Composite modified cement concrete internal maintenance material and preparation method thereof

A technology of cement concrete and compound modification, which is applied in the field of building materials, can solve the problems of unfavorable early strength and impermeability of concrete, impact, and reduction of concrete strength, and achieve the improvement of ion penetration resistance, durability, and frost resistance. rising effect

Active Publication Date: 2020-01-31
西安华泽道路材料有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to improve the curing effect of this method, it is usually necessary to add a large amount of light aggregate. Although the self-shrinkage of concrete will be greatly reduced, the strength of concrete will be reduced due to the addition of a large amount of light aggregate, and the water absorption of light aggregate is not good. The strength of regular concrete has great variation
Among them, the superabsorbent resin in the polymer material is the most concerned object, but because the current technology is limited, it will usually have an adverse effect on the early strength and impermeability of the concrete during use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] This example provides a composite modified cement concrete internal curing material, which includes the following raw materials by weight: 24% methyl acrylate, 13% aconitic acid, 6% 3-hydroxypropionic acid, 15% carboxylate Methylcellulose, 20% hydrotalcite-like, 3% alumite powder, 0.006% polyvinyl alcohol, 0.004% glycerin, 0.25% initiator, 18.74% Ca(OH) 2 .

[0041] The preparation method of the above-mentioned composite modified cement concrete inner curing material comprises the following steps:

[0042] Step 1: Weigh the above-mentioned raw materials according to their quality;

[0043] Step 2: Place the weighed hydrotalcite-like material in a drying oven at 102° C. for 24 hours.

[0044] Step 3: The dried hydrotalcite-like material is placed in a muffle furnace, heated to 500°C at a heating rate of 3°C / min, kept for 5 hours and then cooled naturally.

[0045] Step 4: place the cooled hydrotalcite-like material in a container, add an appropriate amount of distille...

Embodiment 2

[0054] This example provides a composite modified cement concrete internal curing material, which includes the following raw materials by weight: 26% methyl acrylate, 10% aconitic acid, 6% 3-hydroxypropionic acid, 13% carboxylate Methylcellulose, 16% hydrotalcite-like, 1.5% alumite powder, 0.015% polyvinyl alcohol, 0.005% glycerin, 0.4% initiator, 27.08% Ca(OH) 2 .

[0055] The preparation method of the above-mentioned composite modified cement concrete inner curing material comprises the following steps:

[0056] Step 1: Weigh the above-mentioned raw materials according to their quality;

[0057] Step 2: Place the weighed hydrotalcite-like material in a drying oven at 102° C. for 24 hours.

[0058] Step 3: The dried hydrotalcite-like material is placed in a muffle furnace, heated to 500°C at a heating rate of 3°C / min, kept for 5 hours and then cooled naturally.

[0059] Step 4: place the cooled hydrotalcite-like material in a container, add an appropriate amount of distill...

Embodiment 3

[0068] This example provides a composite modified cement concrete internal curing material, which includes the following raw materials by weight: 25% methyl acrylate, 12% aconitic acid, 5% 3-hydroxypropionic acid, 14% carboxylate Methylcellulose, 18% hydrotalcite-like, 2.2% alumite powder, 0.01% polyvinyl alcohol, 0.005% glycerin, 0.32% initiator, 23.465% Ca(OH) 2 .

[0069] The preparation method of the above-mentioned composite modified cement concrete inner curing material comprises the following steps:

[0070] Step 1: Weigh the above-mentioned raw materials according to their quality;

[0071] Step 2: Place the weighed hydrotalcite-like material in a drying oven at 102° C. for 24 hours.

[0072] Step 3: The dried hydrotalcite-like material is placed in a muffle furnace, heated to 500°C at a heating rate of 3°C / min, kept for 5 hours and then cooled naturally.

[0073] Step 4: place the cooled hydrotalcite-like material in a container, add an appropriate amount of distil...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
densityaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention provides a compound modified cement concrete internal-maintenance material and a preparation method thereof. The maintenance material is prepared by compounding inorganic hydrotalcite-like compounds with organic high water-absorbent resin through an intercalation modification technique. The material preparation by virtue of the preparation method has excellent water retention capacity, the shrinkage of concrete is reduced to a great extent, the compressive strengths in the days 7 and 28 are increased by above 10%, the relatively dynamic elasticity modulus after 300 freezing and thawing cycles is above 80%, the anti-freezing property is obviously improvided, and the chloride penetration resistance and sulfate corrosion resistance are remarkably improved.

Description

technical field [0001] The invention belongs to the field of building materials and relates to a cement concrete inner curing material, in particular to a composite modified cement concrete inner curing material and a preparation method thereof. Background technique [0002] As the most widely used and irreplaceable building material, concrete is widely used in highway and civil construction projects in my country because of its high compressive strength, good durability and low price. At present, the curing technology used in most concrete projects in my country is external curing technology. This technology refers to the maintenance technologies such as covering wet straw bags, plastic films, and direct water spray on the surface of concrete. This kind of "outside-in" external curing technology will not only consume a lot of manpower, financial resources and material resources, but especially for the high-performance concrete with low water-to-binder ratio as a typical fe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B24/38
CPCC04B40/0042C04B24/045C04B24/04C04B24/06C04B24/383C04B14/04C04B22/142C04B22/064C04B24/2623C04B24/02C04B22/085
Inventor 何锐谈亚文耿瑶陈华鑫龙景潭张豪
Owner 西安华泽道路材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com