Organic small molecule electron transport material and preparation method and application thereof
A technology of electron transport materials and small molecules, which is applied in the field of organic small molecule electron transport materials and their preparation, can solve problems such as unfavorable device stability, achieve good film morphology stability, and weaken triplet exciton-polaron Annihilation, easy to purify effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0050] The structural formula of the small organic molecule electron transport material of the present embodiment is as follows:
[0051]
[0052] The preparation method of the organic small molecule electron transport material PBI-p-Phen of the present embodiment comprises the following steps:
[0053] Step 1: Preparation of 4-bromo-N-(2-(aniline)phenyl)benzamide (1), the reaction equation is as follows:
[0054]
[0055] O-aminodiphenylamine (3g, 16.3mmol) and p-bromobenzoyl chloride (4.3g, 19.53mmol) were dissolved in a mixed solvent of dichloromethane and triethylamine (50ml, 6:1v / v), under N 2 Under the atmosphere, the reaction was stirred in an ice bath for 8 hours. After the reaction was completed, dichloromethane and triethylamine were distilled off under reduced pressure, dissolved in dichloromethane, added with distilled water and extracted with dichloromethane. The obtained organic layer was dried with anhydrous magnesium sulfate and filtered, dichloromethane ...
Embodiment 2
[0092] In this embodiment, except the following features, all the other features are the same as in Embodiment 1:
[0093] Mixed solvent (50ml, 4:1 v / v) of dichloromethane and triethylamine in step (1).
[0094] The test results of this embodiment are similar to those of Embodiment 1, and will not be repeated here.
Embodiment 3
[0096] In this embodiment, except the following features, all the other features are the same as in Embodiment 1:
[0097] The reaction temperature in step (2) is 80°C.
[0098] The test results of this embodiment are similar to those of Embodiment 1, and will not be repeated here.
PUM
Property | Measurement | Unit |
---|---|---|
glass transition temperature | aaaaa | aaaaa |
wavelength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com