Novel plant composite shoe material

A new type of plant and composite material technology, applied in the field of new plant composite shoe materials, can solve the problems of poor deodorization and antibacterial performance, air permeability, water absorption performance is not obvious, low folding strength, etc., to achieve good shoe purification and low cost Low, easy-to-use effect

Inactive Publication Date: 2017-11-24
JINHOU GRP WEIHAI SHOES
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the midsole and insole materials used in shoemaking are generally made of non-woven fabrics, cardboard, non-woven leather and multi-layer woven fabrics. Although cardboard materials are made of wood pulp or recycled cardboard, but in the colloid The air permeability and water absorption performance are not obvious under the action, and the folding strength is also low; non-woven fabrics and leather materials have good folding resistance, but poor deodorization and antibacterial performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Plant composite preparation:

[0020] Ula grass powder: 3kg, tea powder: 3kg, cypress leaf powder: 3kg, antibacterial powder: 1kg, zeolite powder: 2kg, negative ion powder: 2kg, fragrance powder: 1kg, PVA: 2kg, deionized water: 70kg.

[0021] The antibacterial powder is nanometer zinc dioxide 1nm.

[0022] Described face powder is lavender.

[0023] Described PVA is polyvinyl alcohol.

[0024] The non-woven fabric is 2mm thick.

[0025] The steps of the plant composite shoe material processing method are as follows:

[0026] (1) Drying, pulverizing, and sieving Uralia sativa, tea leaves, and cypress leaves respectively to obtain 50 μm umlaxa powder, tea powder, and cypress leaf powder.

[0027] (2) Add PVA into a reaction kettle filled with deionized water and heat at 80°C, stir while heating to dissolve all the PVA powder, cool it, take it out and add it to the stirrer.

[0028] (3) Gradually add the prepared ulagrass powder, grass leaf powder, cypress leaf powder...

Embodiment 2

[0031] Plant composite preparation:

[0032] Ula grass powder: 4kg, tea powder: 4kg, cypress leaf powder: 4kg, antibacterial powder: 1.5kg, zeolite powder: 3kg, negative ion powder: 3kg, fragrance powder: 1.5kg, PVA: 3kg, deionized water: 80kg.

[0033] The antibacterial powder is nanometer zinc dioxide 10nm.

[0034] Described face powder is cologne powder.

[0035] Described PVA is polyvinyl alcohol.

[0036] The non-woven fabric is 3mm thick.

[0037] The steps of the plant composite shoe material processing method are as follows:

[0038] (1) Drying, pulverizing, and sieving Uralia sativa, tea leaves, and cypress leaves respectively to obtain 80 μm ulata grass powder, tea powder, and cypress leaf powder.

[0039] (2) Add PVA into a reaction kettle filled with deionized water and heat at 85°C, stir while heating to dissolve all the PVA powder, cool it, take it out and add it to the stirrer.

[0040] (3) Gradually add the prepared ulagrass powder, grass leaf powder, cyp...

Embodiment 3

[0043] Plant composite preparation:

[0044] Ula grass powder: 5kg, tea powder: 5kg, cypress leaf powder: 5kg, antibacterial powder: 2kg, zeolite powder: 4kg, negative ion powder: 4kg, fragrance powder: 2kg, PVA: 4kg, deionized water: 90kg.

[0045] The antibacterial powder is nanometer zinc dioxide 50nm.

[0046] Described face powder is cologne powder.

[0047] Described PVA is polyvinyl alcohol.

[0048] The non-woven fabric is 4mm thick.

[0049] The steps of the plant composite shoe material processing method are as follows:

[0050] (1) Drying, pulverizing, and sieving Uralia sativa, tea leaves, and cypress leaves respectively to obtain 100 μm umlaxa powder, tea powder, and cypress leaf powder.

[0051] (2) Add PVA into a reaction kettle filled with deionized water and heat at 90°C, stir while heating to dissolve all the PVA powder, cool it, take it out and add it to the stirrer.

[0052] (3) Gradually add the prepared ulagrass powder, grass leaf powder, cypress lea...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a novel plant composite shoe material, which comprises a plant composite material and a non-woven fabric, wherein the components of the plant composite material formula comprise 3-5 parts of carex meyeriana powder, 3-5 parts of tea leaf powder, 3-5 parts of platycladus orientalis leaf powder, 1-2 parts of antibacterial powder, 2-4 parts of zeolite powder, 2-4 parts of negative ion powder, 1-2 parts of fragrant powder, 2-4 parts of PVA, and 70-90 parts of deionized water. According to the present invention, by using the carex meyeriana powder, the tea leaf powder, the platycladus orientalis leaf powder and other plants, the produced shoe material has functions of strong odor adsorption and strong wet-liquid adsorption; the system contains the antibacterial powder, the negative ion powder, the fragrant powder and the zeolite powder so as to provide strong bacterial killing ability and strong odor decomposition ability and purify the inside-shoe environment; the mid-sole and the insole produced from the product of the present invention have excellent inside-shoe purification function and can achieve the effects of antibacterial effect and deodorization; and the novel plant composite shoe material has characteristics of simple process, low cost, and easy use.

Description

technical field [0001] The invention relates to the technical field of shoemaking materials, in particular to a novel plant composite shoe material. Background technique [0002] At present, the midsole and insole materials used in shoemaking are generally made of non-woven fabrics, cardboard, non-woven leather and multi-layer woven fabrics. Although cardboard materials are made of wood pulp or recycled cardboard, but in the colloid The air permeability and water absorption performance under the action are not obvious, and the folding strength is also low; non-woven fabrics and leather materials have good folding resistance, but poor deodorization and antibacterial performance. In order to solve the above defects, the inventor finally designed a new type of plant composite shoe material made of a mixture of various plant powders as raw materials after years of research and development experiments to solve the deficiencies in the background technology. Contents of the inven...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M15/01D06M13/00D06M15/333D06M11/44D06M11/79
CPCD06M15/01D06M11/44D06M11/79D06M13/00D06M15/333
Inventor 葛生龙林瀚郭夏欢于杰
Owner JINHOU GRP WEIHAI SHOES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com