Anti-aging HIPS foamed plastic

A foamed plastic, aging-resistant technology, applied in the polymer field, can solve the problems of cracking, poor weather resistance, mechanical properties decline, etc., and achieve the effect of synergistic improvement of aging resistance, excellent aging resistance, and improvement of aging resistance.

Pending Publication Date: 2021-02-05
姜丽丽
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, after HIPS products are exposed to sunlight, heat, and oxygen for a long time outdoors, they will turn yellow, become brittle, crack, lose luster on the surface, and greatly reduce their mechanical properties, and eventually lose their use value.
This is because the double bond contained in the butadiene component in the HIPS molecule is easily oxidized and degraded under the action of ultraviolet light, resulting in poor weather resistance. Changes, deterioration of physical and mechanical properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-aging HIPS foamed plastic

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] A kind of preparation method of above-mentioned anti-aging HIPS foamed plastic, it is characterized in that, comprises the following steps: (1) mix HIPS, PMMA, antibacterial agent, composite flame retardant, flame retardant synergist, antioxidant, processing aid Put the agent into the mixer and stir for 1-3 minutes to obtain the mixed raw material;

[0030] (2) Put the mixed raw material in step 2 and the mixing product in step 1 into a twin-screw extruder for reaction, and the material stays in the barrel for 1-2 minutes to obtain a reaction product. The twin-screw extruder The temperature of each zone is as follows: Zone 1 180-200℃, zone 2 200-220℃, zone 3 200-220℃, zone 4 200-220℃, zone 5 200-220℃, zone 6 200-220℃, zone 7 200- 220°C, eighth zone 200-220°C, nine zone 200-220°C, machine head 200-210°C.

[0031] (3) Squeeze the material in the twin-screw extruder into the HIPS foam molding mold, hold the pressure for 1 minute, and take out the HIPS foam molding after t...

Embodiment 1

[0033] An aging-resistant HIPS foamed plastic is characterized in that, in parts by mass, it comprises the following raw materials: 70 parts of HIPS, 15 parts of PMMA, 15 parts of PVC, 5 parts of inorganic anti-aging agent, 5 parts of organic anti-aging agent, and 10 parts of foaming agent 2 parts, 2 parts of fillers, 0.5 parts of antioxidant, 2 parts of processing aids; the inorganic anti-aging agent is conductive copper powder, nano-lanthanum oxide, and red mud is obtained by compounding in a mass ratio of 3:0.3:6, and the The organic anti-aging agent is obtained by compounding tetrabromobisphenol A and o-hydroxybenzophenone at a mass ratio of 1:3; the foaming agent is added with azodicarbonamide and hollow fibers at a ratio of 3:1.

[0034] The hollow fiber is a nylon 66 fiber with a hollow rate of 50%. The processing aid is a stearylamide lubricant. The antioxidant is a polybasic hindered phenol antioxidant. The filler is talcum powder.

[0035] A preparation method acc...

Embodiment 2

[0039] An aging-resistant HIPS foamed plastic, characterized in that, in parts by mass, it comprises the following raw materials: 60 parts of HIPS, 20 parts of PMMA, 10 parts of PVC, 6 parts of inorganic anti-aging agent, 3 parts of organic anti-aging agent, and 15 parts of foaming agent 1 part, 1 part of filler, 1 part of antioxidant, 1 part of processing aid; The inorganic anti-aging agent is conductive copper powder, nano-lanthanum oxide, and red mud is obtained by compounding in a mass ratio of 4:0.2:8, and the described The organic anti-aging agent is obtained by compounding tetrabromobisphenol A and o-hydroxybenzophenone at a mass ratio of 1:2; the foaming agent is added with azodicarbonamide and hollow fibers at a ratio of 4:1.

[0040] The hollow fiber is a nylon 66 fiber with a hollow rate of 30%. The processing aid is one or a mixture of stearylamide lubricants, silicone oil and white mineral oil. The antioxidant is a polybasic hindered phenol antioxidant. The fill...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-aging HIPS (high impact polystyrene) foamed plastic and a preparation method thereof. The anti-aging HIPS foamed plastic comprises the following raw materials: HIPS, PMMA (polymethyl methacrylate), PVC (polyvinyl chloride), an inorganic anti-aging agent, an organic anti-aging agent, a foaming agent, a filler, an antioxidant and a processing aid. According to the anti-aging HIPS foamed plastic and the preparation method thereof provided by the invention, by optimizing the components and dosage, the prepared product can have excellent anti-aging performance on thepremise of not reducing the impact resistance.

Description

technical field [0001] The invention belongs to the technical field of polymers, and in particular relates to an aging-resistant HIPS foamed plastic. Background technique [0002] The continuous bulk polymerization method of rubber grafted toughened polystyrene polymer, that is, HIPS resin, uses polybutadiene rubber or butadiene-styrene copolymer rubber as a toughening agent, and dissolves the toughening agent in a certain proportion Styrene and / or an appropriate amount of solvent, prepared by thermal initiation or initiator initiation. Literature (PengFM.Polybutadienegrafting and crosslinking in high-impact polystyrene bulkthermal process.Journal of Applied Polymer Science, 1990,40(7-8):1289-1302.) In the literature (PengFM.Polybutadienegrafting and crosslinking in high-impact polystyrene bulkthermal process.Journal of Applied Polymer Science,1990,40(7-8):1289-1302.), the thermal initiation of the bulk method for the preparation of HIPS resin polymerization kinetics detail...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L51/04C08L33/12C08L27/06C08K13/02C08K3/08C08K3/22C08K5/132C08K5/13C08J9/12C08J9/10
CPCC08J9/0023C08J9/0066C08J9/103C08J9/122C08J2203/06C08J2203/04C08J2433/12C08J2427/06C08J9/008C08J2351/04C08K13/02C08K2003/085C08K2201/001C08K2201/011C08K2003/221C08K5/132C08K5/13
Inventor 姜丽丽
Owner 姜丽丽