 part of vanadium pentoxide; 21 parts of manganese oxide; 8 parts of copper oxide; 3 parts of nickel oxide parts; 0.1 parts of fluorite powder.

[0053] The raw materials for the adobe of carpet tiles include the following components by weight: SiO 2 50 copies; Al 2 o 3 25 parts; Fe 2 o 3 3 parts; Ti 2 O 0.05 parts; CaO 0.2 parts; MgO 6 parts; K 2 O 7 copies; N a2 O 1 copy; LOI 1 copy.

[0054] Mix the billet with the raw materials and send it to the ball mill for 20 hours and mix it evenly, then...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flexural strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a metal glaze carpet tile and a process for preparing the same, and belongs to the technical field of carpet tiles. The process for preparing the metal glaze carpet tile includes applying ground glaze on a green tile for carpet tiles; carrying out pattern decoration on the green tile; printing metal glaze by the aid of screens to form metal glaze lines; burning the green tile at the high temperatures to obtain the metal glaze carpet tile. The metal glaze carpet tile and the process have the advantage that the shortcomings of difficulty in bringing amiable experience of simulated carpets due to the fact that glaze surfaces of carpet tiles in the prior art are decorated by the aid of single techniques and have single decorative patterns, easiness in slipping, contamination and warping deformation and poor abrasion resistance of the carpet tiles in the prior art can be overcome.

Description

technical field [0001] The invention relates to the technical field of carpet tiles, in particular to a process for metal glazed carpet tiles. Background technique [0002] Carpet is an ancient handicraft and traditional foreign trade product in my country. It has a long history of nearly 3,000 years in China. With the advancement of science and technology, machine-made carpets have developed rapidly with the development of modern industry, making carpets, a luxury that was longed for in the past, quickly spread to all walks of life. According to data, carpets are used as soft floor coverings. In economically developed societies such as Europe and the United States, it accounts for about 60% of all floor coverings. [0003] Carpet is a floor covering made of cotton, linen, wool, silk, grass and other natural fibers or chemical synthetic fiber materials, which are knitted, tufted or woven by hand or mechanically. It is one of the arts and crafts categories with a long histo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/00C04B35/14C04B41/89B28B11/00B28B11/04
CPCB28B11/001B28B11/044C03C8/00C04B35/14C04B41/52C04B41/89C04B2235/3201C04B2235/3203C04B2235/3206C04B2235/3208C04B2235/3217C04B2235/3232C04B2235/3272C04B41/504C04B41/5022
Inventor 欧阳琦
Owner 欧阳琦