Nano silicon-based composite heat insulation tile shell and preparation method thereof

A technology of nano-silicon and tile shells, which is applied in heat exchange equipment, mechanical equipment, and pipelines through heat insulation protection, can solve the problems of non-fragility, low heat conduction system, brittle texture, etc., and achieve tensile strength, compression resistance, light weight, and heat conduction The effect of low coefficient

Active Publication Date: 2018-03-06
烟台科立达节能科技有限公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to solve the problems of high thermal conductivity, brittle texture and fragility of existing tile shells, and provide a nano-silicon-based composite heat-insulating tile shell with low thermal conductivity, high toughness, non-fragility, and long service life and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nano silicon-based composite heat insulation tile shell and preparation method thereof
  • Nano silicon-based composite heat insulation tile shell and preparation method thereof
  • Nano silicon-based composite heat insulation tile shell and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Example 1. Nano-silicon-based composite heat-insulating tile shell, including the following raw materials in parts by weight: 15Kg of waste high-silica cotton, 120Kg of vitrified microbeads, 5Kg of floating beads, 5Kg of attapulgite hydrosol, and 5Kg of silica hydrosol;

[0032] The attapulgite hydrosol is a high-concentration hydrosol with a mass concentration greater than 40%, which is formed by dispersing ultrafine attapulgite with a fineness of more than 800 mesh by an ultra-high-speed disperser;

[0033] The silica hydrosol is a high-concentration hydrosol with a mass concentration greater than 30%, which is formed by dispersing 20 nanometer nano-silica by an ultra-high-speed disperser;

[0034] The preparation method of the nano-silicon-based composite heat-insulating tile shell includes the following steps:

[0035] 1. Treatment of fiber cotton: use a shearing carding machine to shear and comb waste and old loose high-silica cotton to remove impurities, make the...

Embodiment 2

[0045] Example 2. Nano-silicon-based composite heat-insulating tile shell, including the following raw materials in parts by weight: 20 Kg of waste glass fiber cotton, 180 Kg of vitrified microbeads, 10 Kg of floating beads, 10 Kg of attapulgite hydrosol, and 8 Kg of silica hydrosol;

[0046] The attapulgite hydrosol is a high-concentration hydrosol with a mass concentration greater than 40%, which is formed by dispersing ultrafine attapulgite with a fineness of more than 800 mesh by an ultra-high-speed disperser;

[0047] The silica hydrosol is a high-concentration hydrosol with a mass concentration greater than 30%, which is formed by dispersing 60 nanometer nano-silica by an ultra-high-speed disperser;

[0048] The preparation method of the nano-silicon-based composite heat-insulating tile shell includes the following steps:

[0049] 1. Fiber cotton treatment: use a shearing carding machine to cut and card waste glass fiber cotton to remove impurities, make the fiber clean...

Embodiment 3

[0059] Example 3. Nano-silicon-based composite heat-insulating tile shell, including the following raw materials in parts by weight: waste ceramic fiber cotton 17.5Kg, vitrified microbeads 150Kg, floating beads 7.5Kg, attapulgite hydrosol 7.5Kg, silica hydrosol 6.5Kg;

[0060] The attapulgite hydrosol is a high-concentration hydrosol with a mass concentration greater than 40%, which is formed by dispersing ultrafine attapulgite with a fineness of more than 800 mesh by an ultra-high-speed disperser;

[0061] The silica hydrosol is a high-concentration hydrosol with a mass concentration greater than 30%, which is formed by dispersing 40 nanometer nano-silica by an ultra-high-speed disperser;

[0062] The preparation method of the nano-silicon-based composite heat-insulating tile shell includes the following steps:

[0063] 1. Fiber cotton treatment: use a shearing carding machine to cut and card waste ceramic fiber cotton to remove impurities, make the fiber clean, fluffy, and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Finenessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a nano silicon-based composite heat insulation tile shell and a preparation method thereof, and belongs to the field of heat preservation tile shells. In order to overcome theshortcomings of high heat conduction coefficient, brittleness and frangibility of the existing tile shell, the nano silicon-based composite heat insulation tile shell is prepared from the following raw materials in parts by weight: 15 to 20 parts of fiber cotton, 120 to 180 parts of glass beads, 5 to 10 parts of floating beads, 5 to 10 parts of attapulgite hydrosol and 5 to 8 parts of silica hydrosol. By adoption of the fiber cotton, the nano silicon-based composite heat insulation tile shell disclosed by the invention has tensile strength and compressive strength, is light in weight, low inheat conduction system, high in toughness, difficult to break and long in service life.

Description

technical field [0001] The invention relates to a tile shell and a preparation method thereof, in particular to a nano-silicon-based composite heat-insulating tile shell and a preparation method thereof, belonging to the field of thermal insulation tile shells. Background technique [0002] At present, the tile shells for high-temperature pipeline insulation are generally made of perlite, silicate, calcium silicate or microporous calcium silicate tile shells. The main materials of this type of tile shells are pressed from perlite and calcium silicate plus water glass glue. , so the thermal conductivity is high, the texture is brittle, fragile, and the service life is short. Contents of the invention [0003] The purpose of the present invention is to solve the problems of high thermal conductivity, brittle texture and fragility of existing tile shells, and provide a nano-silicon-based composite heat-insulating tile shell with low thermal conductivity, high toughness, non-f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B30/02F16L59/02B28B3/26C04B18/04C04B14/10C04B14/06C04B18/02C04B18/08
CPCB28B3/26C04B30/02C04B2201/20C04B2201/32C04B2201/50F16L59/028C04B14/102C04B14/064C04B18/027C04B18/082C04B18/04Y02W30/91
Inventor 李广志
Owner 烟台科立达节能科技有限公司