Antibacterial and flame-retardant HIPS composite material and preparation method thereof

A technology of composite materials and antibacterial agents, applied in the field of polymers, can solve problems such as inability to provide, and achieve the effect of improving the flame retardant effect and not reducing the impact performance

Active Publication Date: 2018-08-21
佛山市伟奇达新材料有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Mechanisms such as: protective film mechanism, otherwise gas mechanism, cooling mechanism, and termination chain reaction mechanism are given in existing textbooks. These can provide a vague direction for the selection of flame retardants, but they cannot provide real effective information. s help

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0030] A kind of preparation method according to above-mentioned antibacterial flame-retardant HIPS composite material, it is characterized in that, comprises the following steps:

[0031] (1) Put HIPS, PC, antibacterial agent, composite flame retardant, flame retardant synergist, antioxidant, and processing aid into the mixer and stir for 1-3 minutes to obtain mixed raw materials;

[0032] (2) Put the mixed raw material in step 2 and the mixing product in step 1 into a twin-screw extruder for reaction, and the material stays in the barrel for 1-2 minutes to obtain a reaction product. The twin-screw extruder The temperature of each zone is as follows: Zone 1 180-200℃, zone 2 200-220℃, zone 3 200-220℃, zone 4 200-220℃, zone 5 200-220℃, zone 6 200-220℃, zone 7 200- 220°C, eighth zone 200-220°C, nine zone 200-220°C, machine head 200-210°C.

[0033] (3) Cut the reaction product into pellets and dry to obtain the finished product.

Embodiment 1

[0035] An antibacterial and flame-retardant HIPS composite material is characterized in that, in parts by mass, it includes the following raw materials: 70 parts of HIPS, 15 parts of PC, 3 parts of antibacterial agent, 7.5 parts of composite flame retardant, 4 parts of flame-retardant synergist, 2 parts of antioxidants, 2 parts of processing aids; the compounded flame retardant is obtained by compounding dibenzothiophene-4-boronic acid, polyphosphate amine and silicone in a mass ratio of 3: 3:6. The antibacterial agent is obtained by compounding orpiment concentrate powder and chitosan at a mass ratio of 1:3.

[0036] The antibacterial agent is obtained by adding orpigo concentrate powder into chitosan glacial acetic acid solution, stirring evenly, volatilizing the solvent, and then drying. The flame retardant synergist is antimony trioxide. Described processing aid is stearamide lubricant. The antioxidant is a polybasic hindered phenol antioxidant. The silicone is polysilo...

Embodiment 2

[0042]An antibacterial and flame-retardant HIPS composite material is characterized in that, in parts by mass, it includes the following raw materials: 80 parts of HIPS, 10 parts of PC, 4 parts of antibacterial agent, 5 parts of composite flame retardant, 5 parts of flame-retardant synergist, 1 part of antioxidant, 3 parts of processing aids; the compound flame retardant is obtained by compounding dibenzothiophene-4-boronic acid, polyphosphate amine and silicone in a mass ratio of 2: 4: 4, and the The antibacterial agent is obtained by compounding orpiment concentrate powder and chitosan at a mass ratio of 1:4.

[0043] The antibacterial agent is obtained by adding orpigo concentrate powder into chitosan glacial acetic acid solution, stirring evenly, volatilizing the solvent, and then drying. The flame retardant synergist is antimony trioxide. The processing aid is silicone oil. The antioxidant is a polybasic hindered phenol antioxidant. The silicone is polysiloxane with a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an antibacterial and flame-retardant HIPS composite material and a preparation method thereof. The antibacterial and flame-retardant HIPS composite material comprises the following raw materials: HIPS, PC, an antibacterial agent, a composite flame retardant, a flame-retardant synergist, an antioxidant and a processing aid. The antibacterial and flame-retardant HIPS composite material and the preparation method thereof disclosed by the invention have the benefit that through optimizing components and dosages, a prepared product has excellent flame retardance and antibacterial effect under the premise that the impact resistance is not reduced.

Description

technical field [0001] The invention belongs to the technical field of polymers, and in particular relates to an antibacterial and flame-retardant HIPS composite material and a preparation method thereof. Background technique [0002] HIPS (High Impact Polystyrene) has high impact resistance but poor flame retardancy. In our country, the fire situation is also not optimistic, and some major fire accidents occur frequently. Most plastics are flammable substances, and plastic building materials, transportation materials, household appliances materials, etc. require plastic products not to burn, have good flame retardancy, and require plastics to have low smoke in a fire. For this reason, it is very important to choose to add flame retardants in plastic formulations. [0003] Requirements for flame retardants: (1) It must have good flame retardant function, and the flame retardant effect can be obviously achieved with a small amount; (2) The mechanical strength of the plastic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L51/04C08L69/00C08L83/04C08L5/08C08K13/02C08K5/55C08K3/32C08K3/30
CPCC08K2003/3009C08K2003/323C08L51/04C08L2201/02C08L2205/035C08L69/00C08L5/08C08L83/04C08K13/02C08K5/55C08K3/32C08K3/30
Inventor 徐菡
Owner 佛山市伟奇达新材料有限公司