A kind of PET release film applied to oca glue and its production process

A production process and release film technology, applied in the direction of adhesives, film/sheet release liners, film/sheet adhesives, etc. Problems such as poor stability and poor film surface flatness can improve leveling, enhance adhesion and reduce floating dust.

Active Publication Date: 2019-05-24
江阴华美光电科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to overcome the defects of the existing common PET release film, such as poor film surface flatness, poor release force stability, low cleanliness, light transmittance and haze that cannot meet the requirements, Provide a PET release film applied to OCA glue and its production process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of PET release film applied to oca glue and its production process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A PET release film applied to OCA glue, comprising the following components in parts by mass: 3 parts of D120 solvent oil, 8 parts of D30 solvent oil, 4 parts of methyl ethyl ketone, 2 parts of isopropyl alcohol, 0.5 part of silicone oil main agent, Heavy release additive 0.6 part, crosslinking agent 0.05 part, anchoring agent 0.01 part, catalyst 0.02 part.

[0021] The above-mentioned production process of the PET release film applied to OCA glue comprises the following steps:

[0022] 1), paint configuration Mix D120 solvent oil, D30 solvent oil, methyl ethyl ketone and isopropanol, stir at 1200 rpm for 30 minutes, filter with 200 mesh filter, and use within 3 hours;

[0023] 2), the original film treatment includes corona treatment and dust removal treatment; the corona value is greater than 50 during the corona treatment, and the gap between any two points is guaranteed not to exceed 5; thereby enhancing the adhesion of the film surface; the described The dust remo...

Embodiment 2

[0029] A PET release film applied to OCA glue, comprising the following components in parts by mass: 8 parts of D120 solvent oil, 3 parts of D30 solvent oil, 8 parts of methyl ethyl ketone, 0.5 part of isopropyl alcohol, 2 parts of silicone oil main agent, Heavy release additive 0.2 part, crosslinking agent 0.09 part, anchoring agent 0.01 part, catalyst 0.02 part.

[0030] The above-mentioned production process of the PET release film applied to OCA glue comprises the following steps:

[0031] 1), paint configuration Mix D120 solvent oil, D30 solvent oil, methyl ethyl ketone and isopropanol, stir at 1200 rpm for 30 minutes, filter with 200 mesh filter, and use within 3 hours;

[0032] 2), the original film treatment includes corona treatment and dust removal treatment; the corona value is greater than 50 during the corona treatment, and the gap between any two points is guaranteed not to exceed 5; thereby enhancing the adhesion of the film surface; the described The dust remo...

Embodiment 3

[0038] A PET release film applied to OCA glue, comprising the following components in parts by mass: 5 parts of D120 solvent oil, 5 parts of D30 solvent oil, 6 parts of methyl ethyl ketone, 1 part of isopropyl alcohol, 1 part of silicone oil main agent, 0.4 part of heavy release additive, 0.07 part of crosslinking agent, 0.01 part of anchoring agent, and 0.02 part of catalyst.

[0039] The above-mentioned production process of the PET release film applied to OCA glue comprises the following steps:

[0040] 1), paint configuration Mix D120 solvent oil, D30 solvent oil, methyl ethyl ketone and isopropanol, stir at 1200 rpm for 30 minutes, filter with 200 mesh filter, and use within 3 hours;

[0041] 2), the original film treatment includes corona treatment and dust removal treatment; the corona value is greater than 50 during the corona treatment, and the gap between any two points is guaranteed not to exceed 5; thereby enhancing the adhesion of the film surface; the described ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hazeaaaaaaaaaa
transmittivityaaaaaaaaaa
hazeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a production process of a PET release film applied to OCA glue. The production process includes the steps that 1, a coating is prepared, wherein solvent oilD120, solvent oil D30, butanone and isopropanol are mixed to serve as a solvent; 2, a corona value is greater than 50 when a raw film is subjected to corona treatment, and a double-faced dust removal device is used for dust removal processing; 3, a precision coating mode is inverse coating, wherein the coating speed is 40 m / min; 4, drying and curing are performed; 5, material receiving and rolling are performed, wherein the tension during rolling is 230N, the taper is 50%, the pressure of a laminating roller is M: 0.4MPa / G: 0.4 MPa,the pressure of a traction roller is M: 0.2 MPa / G: 0.2 MPa; 6, post-curing treatment is performed at the temperature of 45 DEG C, and curing needs 48 hours. The light transmittance of the production process of the PET release film applied to the OCA glue is 90% or above, the haze is 3.0 or below, the release force stability (normal temperature) is 45 + / - 5 g, no visual particle nor foreign matter does not exist under a hundred times of a magnifying lens, a film surface is flat and free of longitudinal grains, water ripples, cross grains and obvious rainbow stripes, the aging stability is 70g or below, and the residual retention rate is 90% or above.

Description

technical field [0001] The invention relates to the technical field of optical protective films, in particular to a PET release film applied to OCA glue and a production process thereof. Background technique [0002] OCA (Optically Clear Adhesive) is a special adhesive for bonding transparent optical components (such as lenses, etc.). It is required to be colorless and transparent, light transmittance above 90%, good bonding strength, can be cured at room temperature or medium temperature, and has the characteristics of small curing shrinkage. OCA optical adhesive is one of the raw materials for important touch screens. It is made of optical acrylic adhesive without substrate, and then a layer of release film is attached to the upper and lower bottom layers. It is a double-sided adhesive tape without substrate material. This OCA glue must use high-performance PET release film as a carrier during the production and use process. However, due to its unique adhesiveness and s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J7/04C09D183/04C09D7/20C09J7/40C08L67/02
CPCC08J7/0427C08J2367/02C08J2483/04C09D7/20C09D7/40C09D183/04C09J7/401C09J2203/318C09J2483/005
Inventor 王上丹
Owner 江阴华美光电科技有限公司