White ink pretreatment fluid as well as preparation method thereof and direct-injection digital printing process
A technology of pretreatment liquid and white ink, applied in dyeing method, textile and papermaking, etc., can solve the problems of insufficient covering power to meet people's consumer demand, reducing the adhesion of direct inkjet water of white paint, and insufficient inhibition, and achieve good Dispersion stability, sharp and clear lines, improved hiding power and adhesion
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0037] The present invention also provides a preparation method of the pretreatment liquid as described above, which comprises the following steps: sequentially input deionized water, wetting defoamer, bactericide, drying inhibitor, and polyvalent alkaline earth metal salt into the material machine In the process, stir at 300~400r / min for 20~30min to make it evenly mixed; then add cationic colloidal silica, cationic or nonionic binder and cationic mordant in sequence, and stir at 400~500r / min for 20~ 30min to make it evenly mixed; after slowly adding the anti-bleeding agent while stirring at a rotating speed of 300~400r / min, stir for 30~40min to make it evenly mixed; use 300~500 mesh filter cloth to filter the mixed liquid after mixing. The pretreatment liquid is obtained.
[0038] The present invention also provides a direct-injection digital printing process using the above pretreatment liquid, which includes the following steps:
[0039] S1. Fill the prepared pretreatment liqui...
Example Embodiment
[0043] Example 1:
[0044] A white ink pretreatment liquid, which includes the following components in parts by mass:
[0045]
[0046]
[0047] The preparation method of the white ink pretreatment liquid is as follows: put the formula amount of deionized water, wetting defoamer, bactericide, drying inhibitor, and polyvalent alkaline earth metal salt into the material machine in sequence, and stir at 300r / min for 20min. It is evenly mixed; then add cationic colloidal silica, cationic or non-ionic binder and cationic mordant one by one, stir at 300r / min for 20min to make it evenly mixed; at 300r / min while stirring, slowly add the anti-corrosion agent. After the bleeding agent, stir for 30 minutes to make it evenly mixed; filter the mixed liquid with 300 mesh filter cloth to obtain the pretreatment liquid.
[0048] The specific steps of applying the pretreatment liquid prepared in this embodiment to direct-injection digital printing are as follows:
[0049] S1. Fill the prepared pretre...
Example Embodiment
[0053] Example 2:
[0054] A white ink pretreatment liquid, which includes the following components in parts by mass:
[0055]
[0056] The preparation method and the direct-injection digital printing process of this embodiment are similar to those of Embodiment 1, and will not be repeated here.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap