Antiwear self-repairing lubricating oil additive and preparation method thereof

A lubricating oil additive and self-repairing technology, which is applied in the direction of additives, lubricating compositions, petroleum industry, etc., can solve the problems of inability to achieve zero-wear material repairing effect, achieve good anti-wear self-repairing effect, prolong service life, Good anti-aging and anti-oxidation properties

Inactive Publication Date: 2018-07-27
艾润工业介质(镇江)有限公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, most lubricants improve their performance by adding a variety of lubricating additives, while traditional additives achieve go

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] An anti-wear and self-repairing lubricant additive, the preparation steps are as follows:

[0023] (1) Preparation of anti-wear agent: mix dibenzyl disulfide and di-n-butyl phosphite in a mass ratio of 2:3, or put it into a ball mill to mix, and place it in a three-roll mill for grinding, time 45 Minutes to get the anti-wear agent;

[0024] (2. Preparation of antioxidant: place the zinc dialkyldithiocarbamate in a three-roll mill for grinding for 1 hour to obtain the antioxidant;

[0025] (3) Preparation of additives: After heating 10 parts of diisooctyl molybdenum dithiophosphate, 18 parts of triphenyl phosphate, and 15 parts of anti-wear agent to 180-200 degrees Celsius, it is carried out by turning over the seasoning drum and mixing with compressed air. Mix for 1 hour, add 10 parts of antioxidant, and continue mixing for 40 minutes to obtain the finished additive product after mixing evenly.

Embodiment 2

[0027] An anti-wear and self-repairing lubricant additive, the preparation steps are as follows:

[0028] (1) Preparation of anti-wear agent: Put sulfide isobutylene, sodium metaborate, and potassium metaborate into a ball mill at a mass ratio of 2:4:1:3, and then put them in a three-roll mill for grinding, for 45 minutes , Get antiwear agent;

[0029] (2. The preparation of antioxidant: β~(3,5-di-tert-butyl~4-hydroxyphenyl) n-octadecyl propionate, zinc dialkyldithiocarbamate, dialkyl After mixing the molybdenum dithiocarbamate and antimony dialkyldithiocarbamate in a mass ratio of 1:2:1:4, they are placed in a three-roll mill for grinding for 1 hour to obtain an antioxidant;

[0030] (3) Preparation of additives: After heating 10 parts of diisooctyl molybdenum dithiophosphate, 18 parts of triphenyl phosphate, and 15 parts of anti-wear agent to 180 degrees Celsius, they are mixed by turning over a seasoning drum and mixing with compressed air. It takes 1 hour to mix evenly, add 10 ...

Embodiment 3

[0032] An anti-wear and self-repairing lubricant additive, the preparation steps are as follows:

[0033] (1) Preparation of anti-wear agent: Put sulfide isobutylene, sodium metaborate and potassium metaborate into a ball mill at a mass ratio of 5:6:4:7, and then put them into a three-roll mill for grinding, for 55 minutes , Get antiwear agent;

[0034] (2. The preparation of antioxidant: β~(3,5-di-tert-butyl~4-hydroxyphenyl) n-octadecyl propionate, zinc dialkyldithiocarbamate, dialkyl After mixing the molybdenum dithiocarbamate and antimony dialkyldithiocarbamate in a mass ratio of 2:5:3:8, they are placed in a three-roll mill for grinding for 2 hours to obtain an antioxidant;

[0035] (3) Preparation of additives: After heating 22 parts of diisooctyl molybdenum dithiophosphate, 28 parts of triphenyl phosphate, and 20 parts of anti-wear agent to 200 degrees Celsius, it is mixed by turning over the seasoning drum and mixing with compressed air. The time is 2 hours, after mixing eve...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

An antiwear self-repairing lubricating oil additive is composed of the following components in parts by mass: 10-22 parts of molybdenum diisooctyl dithiophosphate, 18-28 parts of triphenyl phosphate,15-20 parts of an antiwear agent and 10-30 parts of an antioxidant. With use of special antiwear agent components, the antiwear agent composed of sulfurized isobutylene, dibenzyl disulfide, di-n-butylphosphite, sodium metaborate, and a potassium metaborate material is added into lubricating oil, the lubricating oil is subjected to a chemical reaction with a metal surface, and a chemical reactionfilm is produced, so a lubricating effect is played, scratching of the metal surface is prevented, even fusion welding is prevented, the self lubricating performance of the lubricating oil is greatlyimproved, and the antiwear self-repairing effect is good. With special preparation of the multi-component antioxidant, the antiwear self-repairing lubricating oil additive has excellent anti-aging andanti-oxidation performance, is added into the lubricating oil, can highly delay the service life of the lubricating oil and improves the practical performance.

Description

Technical field [0001] The invention particularly relates to an anti-wear and self-repairing lubricant additive and a preparation method thereof. Background technique [0002] Friction and wear is a common phenomenon in the friction process. According to statistics, more than one-third of the world's primary energy loss comes from friction. Therefore, it is of great significance to reduce the economic loss caused by friction and wear. Lubrication is an effective technology to reduce friction, reduce or avoid wear. [0003] At present, most lubricants use a variety of lubricating additives to improve their performance, while traditional additives achieve good tribological performance through physical adsorption and chemical reactions. They cannot achieve zero wear and damage to materials. To repair. Lubricating additives determine the performance of lubricants to a large extent. The development and development of new self-repairing lubricating additives to blend lubricating oils, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M141/10C10N30/06C10N30/10
CPCC10M141/10C10M2201/087C10M2207/289C10M2219/022C10M2219/068C10M2219/083C10M2223/041C10M2223/045C10N2030/06C10N2030/10C10N2010/10C10N2010/12C10N2010/02C10N2010/04
Inventor 杨爱华李树白乔奇伟吴东恩
Owner 艾润工业介质(镇江)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap