Golden glazed tile glaze

A glazed tile and glaze technology, which is applied in the field of glaze manufacturing, can solve the problems of high cost, complicated modulation process, and insufficiently bright colors, and achieves the effects of low manufacturing cost, high mechanical strength and bright colors.

Inactive Publication Date: 2018-02-16
NANNING SHENGRUN TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the preparation process of golden glazed tile glaze is relatively complicated, the cost is high, and it is very easy to prepare earthy yellow, and the color is not bright enough.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A golden glazed tile glaze is composed of the following components by weight: 58 parts of potassium albite feldspar, 10 parts of white glass, 20 parts of pearl material, 20 parts of dolomite, 15 parts of iron oxide, 15 parts of glaze fruit, 15 parts of green glass, 3 parts of tin crystal material, and 1 part of red lead; the preparation steps are as follows: A, take the raw materials according to the weight portion, add the above-mentioned raw materials into a pulverizer, and pulverize them to 300 mesh to obtain mixed particles; B, stir the mixed particles Evenly, melt at 1350°C, and keep warm for 2h; C, put into water with a temperature of 15°C to quench into a frit, and then ultrasonically vibrate for 5min to obtain the golden glazed tile glaze.

Embodiment 2

[0018] A golden glazed tile glaze is composed of the following components in parts by weight: 60 parts of potassium albite feldspar, 15 parts of white glass, 25 parts of pearl material, 25 parts of dolomite, 20 parts of iron oxide, 20 parts of glaze fruit, 20 parts of green glass, 4 parts of tin crystal material, and 3 parts of red lead; the preparation steps are as follows: A, take the raw materials according to the weight portion, add the above-mentioned raw materials into a pulverizer, and pulverize them to 320 mesh to obtain mixed particles; B, stir the mixed particles Evenly, melt at 1500°C, and keep warm for 4 hours; C, put into water with a temperature of 18°C ​​to quench into a frit, and then vibrate ultrasonically for 8 minutes to obtain the golden glazed tile glaze.

Embodiment 3

[0020] A golden glazed tile glaze is composed of the following components by weight: 59 parts of potassium albite feldspar, 12 parts of white glass, 22 parts of pearl material, 23 parts of dolomite, 18 parts of iron oxide, 18 parts of glaze fruit, 17 parts of green glass, 3.5 parts of tin crystal material, and 2 parts of red lead; the preparation steps are as follows: A, take the raw materials according to the weight portion, add the above-mentioned raw materials into a pulverizer, and pulverize them to 310 mesh to obtain mixed particles; B, stir the mixed particles uniform, melted at 1450°C, and kept warm for 3 hours; C, quenched into a frit in water with a temperature of 16°C, and then ultrasonically vibrated for 6 minutes to obtain the golden glazed tile glaze.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to golden glazed tile glaze. The golden glazed tile glaze is prepared from potash and soda feldspar, white glass, asbolite, dolomite, ferric oxide, glaze stone, green glass, tinfrit and red lead. The golden glazed tile glaze has good water resistance and weather resistance and high mechanical strength. The golden glazed tile glaze is very easy to blend, bright in color and low in production cost. The golden glazed tile glaze has good waterproof and thermal insulation effects, wide application range and good popularization value.

Description

technical field [0001] The invention relates to the technical field of glaze production, in particular to a golden glazed tile glaze. Background technique [0002] Glaze is a kind of silicate. The glaze applied on ceramics is generally made of quartz, feldspar, and clay. After grinding and adding water, it is coated on the surface of the green body and melted by roasting at a certain temperature. The temperature drops When, a glassy thin layer on the ceramic surface is formed. It makes ceramics increase mechanical strength, thermal stability, dielectric strength and prevent liquid and gas erosion. Glaze also has the functions of increasing the appearance of porcelain, making it easy to wash and wipe, and preventing it from being stained by dust. Glazed tiles are made of high-quality ore raw materials, which are screened and crushed, formed by high pressure, and fired at high temperature. It has significant advantages such as high strength, good flatness, low water absorpt...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/02
CPCC03C8/02
Inventor 符绩承吴锡银
Owner NANNING SHENGRUN TECH