Anti-precipitation modified silicon dioxide, preparation method thereof and application of modified silicon dioxide

A silicon dioxide and anti-precipitation technology, applied in coatings and other directions, can solve the problems of insufficient dispersion of silicon dioxide, failure to meet application performance, and reduced proportion of silicon dioxide, etc., to achieve superior anti-sedimentation performance and uniform modification treatment , The effect of pigment absorption balance

Active Publication Date: 2018-02-09
北京航天赛德科技发展有限公司
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Due to the natural sedimentation process of silica in the resin, as time goes by, silica gradually settles to the bottom of the storage tank, the content of silica in the surface coating decreases, and the silica that can play a role in the film-forming substance A lower proportion of silicon, either as a matting agent or as an ink absorber, will lead to changes in the final application effect
[0004] The existing silica modification treatment methods are mostly hydrophobic modification treatment. However, the silica products after hydrophobic treatment can only be suspended on the surface of the coating in the water-based coating, and cannot fully disperse the silica in all layers of the coating. , making it unusable, therefore, additional modification treatment is required for water-based coatings
At the same time, in oil-based coatings, only through hydrophobic modification to obtain non-sedimented silica additives, it is often accompanied by a significant decrease in extinction efficiency, which cannot meet the requirements of application performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] A modified silicon dioxide modified by an acrylic acid copolymer can be prepared by the following method:

[0044]Add 100 kg of silica substrate into the double power mixer, the silica substrate selected is silica dry powder (i.e. white carbon black dry powder) prepared by precipitation method, keep mixed state, stir for 10min, then acrylic acid copolymer 1kg of DISPER2008 and 0.5kg of organic solvent are stirred evenly, atomized by a pressure pump, sprayed evenly into the mixer, kept stirring for 2.5h, and the mixed material is subjected to ultra-fine airflow pulverization, and the average particle size is controlled to 3.5μm to obtain modified Silica finished product 1, can be used as an oil paint additive.

[0045] Wherein, the organic solvent refers to a mixture of the following components in mass percentage: 75% xylene, 15% cyclohexanone and 10% ethylene glycol. Most of the organic solvent is volatilized during the superjet milling process, and the addition of the...

Embodiment 2

[0047] A modified silicon dioxide modified by a polycarboxylic acid copolymer can be prepared by the following method:

[0048] Add 120kg of silica base material to the double power mixer, the silica base material selected is silica dry powder prepared by macroporous silica gel method, keep the mixed state, stir for 10min, mix polycarboxylic acid copolymer DISPER104 18kg with organic 10 kg of solvent was stirred evenly and atomized by a pressure pump, then evenly sprayed into the mixer, kept stirring for 3 hours, and the mixed material was subjected to ultra-fine airflow pulverization, and the average particle size was controlled to 5.5 μm to obtain the finished product 2 of modified silica. Can be used as an oil paint additive.

[0049] Wherein, the organic solvent refers to a mixture of the following components in mass percentage: 75% xylene, 10% cyclohexanone and 15% ethylene glycol. Most of the organic solvent is volatilized during the superjet milling process, and the ad...

Embodiment 3

[0051] A modified silicon dioxide modified by an acrylic copolymer, which can be prepared by the following method:

[0052] Mix and stir 300kg of silica substrate and 700kg of water to form a slurry, stir for 2 hours, add acetic acid to adjust the pH value to 4.5, stir evenly, and keep stirring. Add 30 kg of acrylic copolymer DISPER2009, keep stirring for 2 hours, dry to control the moisture content to ≤4.5%, make the slurry into a base material, and process it into a finished product with ultra-fine airflow pulverization, with an average particle size of 6.5 μm, to obtain the finished product 3 of modified silica, Can be used as water-based paint additive.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses anti-precipitation modified silicon dioxide, a preparation method thereof and an application of the modified silicon dioxide, and belongs to the field of coating additives. Silicon dioxide is modified by performance additives to prepare the modified silicon dioxide, the average particle size of the modified silicon dioxide is 1-10 micrometers, and the performance additivescomprise anti-precipitation performance additives prepared from one or more of acrylic polymer, polyacrylate copolymer, polybasic carboxylic polymer, polyether modified organic siloxane, aralkyl modified organic siloxane, organic silicon modified polyacrylic ester, high polymer polyacrylic ester containing efficient anchor groups, segmented copolymer containing pigment affine groups and modified urea. The modified silicon dioxide can meet the requirements of waterborne coatings and oily coatings for application of the storage performance of the silicon dioxide, precipitation in the long-term storage process is avoided, and final application effects cannot be affected.

Description

technical field [0001] The invention relates to the field of chemical additives, especially coating additives, and in particular to a modified silica for anti-precipitation and its preparation method and application. Background technique [0002] With the development of modern coating technology, the decorative and protective effect of coatings on substrates has derived many varieties and functions. For many types of additives in coatings, some problems will occur more or less during use. As matting agents, enhancers The application effect of silica used in thickeners or ink absorbers is closely related to the state of silica during paint storage. [0003] Due to the natural sedimentation process of silica in the resin, as time goes by, silica gradually settles to the bottom of the storage tank, the content of silica in the surface coating decreases, and the silica that can play a role in the film-forming substance A lower proportion of silicon, either as a matting agent or...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D7/62
CPCC08K3/36C08K9/08
Inventor 张忆张周赫朱晓辉程彦芬操应军李宝德刘阳
Owner 北京航天赛德科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More