A refractory brick and two-component technology, applied in the field of refractory materials, can solve the problems of high dosage and reduced strength of refractory bricks, and achieve high physical properties, prevent brick cracking, and reduce the amount of use.

Active Publication Date: 2018-07-20
长兴正发热电耐火材料有限公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the amount of binder added in the raw materials of the above-mentioned patent refractory bricks is relatively large (about 2-6%). Even if the binder has high temperature resistance, it still partially decomposes in a high temperature environment, thereby leaving Lower porosity, resulting in a reduction in the strength of refractory bricks

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Two-component refractory brick and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A two-component refractory brick is prepared by mixing slurry A and slurry B.

[0037] The A slurry includes the following raw materials in parts by weight: 50 parts of fused chromium oxide, 15 parts of sintered chromium oxide particles, 15 parts of chromium corundum particles, 4 parts of alumina micropowder, 4 parts of magnesia micropowder, 4 parts of zirconia micropowder, 1 part of yttrium oxide powder, 1 part of lanthanum and lanthanide metal oxide powder, 1 part of metal aluminum powder, 1 part of metal chromium powder, 1 part of metal zirconium powder, 1 part of metal yttrium powder, 1 part of resorcinol diglycidyl ether 0.5 parts of sodium dodecylbenzenesulfonate, 25 parts of ethanol, and 25 parts of water.

[0038]The B slurry includes the following raw materials in parts by weight: 50 parts of fused chromium oxide, 15 parts of sintered chromium oxide particles, 15 parts of chromium corundum particles, 4 parts of alumina micropowder, 4 parts of magnesia micropowd...

Embodiment 2

[0048] A two-component refractory brick is prepared by mixing slurry A and slurry B.

[0049] The A slurry includes the following raw materials in parts by weight: 62 parts of fused chromium oxide, 10 parts of sintered chromium oxide particles, 10 parts of chromium corundum particles, 2 parts of alumina micropowder, 6 parts of magnesia micropowder, 2 parts of zirconia micropowder, 0.1 part of yttrium oxide powder, 2 parts of lanthanum and lanthanide metal oxide powder, 0.1 part of metal aluminum powder, 2 parts of metal chromium powder, 0.1 part of metal zirconium powder, 2 parts of metal yttrium powder, 0.5 parts of resorcinol diglycidyl ether 0.1 part of sodium dodecylbenzenesulfonate, 20 parts of ethanol, and 30 parts of water.

[0050] The B slurry includes the following raw materials in parts by weight: 62 parts of fused chromium oxide, 10 parts of sintered chromium oxide particles, 10 parts of chrome corundum particles, 2 parts of alumina micropowder, 6 parts of magnesia...

Embodiment 3

[0060] A two-component refractory brick is prepared by mixing slurry A and slurry B.

[0061] The A slurry includes the following raw materials in parts by weight: 75 parts of fused chromium oxide, 10 parts of sintered chromium oxide particles, 10 parts of chrome corundum particles, 2 parts of alumina micropowder, 2 parts of magnesia micropowder, 2 parts of zirconia micropowder, 0.1 part of yttrium oxide powder, 0.1 part of lanthanum and lanthanide metal oxide powder, 0.1 part of metal aluminum powder, 0.1 part of metal chromium powder, 0.1 part of metal zirconium powder, 0.1 part of metal yttrium powder, 0.5 part of resorcinol diglycidyl ether 0.1 part of sodium dodecylbenzenesulfonate, 30 parts of ethanol, and 20 parts of water.

[0062] The B slurry includes the following raw materials in parts by weight: 75 parts of fused chromium oxide, 10 parts of sintered chromium oxide particles, 10 parts of chrome corundum particles, 2 parts of alumina micropowder, 2 parts of magnesia...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of refractory materials, and discloses a two-component refractory brick and a production method thereof. The brick is produced from a slurry A and a slurry B; the slurry A includes fused chromium oxide, sintered chromium oxide particles, chrome corundum particles, alumina micro-powder, magnesium oxide micro-powder, zirconia micro-powder, yttrium oxide micro-powder, lanthanum and / or lanthanide metal oxide micro-powder, metallic aluminum micro-powder, metallic chromium micro-powder, metallic zirconium micro-powder, metallic yttrium micro-powder, resorcinol diglycidyl ether, sodium dodecyl benzene sulfonate, ethanol and water; and the slurry B includes the fused chromium oxide, sintered chromium oxide particles, chrome corundum particles, alumina micro-powder, magnesium oxide micro-powder, zirconia micro-powder, yttrium oxide micro-powder, lanthanum and / or lanthanide metal oxide micro-powder, metallic aluminum micro-powder, metallic chromium micro-powder, metallic zirconium micro-powder, metallic yttrium micro-powder, a cationic photocuring initiator, tetradecyltrimethylammonium bromide, ethanol and water. The two slurries are adopted to reduce the use amount of a binder and improve the physical properties of the refractory brick.

Description

technical field [0001] The invention relates to the field of refractory materials, in particular to a two-component refractory brick and a preparation method thereof. Background technique [0002] High chrome bricks have the advantages of high refractoriness and mechanical strength, low thermal expansion coefficient, strong wear resistance and slag resistance, and good thermal shock stability, which are incomparable to ordinary refractory bricks. [0003] The applicant's prior patent CN201510023179.7 discloses a metal high chromium brick, which is composed of fused chromium oxide, sintered chromium oxide particles, chromium corundum particles, alumina micropowder, magnesia micropowder, zirconia micropowder, yttrium oxide micropowder, It is composed of lanthanum and lanthanide metal oxide powder, metal aluminum powder, metal chromium powder, metal zirconium powder, metal yttrium powder and binder. The invention also provides a method for preparing metal high-chrome bricks, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/12C04B35/632C04B35/66
CPCC04B35/12C04B35/632C04B35/66C04B2235/3206C04B2235/3217C04B2235/3224C04B2235/3227C04B2235/3244C04B2235/3255C04B2235/40C04B2235/402C04B2235/404C04B2235/5436C04B2235/77C04B2235/96C04B2235/9607
Inventor 周成周益城周成平
Owner 长兴正发热电耐火材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap