Highly hydrophobic anti-ultraviolet inorganic artificial stone and preparation method thereof

A UV-resistant, artificial stone technology, applied in the field of artificial stone, can solve problems such as insufficient UV resistance, difficulty in cleaning walls, and easy contamination, and achieve the effects of increasing service life, reducing costs, and improving hydrophobic performance

Active Publication Date: 2017-12-15
东莞环球经典新型材料有限公司
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, resin-type artificial stone will bring environmental protection problems with its large-scale use. The existing inorganic artificial stone has low hydrophobicity, insufficient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0019] Example 1

[0020] The present invention provides a highly hydrophobic and ultraviolet resistant inorganic artificial stone. The components and mass parts of the high hydrophobic and ultraviolet resistant inorganic artificial stone are as follows: quartz sand: 60 parts; quartz powder: 5 parts; cement: 18 parts ; Active additives: 2 parts, emulsion: 4 parts; water reducing agent 0.8 parts; water: 2 parts; fluorine-containing group additives: 0.36 parts; UV additives: 0.5 parts. The fluorine-containing group additive is formed by mixing fluorosilicone materials and superhydrophobic nano silica. The ultraviolet additive is an ultraviolet absorber UV-531.

[0021] The invention improves the hydrophobicity and ultraviolet resistance of the inorganic artificial stone, enables the inorganic artificial stone to achieve a self-cleaning effect, facilitates the cleaning of the inorganic artificial stone curtain wall, and enhances the anti-aging performance of the inorganic artificial ...

Example Embodiment

[0030] Example 2

[0031] The present invention provides a highly hydrophobic and ultraviolet resistant inorganic artificial stone. The components and mass parts of the high hydrophobic and ultraviolet resistant inorganic artificial stone are as follows: quartz sand: 70 parts; quartz powder: 10 parts; cement: 23 parts Active additives: 5 parts; emulsion: 6 parts; water reducing agent 1.2 parts; water: 4 parts; fluorine-containing group additives: 0.46 parts; UV additives: 1 part. The fluorine-containing group additive is formed by mixing fluorosilicone materials and superhydrophobic nano silica. The ultraviolet additive is an ultraviolet absorber UV-531.

[0032] The invention improves the hydrophobicity and ultraviolet resistance of the inorganic artificial stone, enables the inorganic artificial stone to achieve a self-cleaning effect, facilitates the cleaning of the inorganic artificial stone curtain wall, and enhances the anti-aging performance of the inorganic artificial ston...

Example Embodiment

[0041] Example 3

[0042] The present invention provides a highly hydrophobic and ultraviolet resistant inorganic artificial stone. The components and mass parts of the high hydrophobic and ultraviolet resistant inorganic artificial stone are as follows: quartz sand: 65 parts; quartz powder: 7.5 parts; cement: 20.5 parts Active additives: 3.5 parts; emulsion: 5 parts; water reducing agent 1 part; water: 3 parts; fluorine-containing group additives: 0.41 parts; UV additives: 0.75 parts. The fluorine-containing group additive is formed by mixing fluorosilicone materials and superhydrophobic nano silica. The ultraviolet additive is an ultraviolet absorber UV-531.

[0043] The invention improves the hydrophobicity and ultraviolet resistance of the inorganic artificial stone, enables the inorganic artificial stone to achieve a self-cleaning effect, facilitates the cleaning of the inorganic artificial stone curtain wall, and enhances the anti-aging performance of the inorganic artificia...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a highly hydrophobic anti-ultraviolet inorganic artificial stone and a preparation method thereof. The highly hydrophobic anti-ultraviolet inorganic artificial stone is prepared from the following components in parts by mass: 60-70 parts of quartz sand, 5-10 parts of quartz powder, 18-23 parts of cement, 2-5 parts of an active additive, 4-6 parts of an emulsion, 0.8-1.2 parts of a water reducer, 2-4 parts of water, 0.36-0.46 part of a fluorine group-containing additive and 0.5-1 part of an ultraviolet additive. The hydrophobic property and the anti-ultraviolet strength of the inorganic artificial stone are improved, so that the inorganic artificial stone can achieve a self-cleaning effect, an inorganic artificial stone curtain wall project is cleaned conveniently, and the anti-ageing performance of the inorganic artificial stone is enhanced, so that the cost of the curtain wall project cleaning is reduced effectively, and the service life of the wall body is prolonged.

Description

technical field [0001] The invention relates to the field of artificial stone, in particular to a highly hydrophobic and ultraviolet-resistant inorganic artificial stone and a preparation method thereof. Background technique [0002] Artificial stone is a mineral-filled polymer composite material that is vacuum-cast or molded from natural ore powder, high-performance resin and natural pigments. It can be widely used in public buildings and home decoration. It is a non-radioactive pollution-free Environmentally friendly and green new building interior decoration materials that can be reused. Artificial stone can be divided into two categories: inorganic artificial stone and resin artificial stone according to the different binders used. Among them, resin-type artificial stone will bring environmental protection problems with its large-scale use. The existing inorganic artificial stone has low hydrophobicity, insufficient anti-ultraviolet ability, easy to be polluted and agin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/00C04B41/66C04B111/20
CPCC04B28/00C04B41/009C04B41/5018C04B41/66C04B2111/20C04B2111/2092C04B14/06C04B2103/0068C04B2103/302C04B22/126C04B22/06C04B2103/605C04B41/4535
Inventor 郗毅郭栋王安群戎延团
Owner 东莞环球经典新型材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap