Aluminum alloy for erbium-containing tank and plate manufacturing method for aluminum alloy

A technology of aluminum alloy plate and manufacturing method, which is applied in the field of manufacturing aluminum alloy and plate for erbium-containing tanks, can solve the problems of short service life of tanks, poor welding performance and corrosion resistance, etc., and achieve prolonging service life, excellent Solderability, recrystallization suppression effect

Inactive Publication Date: 2018-02-27
NORTHEAST LIGHT ALLOY CO LTD
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to solve the problem of poor welding performance and corrosion resistance of the currently used high-magnesium aluminum alloy plate, and the short service life of the tank body, and to provide an aluminum alloy for the erbium-containing tank body and a manufacturing method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0015] Specific Embodiment 1: In this embodiment, the mass percentage of each element in an aluminum alloy for an erbium-containing tank body is as follows: Mg: 4.0% to 4.9%, Mn: 0.40% to 1.00%, Er: 0.25% to 0.40%, Zr: 0.15%~0.30%, Be: 0.0005%~0.005%, Si﹤0.15%, Fe﹤0.25%, Ti<0.15%, single impurity≤0.05%, total impurity≤0.15%, the balance is Al.

[0016] The impurity elements in this embodiment originate from aluminum ingots; impurities Si﹤0.15%, Fe﹤0.25%, Ti<0.15%, other individual impurities≤0.05%, and the total impurities≤0.15%. performance is not affected.

[0017] Compared with general aluminum-magnesium alloys, the aluminum alloy for erbium-containing tanks in this embodiment can achieve the effects of grain refinement, recrystallization inhibition and solid solution strengthening due to the reasonable addition of Er element, and the addition of Zr element , refine the casting structure, change the crystal shape of the second phase, form a fine dispersed phase, and avoid ...

specific Embodiment approach 2

[0018] Specific embodiment 2: The difference between this embodiment and specific embodiment 1 is that the mass percentages of the elements in the aluminum alloy for erbium-containing tanks are as follows: Mg: 4.6%, Mn: 0.6%, Er: 0.26%, Zr: 0.16% , Be: 0.0025%, Si﹤0.15%, Fe﹤0.25%, Ti<0.15%, single impurity≤0.05%, total impurity≤0.15%, and the balance is Al. Others are the same as in the first embodiment.

specific Embodiment approach 3

[0019] Specific embodiment three: the manufacturing method of a kind of aluminum alloy sheet material for erbium-containing tank body in this embodiment comprises the following steps:

[0020] 1. Ingredients: According to the mass percentage of each element in the aluminum alloy containing erbium tank, Mg: 4.0%-4.9%, Mn: 0.40%-1.00%, Er: 0.25%-0.40%, Zr: 0.15%-0.30%, Be: 0.0005% to 0.005% and the ratio of the balance Al to weigh pure aluminum ingots, pure magnesium ingots, aluminum-manganese master alloys, aluminum-erbium master alloys, aluminum-beryllium master alloys and aluminum-zirconium master alloys;

[0021] 2. Melting: A. Add the pure aluminum ingot, aluminum-manganese master alloy and aluminum-zirconium master alloy weighed in step 1 into the melting furnace. The melting temperature is 750-800°C. When the melt temperature reaches ≥780°C, add aluminum erbium For the master alloy, after adding the aluminum-erbium master alloy, keep warm for 20 minutes and then stir for ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
lengthaaaaaaaaaa
widthaaaaaaaaaa
Login to View More

Abstract

The invention relates to aluminum alloy for an erbium-containing tank and a plate manufacturing method for the aluminum alloy, and aims to improve the welding property and the corrosion resistance ofthe alloy for the erbium-containing tank. The aluminum alloy for the erbium-containing tank comprises the following elements: Mg, Mn, Er, Zr and Be. The method comprises the following steps: (1), blending, (2), smelting, (3), casting, (4) homogenizing annealing, (5) hot rolling, and (6) saw cutting of a finished product to obtain the aluminum alloy for the erbium-containing tank. By a manufacturedalloy plate for the erbium-containing tank, the welding property and the corrosion resistance are improved while various properties of common aluminum magnesium alloy are ensured, and therefore, thealloy can meet requirements of a dangerous chemical supplies tank material. The plate manufacturing method is applied to the field of manufacturing of aluminum alloy.

Description

technical field [0001] The invention relates to an aluminum alloy for an erbium-containing tank body and a manufacturing method thereof. Background technique [0002] At present, the tank trucks used for transporting hazardous chemicals such as asphalt, methanol, and ethylene glycol are made of 6mm steel plates and weigh about 4 tons. Because the country has clear regulations on the total weight of transport vehicles, the loading capacity of steel tank trucks is limited and transportation costs increase. The aluminum alloy material is used to make the tank body, which can reduce the weight by more than 50%. The welding performance and corrosion resistance of the currently used high-magnesium aluminum alloy plates are poor, and the service life of the tank body is short. Contents of the invention [0003] The object of the present invention is to provide a kind of aluminum alloy for erbium-containing tank body and a manufacturing method thereof in order to solve the probl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/06C22C1/03C22F1/047
CPCC22C21/06C22C1/026C22C1/03C22F1/047
Inventor 贾宁吕新宇王国军王金花丛福官高新宇刘世雷韩颖刘学赵扬
Owner NORTHEAST LIGHT ALLOY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com