Formula of artificial stone material

A stone and formula technology, which is applied in the field of artificial stone formula, can solve problems such as poor mechanical properties, general artificial stone properties, and affecting the service life of buildings, and achieve long service life, low manufacturing cost, and good mechanical properties.

Inactive Publication Date: 2017-08-11
SHAANXI SCI TECH UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The raw materials of the existing artificial stone are relatively traditional, which are only made of resin, aluminum powder, pigment and curing agent, resulting in the general performance of artificial stone and poor mechanical properties, which directly affect the service life of the building

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] The formula of this artificial stone comprises the raw material of following parts by weight: 23 parts of phthalic anhydrides, 18 parts of glycols, 25 parts of styrene, 35 parts of agate powder, 25 parts of heavy calcium carbonate, 38 parts of lime powder, 38 parts 1 part quartz stone powder, 1 part glycerin.

Embodiment 2

[0012] The formula of this artificial stone comprises the raw material of following parts by weight: 24 parts of phthalic anhydrides, 15 parts of glycols, 28 parts of styrene, 39 parts of agate powder, 29 parts of ground calcium carbonate, 30 parts of lime powder, 28 parts 1 part quartz stone powder, 2 parts glycerin.

Embodiment 3

[0014] The formula of this artificial stone comprises the raw material of following parts by weight: 29 parts of phthalic anhydrides, 13 parts of glycols, 32 parts of styrene, 48 parts of agate powder, 38 parts of ground calcium carbonate, 25 parts of lime powder, 25 parts 1 part quartz stone powder, 3 parts glycerin.

[0015] The formula of the artificial stone adopts phthalic anhydride, glycol, and styrene as the glue, uses agate powder, heavy calcium carbonate, lime powder, and quartz stone powder as the filler, and uses glycerin as the release agent, so the manufacturing cost is low. But the mechanical properties are good and the service life is long.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a formula of an artificial stone material, and relates to the field of building materials. The formula of the artificial stone material adopts phthalic anhydride, dihydric alcohol and styrene as rubber compounds, adopts agate powder, heavy calcium carbonate, lime powder and quartz stone powder as a filler, and adopts glycerol as a mold release agent. The artificial stone material has the advantages of low manufacturing cost, good mechanical properties and long service life.

Description

technical field [0001] The invention relates to the field of building materials, more specifically, the invention relates to a formula of artificial stone. Background technique [0002] Artificial stone is a common building material. Compared with natural stone, artificial stone is safer and healthier, and has better mechanical properties. The raw materials of the existing artificial stones are relatively traditional, which are only made of resin, aluminum powder, pigment and curing agent, which leads to the general performance of artificial stones and poor mechanical properties, which directly affects the service life of buildings. Contents of the invention [0003] The problem to be solved by the present invention is to provide a formula of artificial stone. [0004] In order to achieve the above object, the technical solution adopted by the present invention is: a formula of artificial stone, which is characterized in that the formula of artificial stone includes the f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/12
CPCC04B28/12C04B24/04C04B24/026C04B24/00C04B14/06C04B14/28
Inventor 孟宏睿
Owner SHAANXI SCI TECH UNIV