A kind of transparent anti-impact rigid PVC pellet composition and preparation method thereof
A composition and hard technology, which is applied in the field of transparent impact-resistant rigid PVC pellet composition and its preparation, can solve the problems of high transparency and high impact resistance, improve gloss and light transmittance, and maintain The effect of stability and maintaining light transmittance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0023] Composition formula: 100 parts of PVC, 8 parts of impact modifier ACR, 0 parts of bridging agent vinyl chloride-vinyl acetate-butyl acrylate terpolymer resin, 2 parts of heat stabilizer organotin, plasticizer phthalic acid 2 parts of dioctyl ester, 0.5 part of lubricant stearic acid, 0.2 part of ultramarine blue toner.
[0024] Preparation method: Calculate the required weight of each component according to the weight ratio, and weigh the raw materials of each component according to the calculated result; put each component material into the high-speed mixer, start it for high-speed mixing, first turn on the low-speed mixing, and then start High-speed mixing, control the speed of the mixer to 1200-1400 rpm, and raise the temperature of the material in the machine to 105°C; cool and mature the uniformly mixed material for 12 hours, put it into the extruder for extrusion, and select the extruder screw The length-to-diameter ratio is 20-30, the screw speed is 20-30 rpm, an...
Embodiment 2
[0026] Composition formula: 100 parts of PVC, 10 parts of impact modifier ACR, 2 parts of bridging agent vinyl chloride-vinyl acetate-butyl acrylate terpolymer resin, 2 parts of heat stabilizer organotin, plasticizer phthalic acid 2 parts of dioctyl ester, 0.5 part of lubricant stearic acid, 0.2 part of ultramarine blue toner.
[0027]Preparation method: Calculate the required weight of each component according to the weight ratio, and weigh the raw materials of each component according to the calculated result; put each component material into the high-speed mixer, start it for high-speed mixing, first turn on the low-speed mixing, and then start High-speed mixing, control the speed of the mixer to 1200-1400 rpm, and raise the temperature of the material in the machine to 105°C; cool and mature the uniformly mixed material for 12 hours, put it into the extruder for extrusion, and select the extruder screw The length-to-diameter ratio is 20-30, the screw speed is 20-30 rpm, an...
Embodiment 3
[0029] Composition formula: 100 parts of PVC, 10 parts of impact modifier ACR, 4 parts of bridging agent vinyl chloride-vinyl acetate-butyl acrylate terpolymer resin, 2 parts of heat stabilizer organotin, plasticizer phthalic acid 2 parts of dioctyl ester, 0.5 part of lubricant stearic acid, 0.2 part of ultramarine blue toner.
[0030] Preparation method: Calculate the required weight of each component according to the weight ratio, and weigh the raw materials of each component according to the calculated result; put each component material into the high-speed mixer, start it for high-speed mixing, first turn on the low-speed mixing, and then start High-speed mixing, control the speed of the mixer to 1200-1400 rpm, and raise the temperature of the material in the machine to 105°C; cool and mature the uniformly mixed material for 12 hours, put it into the extruder for extrusion, and select the extruder screw The length-to-diameter ratio is 20-30, the screw speed is 20-30 rpm, a...
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
degree of polymerization | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com