Non-alumite gold stamping product and preparation process thereof

An anodized aluminum and bronzing technology, applied in the field of printing bronzing, can solve the problems of bronzing product paste, anodized aluminum wrinkling, poor surface gloss, etc., so as to improve the registration and fit, avoid waste and pollution, and avoid surface unevenness. Effect

Active Publication Date: 2017-08-15
HUCAIS PRINTING
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Anodized aluminum is the main material used in hot stamping, but there are many problems in using anodized aluminum for hot stamping: (1) the reuse rate of anodized aluminum is low, and the waste phenomenon in the production process of hot stamping is serious; (2) the manufacturing process of anodized aluminum can High consumption and serious pollution; (3) The quality of anodized aluminum directly affects the effect of hot stamping. Wrinkles, poor surface gloss, and blurred outlines of graphics and texts in anodized aluminum will directly lead to paste, reverse pull, and hot stamping failure of hot stamping products. The above problems affect the quality of bronzing products; (4) Anodized aluminum bronzing process has a single layer of anodized aluminum foil, and one bronzing process can only be stamped with one effect. If three kinds of laser effect patterns are required, three bronzing processes can be realized. It is impossible to achieve a variety of laser effects in one bronzing process; (5) The customization requirements of anodized aluminum are high, requiring large-scale customization, and the production and procurement cycle is long, resulting in high costs for small-batch and multi-batch production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-alumite gold stamping product and preparation process thereof
  • Non-alumite gold stamping product and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] as attached figure 1 Shown, a kind of electroless aluminum bronzing process comprises the steps:

[0052] A. Preparation of combined version: use high temperature resistant glue to bond hot stamping version 1 and laser nickel version 2 engraved with graphic information 21 with registration to make a combined version;

[0053] B. Paper coating: apply thermoplastic varnish or high-reflective paint to the position of the paper 3 that needs to be bronzed to obtain the coating layer 31;

[0054] C. Coating bronzing: the combined plate prepared in step A is loaded on the machine, and the coated layer 31 prepared in step B is pressed and bronzed to obtain an electroless aluminum bronzing product.

[0055] as attached Figure 1-2 As shown, the middle part of the hot stamping plate 1 is provided with a boss 11, and the graphic information 21 of the laser nickel plate 2 corresponds to the boss 11 of the hot stamping plate 1, and they are aligned and bonded together.

[0056] I...

Embodiment 2

[0074] The difference between this embodiment and above-mentioned embodiment 1 is:

[0075] An electroless aluminum bronzing process, comprising the steps of:

[0076] A. Preparation of combined version: use high temperature resistant glue to bond hot stamping version 1 and laser nickel version 2 engraved with graphic information 21 with registration to make a combined version;

[0077] B. Paper coating: apply thermoplastic varnish or high-reflective paint to the position of the paper 3 that needs to be bronzed to obtain the coating layer 31;

[0078] C. Coating bronzing: the combined plate prepared in step A is loaded on the machine, and the coated layer 31 prepared in step B is pressed and bronzed to obtain an electroless aluminum bronzing product.

[0079] as attached Figure 1-2 As shown, the middle part of the hot stamping plate 1 is provided with a boss 11, and the graphic information 21 of the laser nickel plate 2 corresponds to the boss 11 of the hot stamping plate 1...

Embodiment 3

[0098] The difference between this embodiment and above-mentioned embodiment 1 is:

[0099] A. Preparation of combined version: use high temperature resistant glue to bond hot stamping version 1 and laser nickel version 2 engraved with graphic information 21 with registration to make a combined version;

[0100] B. Paper coating: apply thermoplastic varnish or high-reflective paint to the position of the paper 3 that needs to be bronzed to obtain the coating layer 31;

[0101] C. Coating bronzing: the combined plate prepared in step A is loaded on the machine, and the coated layer 31 prepared in step B is pressed and bronzed to obtain an electroless aluminum bronzing product.

[0102] as attached Figure 1-2 As shown, the middle part of the hot stamping plate 1 is provided with a boss 11, and the graphic information 21 of the laser nickel plate 2 corresponds to the boss 11 of the hot stamping plate 1, and they are aligned and bonded together.

[0103] In the step A, it is sp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
heightaaaaaaaaaa
epoxy valueaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of printing gold stamping, in particular to a non-alumite gold stamping product and a preparation process thereof. The preparation process of the non-alumite gold stamping product comprises the following steps that A, a combination plate is prepared, specifically, a gold stamping plate and a laser nickel plate with graphics and text information being carved are subjected to alignment and laminating through high temperature resistant glue to prepare the combination plate; B, paper is coated, specifically, the position, needing gold stamping, of the paper is coated with thermoplastic light oil or high-reflectivity coating to prepare a coating layer; and C, coating and gold stamping are conducted, specifically, the combination plate prepared in the step A is subjected to lock up and put on a machine, the coating layer prepared in the step B is pressed and subjected to gold stamping, and the non-alumite gold stamping product is prepared. The graphics and text information of the laser nickel plate can be printed on the paper in a hot stamping mode under the condition of no alumite medium, various laser effects can be shown on the paper through one procedure, the production cost is low, durability is good, the customization period is short, safety and environmental friendliness are achieved, and the multi-batch and small-amount production requirements are met.

Description

technical field [0001] The invention relates to the technical field of printing hot stamping, in particular to an electroless aluminum hot stamping product and a preparation process thereof. Background technique [0002] Hot stamping is a printing and decoration process, which is to heat and apply foil to the metal printing plate, and emboss golden characters or patterns on the printed matter. With the rapid development of hot stamping foil and printing and packaging industries, the application of anodized aluminum hot stamping is increasing. more extensive. The traditional anodized aluminum hot stamping heats the anodized aluminum through the hot stamping plate, the peeling layer melts, and then the adhesive layer also melts. During embossing, the adhesive layer is bonded to the substrate, the colored layer is separated from the base layer of the polyester sheet, and the aluminized layer and The colored layer remains on the substrate. [0003] Anodized aluminum is the mai...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B44C1/24B41N1/00B41C1/00C09J163/00C09J11/04C09J11/06C09J11/08
CPCB41C1/00B41N1/00B44C1/24C08K2003/265C08K2003/3045C08L2201/08C08L2205/035C09J11/04C09J11/06C09J11/08C09J163/00C08L55/02C08L23/0853C08L33/04C08K13/02C08K5/13C08K3/26C08K3/34C08K3/36C08K3/30C08K5/36
Inventor 张文雨张能建蔡锋杨晓
Owner HUCAIS PRINTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products