Silk-ramie fiber spunlace non-woven facial mask base fabric and preparation method thereof

A non-woven and silk fiber technology, applied in the direction of non-woven fabrics, textiles and papermaking, etc., can solve the problems of large shrinkage deformation of fabrics, large elongation at break, and low wet breaking strength, so as to reduce the generation of wrinkles and inhibit Effect of sebum secretion and blood circulation acceleration

Inactive Publication Date: 2017-12-01
ZHONGYUAN ENGINEERING COLLEGE
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the wet breaking strength is small, and the shrinkage deformation of the fabric made of pure viscose fiber is large
The strength of viscose fiber is lower than that of cotton fiber, it is not washable, its elongation at break is higher than that of cotton fiber, it has poor wear resistance, it is easy to deform under small load, it has poor dimensional stability, low stiffness and poor elasticity
[0010] Polyester fiber has the advantages of high strength, good recovery, and good heat setting, but the mass specific resistance of polyester fiber is large, and the electrostatic phenomenon is prominent, which makes it difficult to form a net in the process of carding pure polyester fiber.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Using the above process flow, equipment and technical measures, etc., the silk and hemp fiber spunlace nonwoven mask base fabric has been developed, wherein it is made of the following raw materials in weight ratio: the weight content of silk and hemp fiber accounts for 60%, The weight content of viscose fiber accounts for 10%, and the weight content of polyester fiber accounts for 30%. The performance index of the spunlace nonwoven mask base fabric is: actual weight 64.25g / m 2, average thickness 0.32mm; longitudinal strength 76.25N, transverse strength 80.75N, longitudinal and transverse strength ratio 0.94:1; longitudinal elongation at break 26.17%, transverse elongation at break 38.33%, longitudinal and transverse elongation at break ratio 0.68:1 ; Longitudinal tear strength 11.42N, transverse tear strength 12.50N, longitudinal and transverse tear strength ratio 0.91:1. The antibacterial rate of Staphylococcus aureus (ATCC6538) was 86.1%, that of Escherichia coli (80...

Embodiment 2

[0049] Utilize the above technological process, equipment and technical measure etc., have developed silk hemp fiber spunlaced nonwoven facial mask base cloth, wherein, it is made by the raw material of following weight ratio: the weight content of silk hemp fiber accounts for 50%, The weight content of viscose fiber accounts for 10%, and the weight content of polyester fiber accounts for 40%. The performance index of spunlace nonwoven mask base fabric is: the actual weight is 46g / m 2 , average thickness 0.30mm; longitudinal strength 53.13N, transverse strength 47.54N, longitudinal and transverse strength ratio 1.12:1; longitudinal elongation at break 27.13%, transverse elongation at break 50.88%, longitudinal and transverse elongation at break ratio 0.53:1 ; The longitudinal tear strength is 10.67N, the transverse tear strength is 9.48N, and the longitudinal and transverse tear strength ratio is 1.13:1. The antibacterial rate of Staphylococcus aureus (ATCC6538) was 85.1%, tha...

Embodiment 3

[0052] Using the above process flow, equipment and technical measures, etc., the silk and hemp fiber spunlace nonwoven mask base fabric has been developed, wherein it is made of the following raw materials in weight ratio: the weight content of silk and hemp fiber accounts for 80%, The weight content of viscose fiber accounts for 10%, and the weight content of polyester fiber accounts for 20%. The performance index of spunlace non-woven mask base fabric is: actual weight 65g / m 2 , average thickness 0.45mm; longitudinal strength 69.5N, transverse strength 64.75N, longitudinal and transverse strength ratio 1.07:1; longitudinal elongation at break 26.13%, transverse elongation at break 36.75%, ratio of longitudinal and transverse elongation at break 0.72:1 ; Longitudinal tear strength 8.5N, transverse tear strength 9.63N, longitudinal and transverse tear strength ratio 0.92:1. The antibacterial rate of Staphylococcus aureus (ATCC6538) was 92.2%, that of Escherichia coli (8089) wa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
tear loadaaaaaaaaaa
tear loadaaaaaaaaaa
Login to view more

Abstract

The invention relates to an antibacterial health care spunlace fabric, in particular to a preparation method and application of a silk-ramie fiber spunlace non-woven facial mask base fabric. The silk-ramie fiber spunlace non-woven facial mask base fabric is prepared from the following raw materials including, by weight, 10-100% of silk-ramie fibers, 0-50% of real silk fibers, 0-50% of natural silk fibers, 0-90% of viscose fibers, and 0-70% of polyester fibers. The advantages of the silk-ramie fiber spunlace non-woven facial mask base fabric are that the silk-ramie fiber spunlace non-woven facial mask base fabric can clean skins, retain moisture, and protect skins, is high in sterilizing rate, is nonirritating, has a moisture preservation, cell activating, and oxygen supplying function, and can nourish and care skins.

Description

technical field [0001] The invention relates to a health-care spunlace cloth for medical textiles, in particular to a silk and hemp fiber spunlace non-woven fabric which is processed by mixing silk and hemp fiber, real silk fiber, silk fiber, viscose fiber and polyester fiber. Weaving facial mask base fabric and its preparation method and application. Background technique [0002] The process principle of spunlace technology is to spray the fiber web with multiple strands of fine water jets generated by high pressure. After the water jet passes through the fiber net, it is entrusted with the rebound of the net curtain and penetrates the fiber net again. Therefore, the fibers in the fiber net are displaced, interspersed, entangled and entangled under the hydraulic action of high-speed water jets interspersed in different directions, thus Strengthen the web. [0003] Spunlace nonwoven materials have good hygroscopicity and air permeability, soft hand feeling, high strength, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D04H1/4382D04H1/492
CPCD04H1/4382D04H1/492
Inventor 赵博
Owner ZHONGYUAN ENGINEERING COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap