Preparation method of soaping-resistant soft bath towel

A soft, bath towel technology, applied in the processing field of environmentally friendly bath towels, can solve the problems that cannot meet the softness of bath towels, anti-static wear resistance, poor dyeing performance of bamboo fiber, rough texture of bath towels, etc., achieve good reduction characteristics, improve Color retention and the effect of improving soft touch

Inactive Publication Date: 2018-02-13
JIESHOU SHUANGXIN TEXTILE
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Bath towels are commonly used daily necessities in daily life. The texture of existing bath towels is relatively rough and hard. In order to improve the antibacterial properties of products, bamboo fibers are used for fabrics to realize the antibacterial properties of bath towel fabrics. However, bamboo fiber products have single functions. It has been unable to meet the requirements of consumers for softness, anti-static, and wear resistance of bath towels. At the same time, bamboo fiber has poor dyeing performance and is easy to fade, and it cannot meet people's requirements for product appearance. Therefore, further research on bath towel products is required.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A preparation method for soap-resistant soft bath towel, comprising the following steps:

[0018] (1) By weight, take 25 parts of bamboo fiber, 18 parts of licorice fiber, 6 parts of modified sisal fiber, 4 parts of pineapple leaf fiber, and 43 parts of combed cotton, and perform blending to obtain a blended product;

[0019] The preparation method of the modified sisal fiber is as follows: mix the white pomelo pulp with water equivalent to 18 times its volume, adjust the pH value of the aqueous solution to 8.4 with sodium hydroxide, heat to boil and continue to boil for 30 minutes, then Put in the sisal fiber and keep it for 10 minutes, then take out the sisal fiber and fully dry it;

[0020] (2) Put the blended product obtained above into a vegetable dye solution with a pH value of 8.5. The initial temperature of the vegetable dye solution is 50°C, and then the temperature is raised to 60°C at a constant speed of 2°C / min, and then the temperature is continued to rise ...

Embodiment 2

[0026] A preparation method for soap-resistant soft bath towel, comprising the following steps:

[0027] (1) By weight, take 22 parts of bamboo fiber, 20 parts of licorice fiber, 4 parts of modified sisal fiber, 2 parts of pineapple leaf fiber, and 40 parts of combed cotton, and perform blending to obtain a blended product;

[0028] The preparation method of the modified sisal fiber is as follows: mix the white pomelo pulp with water equivalent to 15 times its volume, adjust the pH value of the aqueous solution to 8.5 with sodium hydroxide, heat to boil and continue to boil for 20 minutes, then Put in the sisal fiber and keep it for 8 minutes, then take out the sisal fiber and fully dry it;

[0029] (2) Put the blended product obtained above into a vegetable dye solution with a pH value of 8.2. The initial temperature of the vegetable dye solution is 50°C, and then the temperature is raised to 60°C at a constant speed of 2°C / min, and then the temperature is continued to rise a...

Embodiment 3

[0034] A preparation method for soap-resistant soft bath towel, comprising the following steps:

[0035] (1) By weight, take 28 parts of bamboo fiber, 16 parts of licorice fiber, 8 parts of modified sisal fiber, 6 parts of pineapple leaf fiber, and 46 parts of combed cotton, and carry out blending to obtain a blended product;

[0036] The preparation method of the modified sisal fiber is as follows: mix the white pomelo pulp with water equivalent to 20 times its volume, adjust the pH value of the aqueous solution to 8.2 with sodium hydroxide, heat to boil and continue to boil for 40 minutes, then Put in the sisal fiber and keep it for 12 minutes, then take out the sisal fiber and fully dry it;

[0037] (2) Put the blended product obtained above into a vegetable dye solution with a pH value of 8.8. The initial temperature of the vegetable dye solution is 50°C, and then the temperature is raised to 60°C at a constant speed of 2°C / min, and then the temperature is continued to ris...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of processing of environment-friendly bath towels, and particularly relates to a preparation method of a soaping-resistant soft bath towel. The preparationmethod comprises preparation, dyeing, color fixation and high temperature setting of blended products. Compared with the prior art, the preparation method of the soaping-resistant soft bath towel disclosed by the invention has the following advantages that a plurality of fibers are reasonably combined to obtain blended fabrics, and modified sisal fibers and pineapple fibers are beneficial for improving wear resistance of the fabrics; sisal fibers are modified before the use, so that the softness of the fabrics can be improved, water absorption performance of the fabrics is also improved, andsurface roughness of the fabrics is reduced; compared with exclusive use of bamboo fibers, combined use of the bamboo fibers and licorice fibers is advantaged in better antibacterial property; becauseof coordination of the licorice fibers and the pineapple fibers, a soft hand feel of the fabrics can be improved, and the obtained fibers are high in elasticity, have better reduction characteristic,are not shrunk after the fibers are wet, and are high in shape retention property; then coordination of variable-speed coloring and low-temperature salt water color fixation is utilized, so that thecolor retention property of the product is improved.

Description

technical field [0001] The invention belongs to the technical field of processing environment-friendly bath towels, and in particular relates to a preparation method of soap-resistant soft bath towels. Background technique [0002] Bath towels are commonly used daily necessities in daily life. The texture of existing bath towels is relatively rough and hard. In order to improve the antibacterial properties of products, bamboo fibers are used for fabrics to realize the antibacterial properties of bath towel fabrics. However, bamboo fiber products have single functions. It has been unable to meet the requirements of consumers for softness, anti-static, and wear resistance of bath towels. At the same time, bamboo fiber has poor dyeing performance and is easy to fade, and it cannot meet people's requirements for product appearance. Therefore, further research on bath towel products is needed. Contents of the invention [0003] The object of the present invention is to provide ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06P3/85D06P1/34D06P1/00D06P5/10D06M15/643D06M15/03D06M13/188D06M13/00A47K10/02D06M101/04
CPCD06P3/828A47K10/02D06M13/00D06M13/188D06M15/03D06M15/643D06M2101/04D06M2200/50D06P1/0032D06P1/34D06P5/10
Inventor 杨双建
Owner JIESHOU SHUANGXIN TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com