Anti-yellowing photocuring liquid acrylic glue and preparation method thereof
An acrylic adhesive and anti-yellowing technology, applied in adhesives, non-polymer organic compound adhesives, etc., can solve problems such as aging, easy yellowing, and short service life, and achieve moderate curing speed, convenient operation and control, and production low cost effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0024] Example 1
[0025] A light-cured yellowing-resistant liquid acrylic adhesive, comprising the following raw materials by weight:
[0026] 15 parts of PMMA resin
[0027] 40 parts methyl methacrylate
[0028] Butyl methacrylate 25 parts
[0029] Leveling agent 0.3 parts
[0030] Photoinitiator 0.5 parts.
[0031] The PMMA resin has a melt index of 3.0g / 10min and a density of 1.17g / cm 3 of methyl hydroxymethacrylate.
[0032] The methyl methacrylate is methyl methacrylate with a glass transition temperature of 104° C. and a relative density of 0.938.
[0033] The butyl methacrylate is butyl methacrylate with a glass transition temperature of 26° C. and a relative density of 0.887.
[0034] The photoinitiator is 2-hydroxy-2-methyl-1-phenylacetone.
[0035] A method for preparing a light-cured yellowing-resistant liquid acrylic adhesive. PMMA resin, methyl methacrylate and butyl methacrylate are heated to 65° C., kept at room temperature for 2.5 hours, and then a lig...
Example Embodiment
[0036] Example 2
[0037] A light-cured yellowing-resistant liquid acrylic adhesive, comprising the following raw materials by weight:
[0038] 18 parts of PMMA resin
[0039] 45 parts of methyl methacrylate
[0040] Butyl methacrylate 28 parts
[0041] Leveling agent 0.4 parts
[0042] Photoinitiator 0.8 parts.
[0043] The PMMA resin has a melt index of 3.1g / 10min and a density of 1.18g / cm 3 of methyl hydroxymethacrylate.
[0044] The methyl methacrylate is methyl methacrylate with a glass transition temperature of 104.5° C. and a relative density of 0.939.
[0045] The butyl methacrylate is butyl methacrylate with a glass transition temperature of 26.5° C. and a relative density of 0.888.
[0046] The photoinitiator is composed of 2-hydroxy-2-methyl-1-phenylacetone, 1-hydroxycyclohexyl phenyl ketone and 2,4,6-trimethylbenzoylphenylphosphonate ethyl ester A mixture of 1.5:0.8:1 by weight.
[0047] A method for preparing light-cured yellowing-resistant liquid acrylic...
Example Embodiment
[0048] Example 3
[0049] A light-cured yellowing-resistant liquid acrylic adhesive, comprising the following raw materials by weight:
[0050] 20 parts of PMMA resin
[0051] Methyl methacrylate 50 parts
[0052] Butyl methacrylate 30 parts
[0053] Leveling agent 0.5 part
[0054] Photoinitiator 1.0 part.
[0055] The PMMA resin has a melt index of 3.2g / 10min and a density of 1.19g / cm 3 of methyl hydroxymethacrylate.
[0056] The methyl methacrylate is methyl methacrylate with a glass transition temperature of 105° C. and a relative density of 0.940.
[0057] The butyl methacrylate is butyl methacrylate with a glass transition temperature of 27° C. and a relative density of 0.889.
[0058] The photoinitiator is composed of 2-hydroxy-2-methyl-1-phenylacetone, 1-hydroxycyclohexyl phenyl ketone and 2,4,6-trimethylbenzoylphenylphosphonate ethyl ester A mixture of 2:1:1 by weight.
[0059]A method for preparing a light-cured yellowing-resistant liquid acrylic adhesive. P...
PUM
Property | Measurement | Unit |
---|---|---|
Melt index | aaaaa | aaaaa |
Density | aaaaa | aaaaa |
Glass transition temperature | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap