Lightweight noise-reducing semi-aromatic nylon material and preparation method and application thereof

A semi-aromatic nylon and noise reduction technology, applied in the field of semi-aromatic nylon materials and their preparation, can solve the problems of high density and increase the weight of the final product, and achieve the effects of uniform distribution, light weight and good mechanical properties

Inactive Publication Date: 2017-06-20
SHANGHAI GENIUS ADVANCED MATERIAL (GRP) CO LTD
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the plastic modification industry, inorganic minerals such as talc, mica, calcium carbonate, and wollastonite are generally used as filling and reinforcing components, and the rigidity and heat resistance of nylon materials are improved or improved by blending and modification. properties such as plasticity, mold shrinkage, chemical resistance, surface gloss, and flammability to meet the specific requirements of the final plastic product. However, since the density of these inorganic mineral fillers is often higher than that of plastics, they are The addition of mineral fillers to plastics increases the relative weight of the final product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lightweight noise-reducing semi-aromatic nylon material and preparation method and application thereof
  • Lightweight noise-reducing semi-aromatic nylon material and preparation method and application thereof
  • Lightweight noise-reducing semi-aromatic nylon material and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0045]

[0046] A kind of preparation method of lightweight noise-reducing semi-aromatic nylon material, it comprises the steps:

[0047] (1) Mix 60-70 parts of dry semi-aromatic nylon, 0.2-0.5 parts of lubricant, 0.5-1 part of antioxidant, and 0.5-1 part of coupling agent to obtain a premix;

[0048](2) Add the premixed material from the main feeding port of the twin-screw extruder, add 10-20 parts of dry glass microspheres from the first side feeding port of the twin-screw extruder, add 10-30 parts A portion of dry glass fiber is fed from the second side feed port of the twin-screw extruder, melted and extruded and granulated by the twin-screw extruder to obtain a light-weight, noise-reducing semi-aromatic nylon material.

[0049] Wherein, in the step (1), the above-mentioned dried semi-aromatic nylon is obtained by drying the semi-aromatic nylon in a drying oven at 100-120°C for 8-10 hours, and the drying temperature may preferably be 110°C.

[0050] In step (1), the abo...

Embodiment 1

[0064] The content of each component of the lightweight noise-reducing semi-aromatic nylon material of this embodiment is shown in Table 1 below.

[0065] Table 1 The component content table of the lightweight noise-reducing semi-aromatic nylon material of Example 1

[0066]

[0067]

[0068] In Table 1, the parts by weight of semi-aromatic nylon, glass microspheres and glass fibers are the weight after drying (dry weight), the same below.

[0069] The preparation method of the lightweight noise-reducing semi-aromatic nylon material in the present embodiment comprises the steps:

[0070] (1), dry semi-aromatic nylon in a drying oven at 110°C for 8 hours to obtain dry semi-aromatic nylon; dry the glass beads in a drying oven at 90°C for 2 hours to obtain dried glass beads; Dry the fibers in a drying oven at 90°C for 2 hours to obtain dried glass fibers;

[0071] (2), according to the weight part of Table 1, take dry semi-aromatic nylon, lubricant, antioxidant, coupling ...

Embodiment 2

[0076] The content of each component of the lightweight noise-reducing semi-aromatic nylon material of this embodiment is shown in Table 2 below.

[0077] Table 2 The component content table of the lightweight noise-reducing semi-aromatic nylon material of embodiment two

[0078]

[0079] The preparation method of the lightweight noise-reducing semi-aromatic nylon material in the present embodiment comprises the steps:

[0080] (1), dry semi-aromatic nylon in a drying oven at 110°C for 8 hours to obtain dry semi-aromatic nylon; dry the glass beads in a drying oven at 90°C for 2 hours to obtain dried glass beads; Dry the fibers in a drying oven at 90°C for 2 hours to obtain dried glass fibers;

[0081] (2), according to the weight part of Table 2, take dry semi-aromatic nylon, lubricant, antioxidant, coupling agent and mix uniformly, obtain premix;

[0082] (3) Add the premixed material from the main feed port of the twin-screw extruder, add the dry glass beads from the fi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a light-weight noise-reducing semi-aromatic nylon material and its preparation method and application; the nylon material comprises the following components: 60-70 parts of semi-aromatic nylon, 10-20 parts of glass beads, 10-30 parts Glass fiber, 0.2-0.5 part of lubricant, 0.5-1 part of antioxidant and 0.5-1 part of coupling agent; the preparation method comprises: mixing semi-aromatic nylon, lubricant, antioxidant and coupling agent uniformly to obtain Premix, add the premix from the main feeding port of the twin-screw extruder, add glass microspheres and glass fibers from different side feeding ports of the twin-screw extruder, and pass through the twin-screw extruder Melt extrusion and granulation to obtain lightweight noise-reducing semi-aromatic nylon material; the light-weight noise-reducing semi-aromatic nylon material of the present invention also has lighter weight and certain noise reduction while ensuring certain mechanical properties Function, when used to manufacture mechanical parts, it can realize the light weight and vibration and noise reduction functions of the mechanical parts.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and relates to a semi-aromatic nylon material and its preparation method and application. Background technique [0002] Semi-aromatic nylon is prepared by melt polycondensation of dicarboxylic acids with aromatic rings and aliphatic diamines. Due to the introduction of aromatic rings into the main chain of polyamide molecules, its heat resistance and mechanical properties are improved. , and reduces the water absorption, so it is a resin with high heat resistance between the general-purpose engineering plastic nylon and the high-temperature-resistant engineering plastic PEEK. [0003] In the plastic modification industry, inorganic minerals such as talc, mica, calcium carbonate, and wollastonite are generally used as filling and reinforcing components, and the rigidity and heat resistance of nylon materials are improved or improved by blending and modification. A series of properties s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L77/06C08K13/04C08K7/20C08K7/14C08K5/098C08K5/134C08K5/5425
CPCC08K13/04C08K5/098C08K5/1345C08K5/5425C08K7/14C08K7/20C08L2201/08
Inventor 杨桂生李宗仁赵冬云
Owner SHANGHAI GENIUS ADVANCED MATERIAL (GRP) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap