Electroplating anode phosphorus copper ball and preparation method thereof

A technology of phosphor bronze balls and anodes, which is applied in the direction of electrodes, etc., can solve the problems of low pressure resistance of hollow phosphor bronze balls, reduce the usage rate of phosphor bronze balls, and easily damage phosphor bronze balls, so as to improve electroplating production efficiency and save auxiliary equipment. The effect of raw materials and tight internal structure

Inactive Publication Date: 2018-08-17
江西江南新材料科技股份有限公司
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Solid phosphor bronze balls are prone to the following problems during electroplating: 1. Copper ions can only be released from the surface of phosphor bronze balls; 2. The generated anode slime will easily cover the surface of phosphor bronze balls to prevent the release of copper ions , reduce the utilization rate of phosphor bronze balls, and the waste is serious; 3. Because they are solid, the quality of phosphor bronze balls is heavy and the cost is high, while some hollow phosphor bronze balls have low compressive capacity and are easy to damage and phosphor bronze balls There are often uneven and dull phenomena. Therefore, it is necessary to invent an electroplated anodic phosphor copper ball and its preparation method to solve the above problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electroplating anode phosphorus copper ball and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The present invention provides such figure 1 An electroplated anode phosphor copper ball and its preparation method are shown, including a sphere 1, characterized in that: the inside of the sphere 1 is provided with a hollow groove 2, and the outside of the hollow groove 2 is surrounded by a reinforcement ring 3, and the reinforcement Protruding blocks 4 are arranged around the outside of the ring 3, and the number of the protruding blocks 4 is set in multiples, and the interval between the protruding blocks 4 is 2-4mm.

[0022] The present invention also provides a kind of preparation method of electroplated anode phosphor bronze ball, and its specific steps are:

[0023] (1) Add phosphor-bronze master alloy and copper raw materials into the reactor for heating. The heating temperature is 1300°C, and the heating time is 6h. During the heating process, it is continuously stirred. The stirring rate of the melt in the reactor during the heating process is 100r / min, stir ...

Embodiment 2

[0028] The present invention provides such figure 1 An electroplated anode phosphor copper ball and its preparation method are shown, including a sphere 1, characterized in that: the inside of the sphere 1 is provided with a hollow groove 2, and the outside of the hollow groove 2 is surrounded by a reinforcement ring 3, and the reinforcement Protruding blocks 4 are arranged around the outside of the ring 3, and the number of the protruding blocks 4 is set in multiples, and the interval between the protruding blocks 4 is 2-4 mm.

[0029] The present invention also provides a kind of preparation method of electroplated anode phosphor bronze ball, and its specific steps are:

[0030] (1) Put the phosphor copper master alloy and copper raw materials into the reactor for heating, the heating temperature is 1000°C, and the heating time is 8h. During the heating process, it is stirred continuously. The stirring rate of the melt in the reactor during the heating process is 60r / min, s...

Embodiment 3

[0035] The present invention provides such figure 1 An electroplated anode phosphor copper ball and its preparation method are shown, including a sphere 1, characterized in that: the inside of the sphere 1 is provided with a hollow groove 2, and the outside of the hollow groove 2 is surrounded by a reinforcement ring 3, and the reinforcement Protruding blocks 4 are arranged around the outside of the ring 3, and the number of the protruding blocks 4 is set in multiples, and the interval between the protruding blocks 4 is 2-4mm.

[0036] The present invention also provides a kind of preparation method of electroplated anode phosphor bronze ball, and its specific steps are:

[0037] (1) Add the phosphor copper master alloy and copper raw materials into the reactor for heating. The heating temperature is 1200°C, and the heating time is 7h. During the heating process, it is continuously stirred. The stirring rate of the melt in the reactor during the heating process is 80 / min, sti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an electroplating anode phosphorus copper ball and a preparation method thereof. The electroplating anode phosphorus copper ball comprises a ball body; a hollow groove is formed in the ball body; reinforcing rings are encircled around the outer side of the hollow groove; and projection blocks are encircled around the outer sides of the reinforcing rings. Hydrogen peroxide is added in a reaction kettle, and can oxidize copper powder to improve the phenomenon of looseness, unevenness and no luster of a cathode deposition layer caused by uniform deposition of Cu+ on a loose crystal and to improve the service life and the beauty of the phosphorus copper ball; through continuous stirring of melts, uniform distribution of phosphorus elements is guaranteed, so that the purposes of compact crystallizing particles and compact structure are achieved, and formation of monovalent copper ions is effectively inhibited; and phosphorus is proper in content and uniform in distribution, anode mud is less, and an anode bag is generally cleaned generally more than half a year, so that the electroplating production efficiency is improved, and such auxiliary raw materials as theanode bags are saved.

Description

technical field [0001] The invention relates to the field of phosphor bronze ball production, in particular to an electroplated anode phosphor bronze ball and a preparation method thereof. Background technique [0002] Phosphor bronze balls are mainly used in the electroplating of double-sided boards and multi-layer boards in printed circuit boards, in addition to electroplating in hardware and other industries. The production of phosphor bronze balls usually adopts the process of horizontal continuous casting to produce phosphor bronze balls and upward drawing method to produce phosphor bronze balls. Most of the existing phosphor bronze balls for electroplating are solid phosphor bronze balls. Solid phosphor bronze balls are prone to the following problems during electroplating: 1. Copper ions can only be released from the surface of phosphor bronze balls; 2. The generated anode slime will easily cover the surface of phosphor bronze balls to prevent the release of copper io...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C25D17/12C22C9/00C22C1/03B22D11/14B23P15/00
CPCC25D17/12B22D11/145B23P15/00C22C1/03C22C9/00
Inventor 徐上金
Owner 江西江南新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap