Treatment method for enhancing durability of clutch friction plate

A processing method and friction plate technology, applied in the field of auto parts, can solve the problems of slippage, ablation and plastic deformation, surface fracture of the friction plate, etc., and achieve the effects of not easy to scratch, large heat capacity, and enhanced durability

Inactive Publication Date: 2018-02-02
HEFEI CITY TENVER PRECISION CASTING
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The friction plate of the clutch is made of asbestos, metal wire and other materials. With the increasing power, speed and load of the car, the operating conditions are increasingly harsh, and higher requirements are put forward for the performance of the friction plate; when working for a long time or Under extreme working conditions, faults such as fracture, slip, ablation and plastic deformation of the friction plate surface caused by abnormal friction are prone to occur. Research shows that the durability of the friction plate has an important impact on the performance of the clutch and even the entire vehicle; therefore , inventing a method that can effectively enhance the durability of clutch friction plates is of great significance to the development of the automotive field

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] In the embodiment of the present invention, a treatment method for enhancing the durability of clutch friction plates, the specific method is as follows:

[0016] (1) Submerge the clutch friction plate in an aqueous solution of 8.8% copper acetate for 28 minutes, heat and soak it for 28 minutes, pass it through ultrasonic waves for ultrasonic treatment, take out the drained liquid, put it into steam treatment at a temperature of 77°C for 440 seconds, and heat at 3.3°C / min Raise the temperature to 104°C and continue the steam treatment for 500s, take it out, and get the pretreated clutch friction plate;

[0017] (2) Dry the pretreated clutch friction plate for 10 minutes in a microwave, immerse in the coating solution for 8 minutes, take it out, dry it in a second microwave for 18 minutes, take it out, and vacuum it for 55 minutes at a vacuum degree of 140 MPa;

[0018] The coating liquid is made of the following raw materials in parts by weight: 11 parts of carboxymethy...

Embodiment 2

[0023] In the embodiment of the present invention, a treatment method for enhancing the durability of clutch friction plates, the specific method is as follows:

[0024] (1) Submerge the clutch friction plate in a 9% copper acetate aqueous solution for 30 minutes, heat and soak it for 30 minutes, pass it through an ultrasonic wave for ultrasonic treatment, take out the drained liquid, put it into a steam treatment at a temperature of 79°C for 450s, and heat it at a temperature of 3.5°C / min. Heat up to 106°C and continue steaming for 510s, take it out, and get the pretreated clutch friction plate;

[0025] (2) Dry the pretreated clutch friction plate for 11 minutes in a microwave, immerse in the coating solution for 9 minutes, take it out, dry it in a second microwave for 19 minutes, take it out, and vacuum it for 58 minutes at a vacuum degree of 150 MPa;

[0026] The coating liquid is made of the following raw materials in parts by weight: 11.5 parts of carboxymethyl cellulose...

Embodiment 3

[0031] In the embodiment of the present invention, a treatment method for enhancing the durability of clutch friction plates, the specific method is as follows:

[0032] (1) Submerge the clutch friction plate in an aqueous solution of 9.2% copper acetate for 32 minutes, heat and soak it for 32 minutes, pass it through ultrasonic waves for ultrasonic treatment, take out the drained liquid, put it into steam treatment at a temperature of 81°C for 460 seconds, and heat at 3.7°C / min Heat up to 108°C and continue steaming for 520s, take it out, and get the pretreated clutch friction plate;

[0033] (2) Dry the pretreated clutch friction plate for 12 minutes in a microwave, immerse in the coating solution for 10 minutes, take it out, dry it in a second microwave for 20 minutes, take it out, and vacuum it for 60 minutes at a vacuum degree of 160 MPa;

[0034] The coating liquid is made of the following raw materials in parts by weight: 12 parts of carboxymethyl cellulose, 9 parts of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of automobile parts, in particular to a treatment method for enhancing the durability of clutch friction plates. Take out, steam treatment, take out to get the pre-treated clutch friction plate; (2) microwave the pre-treated clutch friction plate for one time, immerse it in the coating solution for 8~10min, take out, second microwave dry treatment, take out, vacuum treatment The treated clutch friction plate not only has a sufficiently high and stable friction coefficient, the difference between the static friction coefficient and the dynamic friction coefficient is reduced, and the friction coefficient basically does not change with the external conditions, and has good thermal conductivity, large heat capacity and good performance. High temperature mechanical strength, and has good wear resistance and anti-adhesion, not easy to scratch the surface of the counterpart, low noise and vibration, effectively ensuring the reliability of the clutch friction plate transmission system.

Description

technical field [0001] The invention belongs to the technical field of auto parts, in particular to a treatment method for enhancing the durability of clutch friction plates. Background technique [0002] The friction plate of the clutch is made of asbestos, metal wire and other materials. With the increasing power, speed and load of the car, the operating conditions are increasingly harsh, and higher requirements are put forward for the performance of the friction plate; when working for a long time or Under extreme working conditions, faults such as fracture, slip, ablation and plastic deformation of the friction plate surface caused by abnormal friction are prone to occur. Research shows that the durability of the friction plate has an important impact on the performance of the clutch and even the entire vehicle; therefore , inventing a method that can effectively enhance the durability of clutch friction plates is of great significance to the development of the automotiv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): F16D69/02C09D133/04C09D7/61C09D7/63C09D7/65
CPCF16D69/02C08K2201/014C09D133/04F16D2200/0034F16D2250/0046F16D2300/02F16D2300/10C08L1/286C08K13/02C08K5/098C08K3/38C08K3/28
Inventor 孙爱琴
Owner HEFEI CITY TENVER PRECISION CASTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap