Large-volume epoxy resin concrete pouring process

A kind of epoxy resin and concrete technology, which is used in construction, building structure, construction material processing and other directions to achieve the effect of maintaining high strength and strengthening weakness, reducing cost and ensuring strength

Inactive Publication Date: 2018-07-17
贵阳城市建设工程集团有限责任公司 +1
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the foregoing problems and provide a large-volume epoxy resin concrete pouring process that can ensure the strength of the concrete and maintain the advantages of high-strength and weak-reinforcing epoxy resin during large-volume construction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A kind of large-volume epoxy resin concrete pouring technique of the present invention comprises the following steps:

[0024] (1) Take by weight epoxy resin 180kg, curing agent ethylenediamine 15kg, diluent xylene 5kg, oven-dried sand, stone 500kg, cement 180kg;

[0025] (2) Heating the epoxy resin to 40°C, adding the curing agent ethylenediamine and the diluent xylene, and mechanically mixing to obtain a gelled material;

[0026] (3) Add the dried sand, stone and cement into the cementitious material, and continue mechanical mixing evenly;

[0027] (4) Build a formwork support of the required size, layer the fabric along the length direction, and the thickness of each layer of fabric is 20mm. After the fabric is completed, use an attached vibrator to vibrate until the air bubbles are completely discharged to the concrete surface. Air bubbles are removed, and the next layer of pouring must be carried out before the previous layer of epoxy resin concrete is hardened, a...

Embodiment 2

[0029] A kind of large-volume epoxy resin concrete pouring technique of the present invention comprises the following steps:

[0030] (1) Take by weight epoxy resin 380kg, curing agent ethylenediamine 36kg, diluent xylene 11kg, oven-dried sand, stone 1100kg, cement 400kg;

[0031] (2) Heating the epoxy resin to 50° C., adding the curing agent ethylenediamine and the diluent xylene, and mechanically mixing to obtain a cementitious material;

[0032] (3) Add the dried sand, stone and cement into the cementitious material, and continue mechanical mixing evenly;

[0033] (4) Build a formwork support of the required size, layer the fabric along the length direction, and the thickness of each layer of fabric is 35mm. After the fabric is completed, use an attached vibrator to vibrate until the air bubbles are completely discharged to the concrete surface. Air bubbles are removed, and the next layer of pouring must be carried out before the previous layer of epoxy resin concrete is h...

Embodiment 3

[0035] A kind of large-volume epoxy resin concrete pouring technique of the present invention comprises the following steps:

[0036] (1) Take by weight epoxy resin 400kg, curing agent ethylenediamine 40kg, diluent xylene 12kg, oven-dried sand, stone 1600kg, cement 440kg;

[0037] (2) Heating the epoxy resin to 60° C., adding the curing agent ethylenediamine and the diluent xylene, and mechanically mixing to obtain a gelled material;

[0038] (3) Add the dried sand, stone and cement into the cementitious material, and continue mechanical mixing evenly;

[0039] (4) Build a formwork support of the required size, layer the fabric along the length direction, and the thickness of each layer of fabric is 50mm. After the fabric is completed, use an attached vibrator to vibrate until the air bubbles are completely discharged to the concrete surface. Air bubbles are removed, and the next layer of pouring must be carried out before the previous layer of epoxy resin concrete is hardene...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a large-volume epoxy resin concrete pouring process which takes epoxy resin, a curing agent ethylenediamine and a diluent xylene as cementing materials, after machine-made sandand stone are dried, the machine-made sand and the stone are uniformly stirred through mechanical stirring, and layered casting and mechanical adhesion type vibration are adopted, so that internalbubbles generated by the curing agent are fully removed. The invention provides the large-volume epoxy resin concrete pouring process, the internal gas bubbles of the concrete can be fully removed, and the large-volume pouring is realized, meanwhile the strength of the concrete can be effectively guaranteed, the advantages of high strength and weak supplement of the epoxy resin are maintained, andthe cost of later-period manual repair is reduced.

Description

technical field [0001] The invention relates to a concrete pouring process, in particular to a large-volume epoxy resin concrete pouring process. Background technique [0002] Epoxy resin concrete is made of epoxy resin as the main material, mixed with an appropriate amount of curing agent, plasticizer, diluent and filler as adhesive, and sand and stone as aggregate, which are mixed, formed and cured. Composite material is a kind of pure polymer concrete in polymer concrete. [0003] It has high strength, good toughness, high impact strength, good chemical corrosion resistance, wear resistance, water resistance and frost resistance, and has high bonding strength with metal and non-metal materials, and good electrical insulation, which makes up for the tensile strength of cement concrete. Low, small tensile strain, low crack resistance, high brittleness and other shortcomings. The cured epoxy resin concrete has strong resistance to atmosphere, moisture, chemical medium, bac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/00E04G21/02
CPCC04B28/00E04G21/02C04B24/281C04B24/121C04B24/00C04B14/06C04B14/02
Inventor 郭方丽王成杰汪明星罗丽张翔宇李亚
Owner 贵阳城市建设工程集团有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com