Carbonization treatment method of wood plate

A technology of carbonization treatment and wooden boards, which is applied in wood treatment, wood heat treatment, pressurized wood treatment, etc., can solve the problems of affecting performance, incomplete carbonization treatment, and decrease of surface hardness and wear resistance, so as to improve the carbonization rate, The effect of reducing the defective rate and increasing the carbonization rate

Active Publication Date: 2017-09-15
FUNAN NATURE ARTS & CRAFTS
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the existing wood carbonization treatment methods are various, and the performance of the carbonized wood produced has been greatly improved, it still has certain defects, such as the incomplete carbonization treatment of the wood surface in the existing carbonization treatment, which leads to the use of During the process, it will still be attacked by microorganisms, and its surface hardness and wear resistance will decrease after carbonization, which will affect its performance. Therefore, it is necessary to improve the carbonization treatment process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carbonization treatment method of wood plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A carbonization treatment method for wooden boards, comprising the steps of:

[0027] (1) Plate cleaning:

[0028] Classify and cut the boards to be processed according to the design requirements, and then rinse and clean the processed boards with clean water to remove the sand, dirt, wood chips and other impurities on the surface, and finally drain the surface water for later use;

[0029] (2) Surface modification treatment:

[0030] Put the board processed in step (1) into the closed furnace, put it in a graded code according to the size, then spray the atomized water vapor on the surface of the board, and at the same time raise the pressure in the closed furnace to 3.5MPa for joint treatment After 25 minutes, lower the temperature and lower the pressure in the closed furnace, and take out the plate for later use;

[0031] (3) Soaking treatment:

[0032] Put the plate treated in step (2) into the surface treatment solution, soak it for 1 hour and take it out for la...

Embodiment 2

[0045] A carbonization treatment method for wooden boards, comprising the steps of:

[0046] (1) Plate cleaning:

[0047] Classify and cut the boards to be processed according to the design requirements, and then rinse and clean the processed boards with clean water to remove the sand, dirt, wood chips and other impurities on the surface, and finally drain the surface water for later use;

[0048] (2) Surface modification treatment:

[0049] Put the board processed in step (1) into the closed furnace, put it in a graded code according to the size, then spray the atomized water vapor on the surface of the board, and at the same time raise the pressure in the closed furnace to 3.8MPa for joint treatment After 30 minutes, lower the temperature and lower the pressure in the closed furnace, and take out the plate for later use;

[0050] (3) Soaking treatment:

[0051] Put the plate treated in step (2) into the surface treatment solution, soak the plate for 1.5 hours and take it ...

Embodiment 3

[0064] A carbonization treatment method for wooden boards, comprising the steps of:

[0065] (1) Plate cleaning:

[0066] Classify and cut the boards to be processed according to the design requirements, and then rinse and clean the processed boards with clean water to remove the sand, dirt, wood chips and other impurities on the surface, and finally drain the surface water for later use;

[0067] (2) Surface modification treatment:

[0068] Put the board processed in step (1) into the closed furnace, put it in a graded code according to the size, and then spray the atomized water vapor on the surface of the board, and at the same time raise the pressure in the closed furnace to 4.0MPa for joint treatment After 35 minutes, lower the temperature and lower the pressure in the closed furnace, and take out the plate for later use;

[0069] (3) Soaking treatment:

[0070] Put the plate treated in step (2) into the surface treatment solution, soak the plate for 2 hours and take i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a carbonization treatment method of a wood plate. The carbonization treatment method comprises the following steps of (1) plate cleaning, (2) surface modification treatment, (3) soaking treatment, (4) carbonization treatment, and (5) cooling treatment. According to the carbonization treatment method, the carbonization effect on the wood plate can be effectively improved, the thickness of a surface carbonization layer of the wood plate is effectively increased, the carbonization rate of a surface layer material of the wood plate is also well increased, meanwhile, reasonably-added nanometer silica enhances the density and mechanical property of the surface layer, the machining defective rate is obviously decreased, and good service value is achieved.

Description

technical field [0001] The invention belongs to the technical field of wood processing, and in particular relates to a carbonization treatment method for wood boards. Background technique [0002] Wood is one of the essential substances in people's life. In order to enhance the performance of wood, it is sometimes necessary to carbonize wood. After the wood is carbonized at high temperature, it not only makes the surface more beautiful, but also has the advantages of anti-corrosion, anti-biological attack, anti-deformation and cracking, and high temperature resistance. It also has the advantages of low moisture content, not easy to absorb water, stable material, and no deformation. , complete degreasing without grease, good heat insulation performance, no special smell and so on. Although the existing wood carbonization treatment methods are various, and the performance of the carbonized wood produced has been greatly improved, it still has certain defects, such as the inco...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27M1/06B27M1/08B27K5/00B27K3/02B27K3/00B27K3/52
CPCB27K3/007B27K3/0207B27K3/52B27K5/007B27K5/0085B27K2240/15B27K2240/20B27M1/06B27M1/08
Inventor 马魁潘光灿马之广马军
Owner FUNAN NATURE ARTS & CRAFTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap