Rapid synthesis method for high-purity zeolite molecular sieve

A zeolite molecular sieve, high-purity technology, applied in molecular sieves and alkali exchange compounds, chemical instruments and methods, inorganic chemistry, etc., can solve problems such as poor repeatability, and achieve the effect of high crystallinity and simple and easy method.

Active Publication Date: 2017-09-15
安徽纳蓝环保科技有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, the repeatability is poor, and the mixed phase of MWW type and CHA type zeolite molecular sieve often occurs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rapid synthesis method for high-purity zeolite molecular sieve
  • Rapid synthesis method for high-purity zeolite molecular sieve

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A kind of method for rapidly synthesizing high-purity zeolite molecular sieve that the present invention proposes, comprises the following steps:

[0027] S1. Mix N,N,N-trimethyl-1-adamantyl ammonium hydroxide with deionized water, stir, then add aluminum source, then add tetraethyl orthosilicate to obtain initial gel mixture, and then The initial gel mixture is thermostated and cooled;

[0028] S2. The product obtained in S1 is washed, dried, and then calcined to obtain a high-purity zeolite molecular sieve.

Embodiment 2

[0030] A kind of method for rapidly synthesizing high-purity zeolite molecular sieve that the present invention proposes, comprises the following steps:

[0031] S1. Mix 11.5 parts by weight of N,N,N-trimethyl-1-adamantyl ammonium hydroxide with 2 parts of deionized water, stir magnetically for 4 minutes, then add 0.1 part of aluminum source, continue stirring for 25 minutes, and then Add 4 parts of tetraethyl orthosilicate, continue to stir for 4 minutes to obtain the initial gel mixture, and then carry out constant temperature treatment at 150°C for 7 days;

[0032] S2. The product obtained in S1 was washed with deionized water, dried at 85° C., and then calcined at 540° C. for 8.5 hours to obtain a zeolite molecular sieve.

Embodiment 3

[0034] A kind of method for rapidly synthesizing high-purity zeolite molecular sieve that the present invention proposes, comprises the following steps:

[0035] S1. Mix 13.5 parts by weight of N,N,N-trimethyl-1-adamantyl ammonium hydroxide with 3 parts of deionized water, stir magnetically for 7 minutes, then add 0.5 parts of aluminum source, continue stirring for 35 minutes, and then Add 4 parts of tetraethyl orthosilicate, continue to stir for 7 minutes to obtain the initial gel mixture, and then carry out constant temperature treatment at 170°C for 5 days;

[0036] S2. The product obtained in S1 was washed with deionized water, dried at 95° C., and then calcined at 570° C. for 7.5 hours to obtain a zeolite molecular sieve.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a rapid synthesis method for a high-purity zeolite molecular sieve. The rapid synthesis method comprises the following steps: S1, mixing N,N,N-trimethyl-1-adamantyl ammonium hydroxide with deionized water, stirring, then adding an aluminum source, then adding tetraethoxysilane to obtain an initial gel mixture, then carrying out constant temperature treatment on the initial gel mixture, and cooling; and S2, washing a product obtained in the S1, drying, and then carrying out calcination treatment to obtain the high-purity zeolite molecular sieve. According to the rapid synthesis method for the high-purity zeolite molecular sieve provided by the invention, the method is simple and practicable and easy to operate, and the purity of the obtained zeolite molecular sieve is high.

Description

technical field [0001] The invention relates to the technical field of zeolite molecular sieves, in particular to a method for rapidly synthesizing high-purity zeolite molecular sieves. Background technique [0002] Because the organic templates used are similar, in the existing process of synthesizing MWW-type and CHA-type zeolite molecular sieves, the product is generally a mixture of the two zeolites. In order to obtain high-purity MWW or CHA zeolite molecular sieves, various parameters of synthesis must be strictly controlled to avoid very low repeatability. In this synthesis method, high-purity MWW-type or CHA-type zeolite can be obtained by using the aluminum raw material used in conditional synthesis without changing other synthesis conditions. Synthetic zeolite molecular sieves play an important role in petrochemical and motor vehicle exhaust gas treatment. In the prior art, the repeatability is poor, and a mixed phase of MWW type and CHA type zeolite molecular sie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B39/48
CPCC01B39/48C01P2002/72C01P2006/80
Inventor 李超范炜田炜
Owner 安徽纳蓝环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com