Flame retardant antistatic polypropylene composition and foamed bead prepared therefrom

A polypropylene composition and flame-retardant polypropylene technology, applied in the polymer field, can solve the problems of poor low-temperature impact resistance of polypropylene, difficulty in blending polypropylene base resin, short-acting antistatic agent, etc. The effect of efficiency

Active Publication Date: 2017-11-07
CHINA PETROLEUM & CHEM CORP +1
View PDF21 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Third, EPP beads have poor antistatic properties
However, in general, the filling amount of conductive filler required to form a conductive network or the amount of antistatic agent added is relatively large, resulting in a significant decrease in the mechanical properties of the polymer, and increasing the production cost and process difficulty of the material. Therefore, Reducing the amount of conductive filler is an important content in the development and application of antistatic composite materials
Chinese patent application 200510004023.0 reports the use of polymer antistatic agents to prepare antistatic polyolefin resin foams, with a surface intrinsic resistivity of 10 8 -10 13 Ωcm, the polymer antistatic agent used mainly includes polyether-polypropylene block copolymer, polyether ester amide and polyamide mixture, etc., but the antistatic addition is 4-6%, and it is short-acting Antistatic agent, the antistatic validity period is only 30 days
Chinese patent application 200710192215.8 reports the preparation method of antistatic and anticonductive polypropylene, and the surface intrinsic resistivity of the obtained polypropylene sheet is 10 10 -10 11 Ωcm, the addition amount of carbon black is 5-40%; due to the low apparent d

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame retardant antistatic polypropylene composition and foamed bead prepared therefrom
  • Flame retardant antistatic polypropylene composition and foamed bead prepared therefrom
  • Flame retardant antistatic polypropylene composition and foamed bead prepared therefrom

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0203] Preparation of Polypropylene Base Resin HMSPP

[0204] Preparation of Polypropylene Base Resin HMSPP701

[0205] The propylene polymerization reaction is carried out on a polypropylene unit, and the main equipment of the unit includes a prepolymerization reactor, a first loop reactor, a second loop reactor and a third gas phase reactor. The polymerization method and steps are as follows.

[0206] (1) Prepolymerization reaction

[0207] The main catalyst (DQC-401 catalyst, provided by Beijing Aoda Branch of Sinopec Catalyst Company), co-catalyst (triethylaluminum), and the first external electron donor (isopropylcyclopentyldimethoxysilane, IPCPMS) were After pre-contacting at 6°C for 20 minutes, it is continuously fed into a continuous stirred tank prepolymerization reactor for prepolymerization. The flow of triethylaluminum (TEA) entering the prepolymerization reactor is 6.33g / hr, the flow of isopropylcyclopentyldimethoxysilane is 0.3g / hr, the flow of main catalyst i...

Embodiment 1

[0220] The raw material ratio and reaction conditions of the flame retardant, polypropylene composition and expanded beads prepared in this example are listed in Table 3 and Table 4, and Table 4 also lists the performance parameters of the expanded beads. In the table, flame retardant component A is phosphine oxide, flame retardant component B is a transition metal salt, and flame retardant component C is an inorganic flame retardant component.

[0221] (1) Preparation of (halogen-free) flame retardant

[0222] Add 7kg of triphenylphosphine oxide and cobalt formate into ethanol, stir at a rate of 100rpm, and then use microwave to heat the mixture under stirring, with a heating power of 50W, a temperature of 40°C, and a heating time of 4h. The material after microwave heating reaction is carried out supercritical drying, obtains the chelate Co(CHO of the formation of triphenylphosphine oxide and cobalt formate 2 ) 2 (OPPh 3 ) 2 .

[0223] (2) Preparation of (halogen-free) ...

Embodiment 2

[0240] The preparation method of flame retardant, composite flame retardant, carbon nanofiber antistatic agent, flame retardant antistatic polypropylene composition and expanded beads is similar to embodiment 1, and difference is that shown in table 3 and 4 Raw material formulations and reaction conditions. For example, this embodiment uses HMSPP702, and the halogen-free flame retardant formed is the chelate Ni(CHO) formed by trioctylphosphine oxide and nickel formate. 2 ) 2 (OPot 3 ) 2 , the prepared carbon nanofiber antistatic agent contains nickel 3wt%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Login to view more

Abstract

The invention provides a flame retardant polypropylene composition, a flame retardant antistatic polypropylene composition, and a flame retardant (antistatic) polypropylene foamed bead, and a preparation method and applications thereof. The flame retardant antistatic polypropylene foamed bead is prepared from the flame retardant antistatic polypropylene composition, which comprises polypropylene basic resin with a high melt strength, the flame retardant antistatic composition, a cellular nucleating agent, and optionally selected auxiliary agents such as antioxidant, by a foaming technology; and preferably, the polypropylene basic resin comprises a propylene homopolymer component and an ethylene-1-butene copolymer component. A moulded body prepared from the flame retardant antistatic polypropylene foamed bead has a good flame retardant and antistatic performance, excellent mechanical properties, and a wide application range.

Description

technical field [0001] The invention relates to the technical field of macromolecules, in particular to a flame-retardant polypropylene composition, a flame-retardant antistatic polypropylene composition and a flame-retardant (antistatic) polypropylene foamed bead. Background technique [0002] Due to its light weight, good mechanical properties, and the use of molding to make products with specific shapes, expanded polypropylene beads (EPP) are a polymer foam material with a wide range of uses. Its development and industrial production have been continuously It is the focus of industry and academia in various countries. Compared with polystyrene series resin foamed bead shaped products, polypropylene foamed molded products obtained by molding polypropylene foamed beads have chemical resistance, high toughness, high heat resistance, good Excellent properties such as compression resilience. However, the current industrialized EPP has disadvantages such as high molding proce...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08L23/08C08K13/04C08K7/06C08K5/00C08K3/22C08J9/18C08J9/228
CPCC08J9/18C08J9/228C08J2323/12C08J2423/08C08J2423/12C08K2201/011C08K2201/017C08L23/12C08L2201/02C08L2201/04C08L2201/22C08L2203/14C08L2205/025C08L2205/03C08L23/0815C08K13/04C08K7/06C08K5/0091C08K2003/2224
Inventor 郭鹏徐耀辉吕明福张师军白弈青邵静波毕福勇宋文波徐萌
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap