Steel slag iron removing method
A technology for removing iron from steel slag and magnetic separation, applied in chemical instruments and methods, magnetic separation, solid separation, etc., can solve the problem of low recovery rate of iron element and achieve good effect of iron removal
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0020] The steel slag iron removal method used in this embodiment is as follows: transport the steel slag to the industrial solid waste storage center for stacking, sprinkle tap water to moisten it when stacking, shovel it into the storage hopper by a forklift, transport it to the vibrating screen by belt, and manually pick out large pieces of stainless steel waste slag , falling into the jaw crusher with a grid of 50×50mm and crushing until the particle size is 1 mm to 5 mm, the crushed material is conveyed into the wet ball mill through the belt, and then transferred to the wet ball mill for ball milling until the particle size of the steel slag is 350 microns. The slurry mixture is transported to the shaking table for separation to obtain stainless steel pulp I; the stainless steel pulp I is transported to the electromagnetic separator for magnetic separation to remove iron to obtain stainless steel pulp II; add foaming agent to the stainless steel pulp II, mix evenly, and ad...
Embodiment 2
[0024] The steel slag iron removal method used in this embodiment is as follows: transport the steel slag to the industrial solid waste storage center for stacking, sprinkle tap water to moisten it when stacking, shovel it into the storage hopper by a forklift, transport it to the vibrating screen by belt, and manually pick out large pieces of stainless steel waste slag , the 50×50mm grid falls into the jaw crusher and crushed until the particle size is 1 mm to 5 mm. The crushed material is conveyed into the wet ball mill through the belt, and then transferred to the wet ball mill for ball milling until the particle size of the steel slag is 600 microns. The slurry mixture is transported to the shaking table for separation to obtain stainless steel pulp I; the stainless steel pulp I is transported to the electromagnetic separator for magnetic separation to remove iron to obtain stainless steel pulp II; add foaming agent to the stainless steel pulp II, mix evenly, and adjust The...
Embodiment 3
[0028] The steel slag iron removal method used in this embodiment is as follows: transport the steel slag to the industrial solid waste storage center for stacking, sprinkle tap water to moisten it when stacking, shovel it into the storage hopper by a forklift, transport it to the vibrating screen by belt, and manually pick out large pieces of stainless steel waste slag , falling into the jaw crusher with a grid of 50×50 mm and crushing until the particle size is 1 mm to 5 mm, the crushed material is conveyed into the wet ball mill through the belt, and then transferred to the wet ball mill for ball milling until the particle size of the steel slag is 200 microns. The slurry mixture is transported to the shaking table for separation to obtain stainless steel pulp I; the stainless steel pulp I is transported to the electromagnetic separator for magnetic separation to remove iron to obtain stainless steel pulp II; add foaming agent to the stainless steel pulp II, mix evenly, and a...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com