High-performance polycarbonate composition containing special structure sag compatibilizer and preparation method thereof

A technology of polycarbonate and special structure, which is applied in the field of high-performance polycarbonate composition and its preparation, can solve the problem of poor compatibility between PC resin and PET resin alloy, reduce the application practicability of PC/PET alloy, and composite materials To solve problems such as the decline of mechanical properties, achieve the effect of optimization of initial mechanical properties, optimization of long-term damp heat aging performance, and improvement of compatibility

Active Publication Date: 2020-01-14
JIANGSU KINGFA SCI & TECH ADVANCED MATERIALS CO LTD +1
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, since PET resin is a crystalline polymer and PC resin is an amorphous polymer, the alloy compatibility between PC resin and PET resin is very poor, and the mixing of the two will also lead to a significant drop in the mechanical properties of the composite material.
In addition, since the PC resin contains terminal hydroxyl groups, it is very easy to undergo a two-phase reaction with the residual carboxyl groups and hydroxyl groups in the PET resin at high temperatures and the presence of titanium-based residual catalysts, although the reaction can improve compatibility. With great uncertainty, the above reactions will also cause a sharp deterioration in the performance of the composite material during later use, greatly reducing the practicability of PC / PET alloy applications

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance polycarbonate composition containing special structure sag compatibilizer and preparation method thereof
  • High-performance polycarbonate composition containing special structure sag compatibilizer and preparation method thereof
  • High-performance polycarbonate composition containing special structure sag compatibilizer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] In order to be able to understand the technical means of the present invention more clearly and implement it according to the contents of the description, the specific embodiments of the present invention will be further described in detail below in conjunction with specific examples. The following examples are used to illustrate the present invention, but not to limit it scope of the invention.

[0023] Each raw material used in the following specific examples and comparative examples is as follows:

[0024] PC resin: the viscosity average molecular weight is 20,000, the brand is S-3000F, and the manufacturer is Mitsubishi.

[0025] PET resin: the viscosity is 0.85dl / g, the grade is PET SB500, and the manufacturer is Yizheng Petrochemical.

[0026] Compatibilizer: SAG copolymer (styrene-acrylonitrile-glycidyl methacrylate), self-made, the preparation method refers to the preparation of the following SAG copolymer:

[0027] SAG copolymer-1, GMA content is 2wt.%, acryl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-property polycarbonate composition containing an SAG compatibilizer which has a special structure. The polycarbonate composition comprises PC resin, PET resin, a compatibilizer, a toughening agent, a fire retardant, an antioxidant and other auxiliary agent, wherein the compatbilizer is an SAG copolymer which is prepared from 50-85 wt% of styrene monomers, 10-40 wt% of acrylonitrile monomers and 0.5-30 wt% of glycidyl methacrylate in a water medium by using a suspension polymerization process. In the preparation of the composition, a specially prepared compatibilizer is selected, so that the compatibility of PC resin and PET resin is increased, the transesterification between the PC resin and the PET resin is notably inhibited, and the stability and toughness of the blend products are increased. In addition, a proper amount of a dispersing agent is selectively added in the preparing process of the compatibilizer, so that the long-term influence on PC / PET alloy by damp and hot conditions is deceased to a low level. The initial mechanical properties and long-term aging resistance in damp and hot conditions of the polycarbonate composition provided by the invention are both optimized greatly, so that the polycarbonate composition is especially suitable for occasions with high requirements of using environment.

Description

technical field [0001] The invention relates to a high-performance polycarbonate composition and a preparation method thereof, in particular to a high-performance polycarbonate composition containing a special-structure SAG compatibilizer and a preparation method thereof, and belongs to the technical field of composite polymers. Background technique [0002] Polycarbonate resin (PC resin) is a colorless and transparent amorphous thermoplastic material, because it is easy to process and suitable for injection, extrusion, blow molding and other molding methods, and has good mechanical and optical properties, Therefore, it is widely used in many fields such as packaging, daily necessities, electronic appliances, toys, instruments, transportation and machine manufacturing. However, pure PC resin has high melt viscosity, poor solvent resistance, high sensitivity to notches, and high cost. [0003] Polyethylene terephthalate resin (PET resin) is a translucent crystalline thermopla...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L69/00C08L67/02C08L25/14C08L1/28C08K13/02C08K3/32C08F212/08C08F220/44C08F220/32
CPCC08F212/08C08K2003/325C08L69/00C08L2205/035C08L2205/06C08L2205/08C08L67/02C08L25/14C08K13/02C08K3/32C08L1/284C08F220/44C08F220/325
Inventor 董相茂田征宇艾军伟岑茵夏建盟刘贤文张永殷年伟
Owner JIANGSU KINGFA SCI & TECH ADVANCED MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products