High-efficiency and no-pollution silver ingot casting deoxidizing agent and deoxidizing method and application thereof

A deoxidizer, non-polluting technology, applied in the direction of element selenium/tellurium, can solve the problems of insufficient surface finish, loose internal structure, and lower specific gravity of silver ingots, and achieves inhibition of oxygen dissolution, reduction of reprocessing costs, and low silver content. Effect

Active Publication Date: 2017-11-07
DAYE NONFERROUS METALS
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The purpose of the present invention is to aim at the above-mentioned problems of charcoal as a deoxidizer, to provide a high-efficiency and pollution-free silver ingot casting deoxidizer and its deoxidation method and application. Advantages, it solves the defects of insufficient surface finish, loose internal structure and lower specific gravity of silver ingots, and at the same time avoids cracks and other defects that are easy to cause in the process of mechanical processing, rolling and wire drawing of silver ingots in the later stage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] An efficient and pollution-free deoxidizer for casting silver ingots in this embodiment, the deoxidizer is wheat high-gluten flour.

[0022] The grain size of the wheat high-gluten flour described in this example is 90 mesh.

[0023] In the wheat high-gluten flour described in the present embodiment, the gluten quality is 32% on a wet basis, the protein is 12.5% ​​on a dry basis, the ash content is 0.65% on a dry basis, the sand content is 0.01%, and the magnetic metal is 0.002g / kg. It meets the technical requirements of first-class high-gluten wheat flour in the national standard GB / T 8607-88.

[0024] An efficient and pollution-free silver ingot casting deoxidizer deoxidation method in this embodiment includes the following steps: (1) Melting: put 120kg of electric silver powder in a crucible, and then put the crucible in a 100KW intermediate frequency furnace to melt, high-power Rapidly raise the temperature to 1050°C, at this time, the silver powder starts to melt ...

Embodiment 2

[0029] An efficient and pollution-free deoxidizer for casting silver ingots in this embodiment, the deoxidizer is wheat high-gluten flour.

[0030] The grain size of wheat high-gluten flour described in this example is 80 mesh.

[0031] In the wheat high-gluten flour described in this embodiment, the gluten is 38% on a wet basis, the protein is 13.2% on a dry basis, the ash content is 0.50% on a dry basis, the sand content is 0.01%, and the magnetic metal is 0.001g / kg. It meets the technical requirements of first-class high-gluten wheat flour in the national standard GB / T 8607-88.

[0032] An efficient and pollution-free silver ingot casting deoxidizer deoxidation method in this embodiment includes the following steps: (1) Melting: put 120kg of electric silver powder in a crucible, and then put the crucible in a 100KW intermediate frequency furnace to melt, high-power Rapidly raise the temperature to 1050°C, at this time, the silver powder starts to melt into silver liquid. A...

Embodiment 3

[0034] An efficient and pollution-free deoxidizer for casting silver ingots in this embodiment, the deoxidizer is wheat high-gluten flour.

[0035] The grain size of wheat high-gluten flour described in this example is 100 mesh.

[0036] In the wheat high-gluten flour described in the present embodiment, the gluten quality is 37% on a wet basis, the protein is 14.1% on a dry basis, the ash content is 0.60% on a dry basis, the sand content is 0.01%, and the magnetic metal is 0.002g / kg. It meets the technical requirements of first-class high-gluten wheat flour in the national standard GB / T 8607-88.

[0037]An efficient and pollution-free silver ingot casting deoxidizer deoxidation method in this embodiment includes the following steps: (1) Melting: put 120kg of electric silver powder in a crucible, and then put the crucible in a 100KW intermediate frequency furnace to melt, high-power Rapidly raise the temperature to 1050°C, at this time, the silver powder starts to melt into s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-efficiency and no-pollution silver ingot casting deoxidizing agent and a deoxidizing method thereof. The deoxidizing agent is wheat strong flour; and the deoxidizing method comprises the following steps: (1) melting: electric silver powder is put in a crucible; the crucible is put in a medium-frequency furnace of 100 KW for melting; the temperature is quickly increased to 1050 DEG C with high power; at this time, the silver powder is molten to silver liquid; and when the weight of the silver powder reaches the casting weight, the power of the medium-frequency furnace is adjusted to 80 KW; (2) deoxidation: after the silver powder is totally molten to the silver liquid, the wheat strong flour is added in the crucible; the adding quantity of the flour is 0.42-1.67% of the weight of the silver powder; the paving thickness is 15-20 mm; the deoxidizing time is 6-20 min; and deslagging is performed after deoxidation; and (3) casting: a port of the crucible is aligned to a casting mold port; and the silver liquid is cast in a casting mold with a temperature of 250-300 DEG C and coated with a layer of carbon black. The deoxidizing agent has such advantages as low cost, short deoxidizing time and deoxidizing efficiency of not lower than 98%.

Description

technical field [0001] The invention relates to the technical field of precious metal casting process improvement, in particular to an efficient and pollution-free silver ingot casting deoxidizer and its deoxidation method and application. Background technique [0002] At present, the current production process of major smelters at home and abroad to deal with copper anode slime mainly adopts pyromelting-electrolysis or wet extraction-electrolysis process. The electrolysis process is to recover gold and silver from copper electrolysis anode slime. The main process is as follows: the anode slime undergoes sulfate roasting, leaching and decopper, and then separates gold from chloride and silver from sodium sulfite to obtain coarse silver powder, and the coarse silver powder undergoes fire blowing Become a silver anode plate, and then produce silver ingots that meet the national standard through electrolytic refining. The silver ingot casting process consists of four processes...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22B9/10C22B11/00C22B30/06C01B19/02
CPCC01B19/02C22B9/10C22B11/00C22B30/06
Inventor 宋幸福李伟程春喜王建新宁瑞杨彦
Owner DAYE NONFERROUS METALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More