Process for preparing nylon roller brush hair

A preparation process and rolling brushing technology, applied in the field of rolling brushing, can solve the problems of uneven brushing of walls or furniture, affecting the effect of house decoration, difficulty in meeting market demands, etc., and achieve uniform brushing of walls or furniture. , The effect of high market promotion value and meeting market demand

Inactive Publication Date: 2018-01-09
ZAOZHUANG ZHENGHE BRUSH MAKING CO LTD
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing roller bristles are generally made of wool, which not only has a high price and is difficult to meet the market demand; but also has the disadvantages of poor slurry absorption and poor antibacterial effect, and it is easy to make the painted wall or furniture brushed unevenly. Affect the effect of house decoration

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A kind of preparation technology of nylon roller brush pile, comprises the following steps:

[0025] (1) Weigh the following raw materials in parts by weight: 100 parts of nylon masterbatch, 0.05 parts of vitamin C, 0.01 part of vitamin E, 0.5 parts of niacin, 2 parts of jellyfish powder, 8 parts of PBT particles, 2 parts of nano-silver particles, 2 parts of pearl powder, 2 parts of traditional Chinese medicine residue, 2 parts of dry powder of aloe bark, 3 parts of aluminum oxide, 2 parts of straw powder, 2 parts of kaolin, 0.1 part of nano-titanium oxide, 0.1 part of nano-zinc oxide;

[0026] (2) Mix nylon masterbatch, vitamin E, jellyfish powder, PBT particles, nano-silver particles, nano-pearl powder, kaolin, nano-titanium oxide and nano-zinc oxide, and mix at 225°C for 1 hour to obtain mixture A;

[0027] (3) Add niacin, dry aloe bark powder, alumina, traditional Chinese medicine residue and straw powder to mixture A, and mix at 225°C for 25 minutes to obtain mixtu...

Embodiment 2

[0032] A kind of preparation technology of nylon roller brush pile, comprises the following steps:

[0033] (1) Weigh the following raw materials in parts by weight: 180 parts of nylon masterbatch, 0.2 parts of vitamin C, 0.7 parts of vitamin E, 2 parts of niacin, 5 parts of jellyfish powder, 20 parts of PBT particles, 6 parts of nano silver particles, 7 parts of pearl powder, 6 parts of traditional Chinese medicine residue, 6 parts of dry powder of aloe bark, 8 parts of aluminum oxide, 7 parts of straw powder, 7 parts of kaolin, 1 part of nano-titanium oxide, and 1 part of nano-zinc oxide;

[0034] (2) Mix nylon masterbatch, vitamin E, jellyfish powder, PBT particles, nano-silver particles, nano-pearl powder, kaolin, nano-titanium oxide and nano-zinc oxide, and mix at 250°C for 2 hours to obtain mixture A;

[0035] (3) Add niacin, dry aloe bark powder, alumina, traditional Chinese medicine residue and straw powder to mixture A, and mix at 235°C for 40 minutes to obtain mixtur...

Embodiment 3

[0040] A kind of preparation technology of nylon roller brush pile, comprises the following steps:

[0041] (1) Weigh the following raw materials in parts by weight: 160 parts of nylon masterbatch, 0.1 part of vitamin C, 0.1 part of vitamin E, 1.2 parts of niacin, 2.5 parts of jellyfish powder, 11 parts of PBT particles, 4 parts of nano silver particles, nano 5 parts of pearl powder, 4 parts of traditional Chinese medicine residue, 4 parts of dry powder of aloe bark, 5 parts of aluminum oxide, 5 parts of straw powder, 5 parts of kaolin, 0.4 parts of nano-titanium oxide, and 0.5 part of nano-zinc oxide;

[0042] (2) Mix nylon masterbatch, vitamin E, jellyfish powder, PBT particles, nano-silver particles, nano-pearl powder, kaolin, nano-titanium oxide and nano-zinc oxide, and mix at 232°C for 1.7 hours to obtain mixture A;

[0043] (3) Add niacin, dry aloe bark powder, alumina, traditional Chinese medicine residue and straw powder to mixture A, and mix at 228°C for 30 minutes to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a process for preparing nylon roller brush hair. The process comprises the following steps: (1) weighing various raw materials for later use; (2) mixing a nylon master batch, vitamin E, jellyfish powder, PBT particles, nano-silver particles, nano pearl powder, kaolin, nanometer titania and nano-zinc oxide so as to obtain a mixture A; (3) adding nicotinic acid, dried aloe husk powder, alumina, traditional Chinese medicine residues and straw powder into the mixture A so as to obtain a mixture B, and drawing; (4) cutting into sections and cleaning; (5) dyeing, fixing and adding vitamin C and a sodium silicate solution; and (6) cleaning, dewatering, and drying, thereby obtaining the product. The brush hair disclosed by the invention is prepared from nylon and other rawmaterials, and is low in cost, excellent in slurry absorption property, excellent in antibacterial effect, non-toxic in raw materials, environment-friendly, safe and high in market popularization value.

Description

technical field [0001] The invention relates to the technical field of brushed fleece, in particular to a preparation process of nylon brushed fleece. Background technique [0002] At present, when the house is decorated and decorated, the wall surface needs to be painted, and a roller brush is generally used. The roller brush is the most labor-saving and time-saving brush tool due to its wide range of rolling surfaces, especially when it is connected with an extension rod, it can easily paint high places on the wall or ceiling. There are three types of roller brushes: long hair, medium hair and short hair. Different roller brushes will produce different effects, and the long-haired roller will produce some fine textures, which have a concave and convex feeling, similar to the texture effect. After brushing with a short-haired roller, the paint surface is relatively uniform, smooth, without unevenness, and the middle hair is in between. [0003] The existing roller bristl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/90D01F1/10D06M11/79D06M13/228D06P3/04D06M101/34
Inventor 孙鹏孙中华
Owner ZAOZHUANG ZHENGHE BRUSH MAKING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com