Diamond lapping paste and preparation method thereof

A diamond abrasive paste, synthetic diamond technology, applied in chemical instruments and methods, polishing compositions containing abrasives, other chemical processes, etc. Difficulty in processing workpiece materials

Inactive Publication Date: 2017-11-28
YUNNAN MINZU UNIV
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The characteristic of grinding is that the abrasive is constantly rolling during the grinding process, producing two effects of extrusion and cutting. During the processing of the workpiece, as the contact area between the abrasive paste and the workpiece continues to increase, some gr...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0072] Example 1 :Prepare easily a diamond paste

[0073] The implementation steps of this embodiment are as follows:

[0074] A, dissolve

[0075] Under the condition of a heating temperature of 70°C in a water bath, 75 parts by weight of petroleum jelly and 75 parts by weight of stearic acid are added to 30 parts by weight of diesel, and after melting, 20 parts by weight of polytetrafluoroethylene and 20 parts by weight of graphite are added to obtain a Emulsion.

[0076] B. Scatter

[0077] Add 6 parts by weight of synthetic diamond powder and 55 parts by weight of oleic acid to the solution obtained in step A, mix them evenly, and then place them in a heat-collecting thermostatic heating magnetic stirrer for 18 minutes to stir and disperse to obtain a black milky mixture;

[0078] C, cooling

[0079] Using a cold water bath cooling method, the milky mixture obtained in step B is cooled to room temperature to obtain the diamond abrasive paste.

[0080] A standard ZYP300 grinder was u...

Embodiment 2

[0082] Example 2 :Preparation of a diamond grinding paste

[0083] The implementation steps of this embodiment are as follows:

[0084] A, dissolve

[0085] Under the condition of a heating temperature of 75°C in a water bath, 180 parts by weight of petrolatum and 180 parts by weight of stearic acid are added to 100 parts by weight of diesel, and after melting, 24 parts by weight of polytetrafluoroethylene and 24 parts by weight of graphite are added to obtain a Emulsion.

[0086] B. Scatter

[0087] Add 12 parts by weight of synthetic diamond powder and 74 parts by weight of oleic acid to the solution obtained in step A, mix them evenly, and then place them in a heat-collecting thermostatic heating magnetic stirrer for 10 minutes to stir and disperse to obtain a black milky mixture;

[0088] C, cooling

[0089] Using a refrigerator cooling method, the milky mixture obtained in step B is cooled to room temperature to obtain the diamond abrasive paste.

[0090] A standard ZYP300 grinder ...

Embodiment 3

[0092] Example 3 :Preparation of a diamond grinding paste

[0093] The implementation steps of this embodiment are as follows:

[0094] A, dissolve

[0095] Under the condition of a water bath heating temperature of 80°C, 30 parts by weight of petroleum jelly and 30 parts by weight of stearic acid are added to 30 parts by weight of diesel, and 5 parts by weight of polytetrafluoroethylene and 5 parts by weight of graphite are added after melting to obtain a Emulsion.

[0096] B. Scatter

[0097] Add 2 parts by weight of synthetic diamond powder and 15 parts by weight of oleic acid to the solution obtained in step A, mix them evenly, and then place them in a heat-collecting thermostatic heating magnetic stirrer for stirring and dispersing for 12 minutes to obtain a black milky mixture;

[0098] C, cooling

[0099] Using a cold water bath cooling method, the milky mixture obtained in step B is cooled to room temperature to obtain the diamond abrasive paste.

[0100] A standard ZYP300 grind...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Surface roughnessaaaaaaaaaa
Surface roughnessaaaaaaaaaa
Surface roughnessaaaaaaaaaa
Login to view more

Abstract

The invention relates to diamond lapping paste and a preparation method thereof. The diamond lapping paste is composed of artificial diamond micro powder, vaseline, diesel, oleic acid, graphite, stearic acid and polytetrafluoroethylene. The diamond lapping paste disclosed by the invention has excellent lapping and polishing properties, is fine and smooth in paste body and has an excellent effect of polishing sapphire lens materials.

Description

Technical field [0001] The invention belongs to the technical field of material polishing and grinding. More specifically, the present invention relates to a diamond polishing paste, and also relates to a preparation method of the diamond polishing paste. Background technique [0002] Grinding is characterized by the continuous rolling of the abrasive during the grinding process, resulting in both extrusion and cutting. During the processing of the workpiece, as the contact area between the grinding paste and the workpiece continues to increase, there will be some grinding immobility and The grinding paste cannot adhere well to the surface of the workpiece, which reduces the grinding efficiency. The emergence of these problems will make the processing of workpiece materials difficult, especially for some precision devices and devices that require high finish on the surface of the material. [0003] In order to better solve the defects of the prior art, the present invention, base...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09K3/14C09G1/02
CPCC09K3/1454C09G1/02
Inventor 陈菓李毅恒冯康露何奥希彭金辉
Owner YUNNAN MINZU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap