Modified ABS composite material for remote control shell

A composite material and remote control technology, applied in the field of modified ABS composite materials, can solve the problems of internal component damage, drop, indoor floor damage, etc., and achieve the effects of facilitating processing, prolonging service life, and increasing glass transition temperature

Inactive Publication Date: 2018-01-19
天长市天利达电子厂
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The usual TV remote control generally uses a plastic shell, which not only has high hardness, but also has a smooth surface. With frequent use, it i

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0013] Example 1

[0014] A modified ABS composite material for remote control shells, the raw materials of which by weight include: 80 parts of modified ABS resin, 50 parts of polyphenylene sulfide, 2 parts of compatibilizer, 4 parts of diphenyl monooctyl phosphate, 1.5 parts of tricresyl phosphate, 60 parts of filler, 2 parts of coumarone resin, 4 parts of antioxidant.

Example Embodiment

[0015] Example 2

[0016] A modified ABS composite material for remote control shells, the raw materials of which by weight include: 100 parts of modified ABS resin, 30 parts of polyphenylene sulfide, 4 parts of compatibilizer, 2 parts of diphenyl monooctyl phosphate, 2.5 parts of tricresyl phosphate, 50 parts of filler, 4 parts of coumarone resin, 2 parts of antioxidant.

[0017] The modified ABS resin is prepared by the following process: irradiating the ABS resin, adding polybutadiene, heating and stirring, adding polyamide and continuing to stir to obtain the modified ABS resin.

Example Embodiment

[0018] Example 3

[0019] A modified ABS composite material used for remote control shells. Its raw materials include, by weight, 85 parts of modified ABS resin, 45 parts of polyphenylene sulfide, 2.5 parts of compatibilizer, 3.5 parts of diphenyl monooctyl phosphate, 1.8 parts of tricresol phosphate, 58 parts of fillers, 2.5 parts of coumarone resin, 3.5 parts of antioxidants.

[0020] The filler includes 20 parts by weight of mica powder and 30 parts of nano white carbon black. The antioxidant includes 0.8 parts by weight of 2,6-tertiary butyl-4-methylphenol and 2 parts by dodecyl alcohol ester.

[0021] The modified ABS resin is prepared by the following process: 90 parts of ABS resin are irradiated by weight for 15 minutes, the irradiation power is 22kGy, 30 parts of polybutadiene are added, and the temperature is raised to 195°C and stirred for 50 minutes, and the stirring speed is 950r / min. Add 25 parts of polyamide and continue stirring for 25 minutes to obtain a modified AB...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a modified ABS composite material for a remote control shell. The modified ABS composite material comprises raw materials in parts by weight as follows: 80-100 parts of modified ABS resin, 30-50 parts of polyphenylene sulfide, 2-4 parts of a compatilizer, 2-4 parts of diphenyl octyl phosphate, 1.5-2.5 parts of tricresyl phosphate, 50-60 parts of filler and 2-4 parts of coumarone indene resin and 2-4 parts of an antioxidant, wherein the compatilizer is prepared with the following process: ABS resin is subjected to irradiation treatment, polybutadiene is added, the mixture is heated and stirred, polyamide is added, the mixture is stirred continuously, and the modified ABS resin is obtained. The modified ABS composite material for the remote control shell is high in hardness, has excellent impact resistance, surface scratch resistance and flame retardance, is high in thermal decomposition temperature and glass transition temperature, can meet requirements of plastics for the remote control shell and has high popularization and application values.

Description

technical field [0001] The invention relates to the technical field of remote controllers, in particular to a modified ABS composite material used for remote controller shells. Background technique [0002] With the development of modern society, TV is widely used in various fields, and as an accessory product of TV, the TV remote control has also become a part of people's life. A common TV remote control generally adopts a plastic shell, which not only has high hardness, but also has a smooth surface. With frequent use, it is easy to drop from a high place, which not only causes certain damage to the indoor floor, but also easily causes damage to internal components. As an indoor TV remote control, we hope to add some new functions to its shell. Under the premise of meeting a certain hardness, it has good toughness and high impact resistance, so that the TV remote control can be closer to people's lives and satisfy people. needs. Contents of the invention [0003] Based...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L55/02C08L81/02C08L45/02C08L47/00C08L77/00C08K13/02C08K5/523C08K3/34C08K3/36C08K5/13C08J3/28
Inventor 张晓斌
Owner 天长市天利达电子厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap