White nitrocellulose finish and preparation method thereof

A white and topcoat technology, applied in the field of nitro white topcoat and its preparation, can solve the problems of poor dispersion, low hardness of nitrowhite topcoat, high production cost, etc., achieve good fineness, reduce production equipment and production processes , the effect of reducing production time

Inactive Publication Date: 2017-08-22
中华制漆(新丰)有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the above-mentioned deficiencies of the prior art, provide a kind of nitro white topcoat and its preparation method, aim to solve the technical problems of low hardness, poor dispersibility and high production cost of the existing nitro white topcoat

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • White nitrocellulose finish and preparation method thereof
  • White nitrocellulose finish and preparation method thereof
  • White nitrocellulose finish and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0028] On the other hand, the embodiment of the present invention also provides a preparation method of nitro white finish paint. This preparation method comprises the steps:

[0029] S01: Weigh the raw materials of each component according to the components contained in the above-mentioned nitro white finish paint and their contents;

[0030] S02: performing the first mixing treatment on the rosin resin, plasticizer, dispersant, defoamer, anti-settling agent and 60-80% alcohol solvent to obtain the first mixed material;

[0031] S03: adding nitrocellulose, titanium dioxide and the remaining alcohol solvent to the above-mentioned first mixed material to perform a second mixed material to obtain a second mixed material;

[0032] S04: adding alkyd resin, leveling agent and 80-90% ester solvent to the second mixed material to perform a third mixed material to obtain a third mixed material;

[0033] S05: Use the remaining ester solvent to adjust the viscosity of the third mixed ...

Embodiment 1

[0041] A kind of nitro white finish paint, its formula sees embodiment 1 in table 1. The preparation method of this nitro white finish paint comprises the steps:

[0042] S11: According to the ingredients contained in the nitro white finish paint of Example 1 in Table 1 and their contents, the raw materials of each ingredient were weighed.

[0043] S12: dissolving the rosin resin into a rosin resin solution with xylene, and performing the first mixing treatment with plasticizer, dispersant, defoamer, anti-settling agent and 80% isopropanol to obtain the first mixed material ; Wherein, the conditions of the first mixing treatment are: the rotating speed is 200rpm-250rpm, and the time is 5min-10min.

[0044] S13: Add nitrocellulose, titanium dioxide and the remaining 20% ​​isopropanol to the above-mentioned first mixed material to perform the second mixed material to obtain the second mixed material, and its fineness is ≤10 μm; wherein, the second mixed material The treatment ...

Embodiment 2

[0048] A kind of nitro white finish paint, its formula sees embodiment 2 in table 1. The preparation method of this nitro white finish paint comprises the steps:

[0049] S21: According to the ingredients contained in the nitro white finish paint of Example 2 in Table 1 and their contents, the raw materials of each ingredient were weighed.

[0050] S22: dissolving the rosin resin into a rosin resin solution with xylene, and performing the first mixing treatment with plasticizer, dispersant, defoamer, anti-settling agent and 75% isopropanol to obtain the first mixed material ; Wherein, the conditions of the first mixing treatment are: the rotating speed is 200rpm-250rpm, and the time is 5min-10min.

[0051] S23: Add nitrocellulose, titanium dioxide and the remaining 25% isopropanol to the above-mentioned first mixed material to perform the second mixed material to obtain the second mixed material, and its fineness is ≤10 μm; wherein, the second mixed material The treatment co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of paint and in particular relates to white nitrocellulose finish and a preparation method thereof. The white nitrocellulose finish is prepared from the following components: 10 percent to 35 percent of nitrocotton, 10 percent to 35 percent of alkyd resin, 8 percent to 10 percent of rosin resin, 5 percent to 15 percent of a plasticizer, 20 percent to 40 percent of titanium white, 0.1 percent to 1 percent of a dispersant, 0.5 percent to 1 percent of a de-foaming agent, 0.5 percent to 1 percent of a flatting agent, 2 percent to 4 percent of an anti-sedimentation agent, 5 percent to 10 percent of an alcohol solvent and 10 percent to 20 percent of an ester solvent. The white nitrocellulose finish provided by the invention has very good fineness and dispersion uniformity and also has very good rigidity; comprehensive properties are remarkably better than those in the prior art. The preparation method has the advantages that a process is simplified, production equipment and production procedures are reduced, the production time is shortened, the production efficiency is improved and the cost is remarkably reduced, so that the preparation method is worthy of being popularized.

Description

technical field [0001] The invention belongs to the technical field of coatings, and in particular relates to a nitro white finish paint and a preparation method thereof. Background technique [0002] Nitro lacquer is a relatively common wood and decoration coating. The main film-forming material of nitro lacquer is mainly composed of nitrocellulose, combined with some soft and hard resins. Nitro topcoat is a kind of nitro paint. The advantages of nitro topcoat are environmental protection and fast drying speed, but the disadvantages are poor yellowing resistance, low plumpness and low hardness. [0003] The existing production method of nitro white topcoat requires grinding to achieve the required fineness and performance of the coating due to the use of titanium dioxide pigment in the formula. Ordinary grinding is completed by a sand machine or a three-roller machine, and the process is complicated , the production time is long, the production cost is high, the efficienc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D101/18C09D167/08C09D193/04C09D7/00C09D7/12C09D7/14
CPCC09D101/18C08K2003/2241C08L2205/03C09D7/20C09D7/61C09D7/80C09D167/08C08L67/08C08L93/04C08K13/02C08K3/22C08L1/18
Inventor 朱会明连剑超
Owner 中华制漆(新丰)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap