High-carbon and low-alloy steel for grinding balls and manufacturing method thereof

A manufacturing method and low-alloy technology, which is applied in the field of metal smelting, can solve problems such as low production efficiency, high cost, and low content of wear-resistant alloys, and achieve the effects of increasing service life, enhancing hardness, and improving wear resistance

Inactive Publication Date: 2018-08-14
TIANJIN RONGCHENG UNITED IRON & STEEL GRP CO LTD
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

On the other hand, although high-alloy steel balls have good wear resistance, since most of the high-alloy ball milling steels are die-cast, the production efficiency is low and the cost is high, which cannot meet the market demand at all. Therefore, it is urgent to develop a product with better wear resistance than Carbon steel ball with low alloy content, a new type of high wear-resistant steel ball suitable for industrial mass production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-carbon and low-alloy steel for grinding balls and manufacturing method thereof
  • High-carbon and low-alloy steel for grinding balls and manufacturing method thereof
  • High-carbon and low-alloy steel for grinding balls and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0039] The following is attached figure 1 The present invention is described in further detail.

[0040] A method for manufacturing steel for high-carbon and low-alloy grinding balls, comprising the following steps:

[0041] Step 1: In terms of mass percentage, 115t steel containing C0.73-0.83%, Si0.15-0.20%, Mn0.75-0.85%, Cr0.40-0.50%, P≤0.020%, S≤0.025% Add it into the converter for smelting, then add low nitrogen carbon powder, deoxidizer, silicomanganese, ferrosilicon, high carbon ferrochrome, titanium, copper, indium, gallium, nickel, zinc and tin into the converter in sequence, and the whole process is from the converter Argon is blown into the bottom of the furnace to control the oxygen pressure ≥ 0.8Mpa, and the end point of smelting is C ≥ 0.15%, P ≤ 0.015%. The amount added is 0.24% to 0.28% of the total weight of the materials charged into the converter;

[0042] Step 2: The molten steel tapped in Step 1 is transferred to the LF furnace for refining, and Ar is bl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses high-carbon and low-alloy steel for grinding balls. The steel comprises the following components, by mass percentage: 0.88-0.94% of C, 0.20-0.30% of Si, 0.90-1.00% of Mn, lessthan or equal to 0.025% of P, less than or equal to 0.025% of S, 0.50-0.60% of Cr, 0.010-0.050% of Ti, 0.20-0.30% of In, less than or equal to 0.25% of Cu, 0.080-0.100% of Ga, 0.20-0.26% of Ni, 0.10-0.14% of Zn, 0.14-0.16% of Sn and the balance Fe and inevitable impurities. The steel has the advantages that the production cost is relatively low, meanwhile, high-content carbon, manganese, tin, titanium and other elements are contained in the steel, so that the as-cast structure of the steel can be refined, and therefore the hardness of the grinding balls can be greatly improved, and good wear resistance of the grinding balls in the grinding process of an object with large hardness can be ensured; and in addition, high-content chromium is further contained in the steel, so that the grindingballs can also have relatively strong corrosion resistance, and therefore the grinding balls can be suitable for being used for grinding in a variety of fields.

Description

technical field [0001] The invention relates to the field of metal smelting, in particular to a steel for high-carbon and low-alloy grinding balls and a manufacturing method thereof. Background technique [0002] Wear-resistant steel is mainly used to manufacture various wear-resistant steel balls. Most of the traditional ball milling steels are carbon steel or high alloy steel. In recent years, with the rapid development of mining, construction, metallurgy, chemical industry, ceramics, energy, power plants and cement industries at home and abroad, the market demand for wear-resistant steel balls is increasing, and the working environment of steel balls is also increasing. The wear resistance of carbon steel balls can no longer meet the grinding requirements of the above industries. On the other hand, although high-alloy steel balls have good wear resistance, because most of the high-alloy ball milling steels are die-cast, the production efficiency is low and the cost is h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/50C22C38/42C22C38/02C22C38/04C22C33/04C21C7/10C21C7/072C21C7/00
CPCC22C38/50C21C7/0056C21C7/072C21C7/10C22C33/04C22C38/002C22C38/008C22C38/02C22C38/04C22C38/42
Inventor 包石磊梁加银顾龙
Owner TIANJIN RONGCHENG UNITED IRON & STEEL GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com