High-strength expansive agent used for oil-well cement
An oil well cement and high-strength technology, which is applied in the field of expansion agent, can solve the problems that the performance of cement can not meet the actual use needs, the strength of oil well cement is not high, and the performance does not meet the actual use needs, etc., and achieves high strength and high temperature stability. , Good anti-penetration effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0023] The high-strength expansion agent used for oil well cement of the present invention includes the following components in parts by weight: 40 parts of sulfonyl hydrazide compounds, 26 parts of magnesium oxide, 23 parts of butadiene-styrene, 21 parts of slag, 12 parts of graphite powder, 7 parts of calcium silicate, 2 parts of styrene-butadiene rubber emulsion, 8 parts of cement waterproofing agent, and 17 parts of calcium oxide. The sulfonylhydrazide compound is one or more of benzenesulfonylhydrazide, benzenesulfonylhydrazide, and 3,3-disulfonylhydrazide diphenylsulfone. The slag is the slag mainly composed of aluminosilicate material in the steelmaking blast furnace, and its activity is more than 80%. The graphite powder is flake graphite powder.
[0024] After the expansion agent prepared in Example 1 is evenly mixed with cement, nitrogen gas will be released when the temperature reaches 35°C under alkaline conditions, and the tiny bubbles can be evenly distributed i...
Embodiment 2
[0026] The high-strength expansion agent used for oil well cement of the present invention comprises the following components in parts by weight: 25 parts of sulfonyl hydrazide compounds, 10 parts of magnesium oxide, 5 parts of butadiene-styrene, 2 parts of slag, 1 part of graphite powder, 2 parts of calcium silicate, 0.4 part of styrene-butadiene rubber emulsion, 2 parts of cement waterproofing agent, 7 parts of calcium oxide. The sulfonylhydrazide compound is one or more of benzenesulfonylhydrazide, benzenesulfonylhydrazide, and 3,3-disulfonylhydrazide diphenylsulfone. The slag is the slag mainly composed of aluminosilicate material in the steelmaking blast furnace, and its activity is more than 80%. The graphite powder is flake graphite powder.
[0027] The value range of the components of the expansion agent prepared in Example 2 is outside the value range of the present invention, and it and the prepared expansion agent begin to release nitrogen when the temperature reac...
Embodiment 3
[0029] The high-strength expansion agent used for oil well cement of the present invention includes the following components in parts by weight: 55 parts of sulfonyl hydrazide compounds, 35 parts of magnesium oxide, 38 parts of butadiene-styrene, 36 parts of slag, 28 parts of graphite powder, 24 parts of calcium silicate, 12 parts of styrene-butadiene rubber emulsion, 19 parts of cement waterproofing agent, 37 parts of calcium oxide. The sulfonylhydrazide compound is one or more of benzenesulfonylhydrazide, benzenesulfonylhydrazide, and 3,3-disulfonylhydrazide diphenylsulfone. The slag is the slag mainly composed of aluminosilicate material in the steelmaking blast furnace, and its activity is more than 80%. The graphite powder is flake graphite powder.
[0030] The value range of the components of the expansion agent prepared in Example 3 is outside the value range of the present invention, and it and the prepared expansion agent begin to release nitrogen when the temperatur...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap