Polymer composite fiber summer sleeping mat and preparation method thereof

A composite fiber and polymer technology, applied in fiber processing, fiber chemical characteristics, rayon manufacturing, etc., can solve the problems of low strength, high hardness, low comfort, etc., and achieve the effect of improving strength

Inactive Publication Date: 2018-01-12
宁波黄古林工艺品有限公司
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Mat is an essential item for modern household. Traditional mats are made of grass, bamboo and other materials. This kind of mat has high hardness, low comfort, poor sweat absorption performance, and after absorbing sweat, its strength becomes lower and its service life is shortened.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of polymer composite fiber summer mat provided by the present embodiment comprises a mat body, the mat body is woven from warp threads and weft threads, the weft threads are modal fibers, and the modal fibers are 100 parts by weight of modal The melt contains 70 parts of polylactic acid, 0 parts of nylon, 5 parts of flame retardant, 5 parts of crosslinking agent, 5 parts of calcium carbonate and 10 parts of silicon dioxide;

[0020] The warp thread is formed by twisting polyester viscose composite fiber, and the polyester viscose composite fiber includes polyester fiber and viscose fiber, wherein the polyester fiber is the core thread, the viscose fiber is coated on the outside of the polyester fiber, and the polyester fiber The weight ratio of fiber and viscose fiber is 1:1, and the composition of above-mentioned polyester fiber comprises 80 parts of polyester chips, 3 parts of titanium dioxide, 6 parts of lanthanum nitrate and 3 parts of nano-alumina by parts by...

Embodiment 2

[0031] The polymer composite fiber mat provided in this embodiment, its raw material and preparation method are roughly the same as in Example 1, the main difference is that in this embodiment, the modal fiber is in the melt of 100 parts by weight of modal Contains 50 parts of polylactic acid, 20 parts of nylon, 1 part of flame retardant, 3 parts of crosslinking agent, 2 parts of calcium carbonate and 5 parts of silicon dioxide.

[0032] The polymer composite fiber mat prepared in this example has good wear durability, and the tensile strength is 57 MPa.

Embodiment 3

[0034] The polymer composite fiber mat provided in this embodiment, its raw material and preparation method are roughly the same as in Example 1, the main difference is that in this embodiment, the modal fiber is in the melt of 100 parts by weight of modal Contains 60 parts of polylactic acid, 30 parts of nylon, 3 parts of flame retardant, 4 parts of crosslinking agent, 5 parts of calcium carbonate and 10 parts of silicon dioxide.

[0035] The polymer composite fiber mat prepared in this example has good wear durability and a tensile strength of 52 MPa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polymer composite fiber summer sleeping mat. The summer sleeping mat comprises a mat body, and the mat body is formed by weaving warp and weft, wherein the weft is modal fiber, and the warp is formed by twisting polyester viscose composite fiber; the polyester viscose composite fiber comprises polyester fiber and viscose fiber, the polyester fiber is core yarn, and the viscose fiber wraps the polyester fiber. The weft of the obtained polymer composite fiber summer sleeping mat is the modal fiber, the modal fiber is mixed with polylactic acid fiber and polyamide fiber,and the advantages of the modal fiber, the polylactic acid fiber and the polyamide fiber are integrated, so that the strength, wear resistance and flame resistance of the weft are improved. In addition, the warp of the polymer composite fiber summer sleeping mat is formed by twisting the polyester viscose composite fiber, titanium dioxide and aluminium oxide in the polyester viscose composite fiber can improve the strength of the warp, and negative ion powder is used for releasing negative ions.

Description

technical field [0001] The invention relates to a mat, in particular to a polymer composite fiber summer mat and a preparation method thereof. Background technique [0002] Mat is an essential product for modern living and home furnishing. Traditional mats are made of grass, bamboo and other materials. This kind of mat has high hardness, low comfort, poor sweat absorption performance, and the strength becomes lower after sweat absorption, and the service life is shortened. Contents of the invention [0003] The object of the present invention is to provide a polymer composite fiber mat with strong wear resistance and comfort and a preparation method thereof in order to solve the above-mentioned deficiencies in the prior art. [0004] In order to achieve the above object, a polymer composite fiber summer mat designed by the present invention includes a mat body, the mat body is woven from warp threads and weft threads, the weft threads are modal fibers, and the modal fibers...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D03D15/00D03D15/12D01D5/34D01F8/14D01F8/12D01F1/10D01F1/07D01F6/92
Inventor 俞斌
Owner 宁波黄古林工艺品有限公司