Environment-friendly type stainless steel polishing liquid and preparation method and polishing technology thereof

A technology of stainless steel and polishing liquid, applied in the field of metal surface treatment, can solve the problems of large amount of waste liquid treatment, high production cost, difficult to control process parameters, etc.

Active Publication Date: 2017-10-27
佛山市顺德区亚特祥展洗涤剂有限公司
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Commercially available polishing liquid mainly has the following types: sulfuric acid type chemical polishing liquid, phosphoric acid type chemical polishing liquid, dichromic acid and its salt series, hydrogen peroxide series, each type of polishing liquid has its own advantages, For example, sulfuric acid polishing liquid is easy to meet the requirements of environmental protection because it does not volatilize and produce smoke. Phosphoric acid can form a mucous film on the me

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly type stainless steel polishing liquid and preparation method and polishing technology thereof
  • Environment-friendly type stainless steel polishing liquid and preparation method and polishing technology thereof
  • Environment-friendly type stainless steel polishing liquid and preparation method and polishing technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A kind of environment-friendly stainless steel polishing fluid is characterized in that described polishing fluid comprises:

[0034] Strong oxidizing agent: NaNO 3 40g / L, HNO 3 10ml / L and H 3 PO 4 100ml / L;

[0035] Corrosive acid: HCl 50ml / L;

[0036] Compound complexing agent: hydroxyethylidene diphosphate and ammonium bifluoride, mass ratio 1:1.5, total amount 12~15g / L;

[0037] Corrosion inhibitor: Na 2 MoO 4 . 10H 2 O, 2g / L;

[0038] Rare earth additives: La(NO 3 ) 3 . 6H 2 O, 1g / L;

[0039] Viscosity regulator: polyethylene glycol, 4g / L;

[0040] Brightener: sulfosalicylic acid, 3g / L;

[0041] Defoamer: silicone defoamer, 0.1g / L;

[0042] Surfactant: Sodium Dodecyl Sulfonate, 5g / L;

[0043] NO x Remover: ethanol solution of bentonite rock above 1600 mesh, 3g / L;

[0044] The rest is deionized water.

[0045] The method steps for preparing the polishing liquid are: (1) Sieve and grind the bentonite rock particles to make them higher than 1600...

Embodiment 2

[0048] A kind of environment-friendly stainless steel polishing fluid is characterized in that described polishing fluid comprises:

[0049] Strong oxidizing agent: NaNO 3 50g / L, HNO 3 20ml / L and H 3 PO 4 110ml / L;

[0050] Corrosive acid: HCl 80ml / L;

[0051] Compound complexing agent: hydroxyethylidene diphosphate and ammonium bifluoride, mass ratio 1:1.5, total amount 13g / L;

[0052] Corrosion inhibitor: sodium molybdate, 2.6g / L;

[0053] Rare earth additives: La(NO 3 ) 3 . 6H 2 O, 1.3g / L;

[0054] Viscosity regulator: polyethylene glycol, 5.5g / L;

[0055] Brightener: sulfosalicylic acid, 5g / L;

[0056] Defoamer: silicone defoamer, 0.6 / L;

[0057] Surfactant: Sodium Dodecyl Sulfonate, 7g / L;

[0058] NO x Remover: ethanol solution of bentonite rock above 1600 mesh, 8g / L;

[0059] The rest is deionized water.

Embodiment 3

[0061] A kind of environment-friendly stainless steel polishing fluid is characterized in that described polishing fluid comprises:

[0062] Strong oxidizing agent: NaNO 3 60g / L, HNO 3 20ml / L and H 3 PO 4 120ml / L;

[0063] Corrosive acid: HCl 100ml / L;

[0064] Compound complexing agent: hydroxyethylidene diphosphate and ammonium bifluoride, mass ratio 1:2, 15g / L;

[0065] Corrosion inhibitor: Na 2 MoO 4 . 10H 2 O, 3g / L;

[0066] Rare earth additives: La(NO 3 ) 3 . 6H 2 O, 1.5g / L;

[0067] Viscosity regulator: polyethylene glycol, 8g / L;

[0068] Brightener: sulfosalicylic acid, 7g / L;

[0069] Defoamer: silicone defoamer, 1g / L;

[0070] Surfactant: Sodium Dodecyl Sulfonate, 7g / L;

[0071] NO x Remover: ethanol solution of bentonite rock above 1600 mesh, 10g / L;

[0072] The rest is deionized water.

[0073] Effect of strong oxidizing agent on polishing quality (other components of polishing fluid remain unchanged):

[0074]

[0075] The role of the oxi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides environment-friendly type stainless steel polishing liquid and a preparation method and a polishing technology thereof. The environment-friendly type stainless steel polishing liquid is prepared from a strong oxidant, corrosive acid, a compound complexing agent, a corrosion inhibitor, a rare earth additive, a viscosity adjuster, a polishing agent, a defoaming agent, a surfacant, an NOx removal agent and deionized water. The environment-friendly type stainless steel polishing liquid has the advantages that the stability is good, the service life is long, a technology of preparing the polishing liquid and treating stainless steel is simple, the surface of the treated stainless steel is flat, the forming of an oxide film and pitting corrosion are avoided, a mirror surface is excellent, the polishing time is shorter, the production of irritant gas in the use process is avoided, and the polishing liquid can be recycled for multiple times.

Description

technical field [0001] The invention belongs to the technical field of metal surface treatment, and in particular relates to a chemical polishing solution for stainless steel, a preparation method and a polishing process thereof. Background technique [0002] With the improvement of people's living standards, stainless steel products are becoming more and more widely used in chemical industry, petroleum, home appliances, hardware, food, machinery manufacturing and other fields, and the requirements for stainless steel products are getting higher and higher, not only must be durable, but also To achieve the appearance of mirror, bright, delicate and pleasing effect. [0003] At present, the commonly used methods of polishing stainless steel mainly include (1) electrochemical polishing. Although the effect of electrochemical polishing is excellent, the energy consumption is high. For complex parts, not only special fixtures are required, but also for anodes, cathodes, and blin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23F3/06C23G1/19
Inventor 白林森梁莲芝
Owner 佛山市顺德区亚特祥展洗涤剂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap