A kind of ultra-soft environment-friendly TPO automotive interior material and preparation method thereof

An automotive interior and environmental-friendly technology, which is applied in the field of ultra-soft and environmentally friendly TPO automotive interior materials and its preparation, can solve problems such as high hardness and hard hand feeling, achieve high-grade, reduce VOC content, and improve environmental protection. Effect

Active Publication Date: 2018-08-07
BENECKE CHANGSHUN AUTO TRIMZHANGJIAGANG
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the use of soft TPO skin formula and soft sponge formula, the feel and comfort of the final product have been greatly improved, which solves the shortcomings of traditional TPO materials with high hardness and hard hand feel, and meets consumers' soft feel for interior materials , soft touch, high-grade requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ultra-soft environment-friendly TPO automotive interior material and preparation method thereof
  • A kind of ultra-soft environment-friendly TPO automotive interior material and preparation method thereof
  • A kind of ultra-soft environment-friendly TPO automotive interior material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Such as figure 1 As shown, a kind of ultra-soft environment-friendly TPO automobile interior material is disclosed in the present embodiment, and it comprises successively from top to bottom: paint layer 1, TPO skin layer 2, sponge layer 3, base layer 4, adopts in the present embodiment The soft TPO skin and soft sponge formula improve the soft feel of the interior materials and increase the comfort of the product, and the surface is coated with soft water-based polyurethane paint, compounded with soft sponge, and the three-layer structure improves the material quality. Excellent soft performance reduces the density of the product, meets the demand for lightweight products, reduces the VOC content of materials in the car, and improves the environmental protection of the product.

[0040] Wherein, according to parts by weight, the above-mentioned TPO skin layer includes:

[0041]

[0042] Above-mentioned sponge layer comprises:

[0043]

[0044] Wherein, the rubb...

Embodiment 2

[0064] Wherein, the above-mentioned TPO skin layer includes:

[0065]

[0066] Above-mentioned sponge layer comprises:

[0067]

[0068] Wherein, the rubber in the above-mentioned TPO skin layer includes: EPDM rubber, ethylene octene rubber, ethylene-butylene rubber, ethylene-propylene rubber; the rubber in the above-mentioned sponge layer includes: nitrile rubber, silicone rubber, EPDM rubber .

[0069] The above-mentioned tackifying resin includes rosin resin, terpene resin, hydrocarbon resin, and the ring and ball softening point of the above-mentioned tackifying resin is 140-150°C.

[0070] The above-mentioned additives include: metal soaps, phenols, stearic acid complex esters, and phosphorous acid.

[0071] The above-mentioned inorganic fillers include: talcum powder, calcium carbonate, barium sulfate, montmorillonite, and nano glass microspheres, and the particle size of the above-mentioned inorganic fillers is 3500 mesh.

[0072] The above blowing agents inclu...

Embodiment 3

[0087] Wherein, the above-mentioned TPO skin layer includes:

[0088]

[0089] Above-mentioned sponge layer comprises:

[0090]

[0091] Wherein, the rubber in the above-mentioned TPO skin layer includes: EPDM rubber, ethylene octene rubber, ethylene-butylene rubber, ethylene-propylene rubber; the rubber in the above-mentioned sponge layer includes: nitrile rubber, silicone rubber, EPDM rubber .

[0092] The above-mentioned tackifying resin includes rosin resin, terpene resin, hydrocarbon resin, and the ring and ball softening point of the above-mentioned tackifying resin is 140-150°C.

[0093] The above-mentioned additives include: metal soaps, phenols, stearic acid complex esters, and phosphorous acid.

[0094] The above-mentioned inorganic fillers include: talcum powder, calcium carbonate, barium sulfate, montmorillonite, and nano glass microspheres, and the particle size of the above-mentioned inorganic fillers is 4000 mesh.

[0095] The above blowing agents inclu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an environment-friendly type TPO automobile trim material with ultra-soft quality. A TPO surface layer comprises the following components: 10-40 parts of low density polyethylene, 10-40 parts of polypropylene, 10-40 parts of tackifying resin, 30-60 parts of rubber, 1-5 parts of an auxiliary agent, 0-10 parts of an inorganic filling material, and 2-5 parts of a color master batch; and a sponge layer comprises the following components: 35-60 parts of polypropylene, 40-55 parts of a toughening material, 15-25 parts of rubber, and 20-30 parts of a foaming agent. Formulas of the soft TPO surface layer and the soft sponge layer improve soft handfeel of the trim material, and increases comfort level of the product; soft aqueous polyurethane paint which is used for surface coating, the composite soft sponge, and the three-layer structure improve soft performance of the material, reduce density of the product, satisfy the light weighting demand of the product, reduce VOC content of the material in the vehicle, and improve environmental protection performance of the product.

Description

technical field [0001] The invention relates to the field of automotive interior materials, in particular to an ultra-soft environment-friendly TPO automotive interior material and a preparation method thereof. Background technique [0002] In the interior design of automobiles, in order to achieve a certain feel and aesthetic effect on the instrument panel and door panels, some treatments are usually done on the skeleton. At present, the mainstream methods are: slush molding, polyurethane spraying or direct use of ABS skin. [0003] Taking the interior material of the instrument panel as an example, the soft material can be slush-molded polyvinyl chloride, polyolefin elastomer material, etc. In terms of texture and appearance, polypropylene injection molded parts are far from soft materials. On the other hand, the mold life of slush-molded PVC is generally short, and the interior materials contain halogens and plasticizers, which are not environmentally friendly; polyolefi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B25/08B32B27/06B32B27/20B32B27/32B32B37/15B32B38/00C08L23/16C08L23/08C08L23/06C08L23/12C08L93/04C08L45/00C08L23/00C08K13/04C08L53/02C08L25/06C08L9/02C08L83/04C08J9/10C09D175/04C09D7/61C09J7/38
CPCB32B5/18B32B25/045B32B25/08B32B27/06B32B27/065B32B27/20B32B27/32B32B37/153B32B38/0008B32B2255/10B32B2255/26B32B2266/02B32B2266/025B32B2605/08C08J9/08C08J9/103C08J9/105C08J2203/02C08J2203/04C08J2203/20C08J2323/08C08J2323/12C08J2325/06C08J2353/02C08J2423/08C08J2423/12C08J2425/06C08J2453/02C08K2201/011C08L23/00C08L23/06C08L23/0815C08L23/12C08L23/16C08L25/06C08L45/00C08L53/025C08L93/04C08L2203/14C08L2205/025C08L2205/035C08L2207/066C09D175/04C08K13/04C08L9/02C08L83/04C08L75/04C08K3/36C08K5/29
Inventor 李帅陈红梅滕大勇
Owner BENECKE CHANGSHUN AUTO TRIMZHANGJIAGANG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com