Preparation method for flame retardant building block
A technology for building blocks and fly ash, which is applied in the field of preparing flame-retardant building blocks, can solve the problems of low heat resistance temperature, complicated process, poor safety, etc., and achieves good flame-retardant effect, simple production process, product quality and performance. boosted effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0019] A method for preparing a flame retardant block, comprising the following steps:
[0020] After the raw materials are mixed in proportion, bricks are formed on a 630T friction brick press, sintered at 1180°C for 3 hours under a pressure of 3T, and then heated to 1300°C for 1.5 hours to form bricks;
[0021] Described block comprises the following components by weight percentage:
[0022] Guangxi white clay 12%
[0023] Fly ash particle size ≤ 1mm 15%
[0024] Fly ash 100μm<particle size≤1mm 55%
[0025] Andalusite Purity above 55% Mesh size 200 mesh 5%
[0026] Spinel balance.
Embodiment 2
[0028] A method for preparing a flame retardant block, comprising the following steps:
[0029] After the raw materials are mixed in proportion, bricks are formed on a 630T friction brick press, sintered at 1180°C for 7 hours under a pressure of 3T, and then heated to 1300°C for 1 hour to form bricks.
[0030] Described block comprises the following components by weight percentage:
[0031] Guangxi white clay 15%
[0032] Fly ash particle size ≤ 100 microns 10%
[0033] Fly ash 100 microns < particle size ≤ 300 microns 54.3%
[0034] Andalusite Purity above 55% Mesh size 200 mesh 10%
[0035] Spinel balance.
Embodiment 3
[0037] A method for preparing a flame retardant block, comprising the following steps:
[0038] After the raw materials are mixed in proportion, bricks are formed on a 630T friction brick press, sintered at 1200°C for 5 hours under a pressure of 5T, and then heated to 1300°C for 1 hour to form bricks.
[0039] Described block comprises the following components by weight percentage:
[0040] Guangxi white clay 15%
[0041] Fly ash particle size ≤ 100 microns 15%
[0042] Fly ash 100 microns < particle size ≤ 300 microns 40%
[0043] Andalusite Purity above 55% Mesh size 200 mesh 13%
[0044] Spinel balance.
PUM
Property | Measurement | Unit |
---|---|---|
flame retardant | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com