Sizing material for producing high-strength synchronous belt
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A synchronous belt and high-strength technology, applied in the field of rubber compound for producing high-strength synchronous belt, can solve the problem of high price of hydrogenated nitrile rubber, and achieve the effects of improving anti-aging performance, improving service life and reducing compound cost.
Inactive Publication Date: 2018-05-08
江西康琪实业有限公司
View PDF5 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, its main raw material, hydrogenated nitrile rubber, is expensive, nearly 300 yuan / kg, which is 10 times that of neoprene
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0014] If the total weight of various raw materials is 247.5kg, by weight, the rubber compound includes the following effective components: 100kg of neoprene rubber, 40kg of styrene-butadiene rubber, 25kg of high styrene, 5 kg of zincoxide, 4 kg of magnesium oxide, Stearic acid 1 kg, antioxidant 4010NA 1 kg, dodecanethiol 8 kg, antioxidant ODA 2 kg, antiozonant 1 kg, carbon black N762 60 kg and accelerator 0.5 kg.
[0015] When preparing rubber compound, it is necessary to mix chloroprene rubber, zinc oxide, magnesium oxide, stearic acid, antioxidant 4010NA, dodecyl mercaptan, antioxidant ODA, antiozonant, carbon black N762 and accelerator in the above parts by weight Mix evenly, pour it into a kneader and stir for 1-2 hours; the synchronous belt rubber can be obtained.
Embodiment 2
[0017] If the total weight of various raw materials is 200kg, by weight, the rubber compound includes the following effective components: neoprene rubber 79.52kg, styrene-butadiene rubber 32.32kg, high styrene 19.08kg, zinc oxide 2.9 kg, magnesium oxide 5.78 kg, stearic acid 0.58 kg, antioxidant 4010NA 0.62kg, dodecanethiol 7.94 kg, antioxidant ODA 1.92kg, antiozonant 0.94kg, carbon black N762 47.74kg and accelerator 0.66kg.
[0018] When preparing rubber compound, it is necessary to mix chloroprene rubber, zinc oxide, magnesium oxide, stearic acid, antioxidant 4010NA, dodecyl mercaptan, antioxidant ODA, antiozonant, carbon black N762 and accelerator in the above parts by weight Mix evenly, pour it into a kneader and stir for 1-2 hours; the synchronous belt rubber can be obtained. So far, the object of the present invention is accomplished.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention discloses a sizing material for producing a high-strength synchronous belt. The sizing material for producing the high-strength synchronous belt is prepared from, by weight, 37.89%-42.64% of chloroprene rubber, 14.87%-18.67% of butadiene styrene rubber, 8.14%-12.48% of high styrene rubber, 1.23%-4.35% of zincoxide, 1.14%-3.15% of magnesiumoxide, 0.26%-0.67% of stearic acid, 0.25%-0.75% of an anti-aging agent 4010 NA, 1.98%-4.87% of 1-dodecanethiol, 0.67%-1.95% of an anti-aging agent ODA, 0.24%-0.65% of antiozonant, 21.68%-26.89% of carbon black N762 and 0.14%-0.37% of accelerant. According to the sizing material for producing the high-strength synchronous belt, by synchronously using the chloroprene rubber, the butadiene styrene rubber, the high styrene rubber, stearic acid, the anti-aging agents, 1-dodecanethiol, the antiozonant, the carbon black N762 and the accelerant, the properties of the raw materials complement each other, so that the cost of the sizing materialis reduced; by adding the butadiene styrene rubber and the high styrene rubber, the toughness and the strength are improved; by adding the anti-aging agents and the antiozonant, the anti-aging performance is improved, and the service life of the synchronous belt is improved.
Description
technical field [0001] The invention belongs to the technical field of synchronous belt processing and manufacturing, and in particular relates to a rubber material for producing high-strength synchronous belts. Background technique [0002] The synchronous belt is a sealed endless belt with equally spaced teeth on the inner peripheral surface. When rotating, the power is transmitted through the meshing of the belt teeth and the gear teeth. The synchronous belt combines the advantages of belt drive, chain drive and gear drive, and has many advantages such as high transmission efficiency, accurate transmission ratio, large transmission ratio range, stable transmission, small force on the shaft, low noise, and energy saving. [0003] The timing belt is mainly composed of three parts: the timing belt film, the timing belt skeleton and the timing belt cloth layer. At present, there are two kinds of products in the production of automobile synchronous belts at home and abroad, o...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More 