Aqueous acrylic acid-modified alkyd resin and preparation method thereof

A technology of water-based acrylic and alkyd resins, which is applied in coatings and other directions, can solve the problems of poor storage stability, water resistance and aging resistance of acrylic modified alkyd resins, and achieve excellent gloss and color retention Excellent film performance and low production cost

Active Publication Date: 2014-02-05
西北永新涂料有限公司
View PDF7 Cites 43 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The above four patents are respectively related to acrylic modified alkyd water-emulsion or water-soluble resins, but the formula design does not address the poor storage stability of acrylic modified alkyd resins, water resistance and aging resistance after single-component curing of resins into films Make special improvements for problems such as poor performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aqueous acrylic acid-modified alkyd resin and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] 1. Waterborne acrylic modified alkyd resin products

[0053] Prepare 30g of linoleic acid, 6g of benzoic acid, 11g of trimethylolpropane, 2g of pentaerythritol, 2g of maleic anhydride, 9g of isophthalic acid, 20g of ethylene glycol monobutyl ether, and 17g of butanol into a basic alkyd resin ; In this basic alkyd resin 46g, add styrene 9g, methyl methacrylate 11g, butyl acrylate 10g, acrylic acid 7g, vinyltriethoxysilane 1.2g, benzoyl peroxide 0.9g, tert-butyl Hydrogen peroxide 0.09g, ethylene glycol monobutyl ether 1.5g, dimethylethanolamine 7g and sodium metasilicate 1g were used to prepare water-based acrylic modified alkyd resin.

[0054] Two, the preparation method of waterborne acrylic acid modified alkyd resin:

[0055] Step A, preparation of basic alkyd resin:

[0056] The basic alkyd resin is prepared from the following quality raw materials: linoleic acid 30g, benzoic acid 6g, trimethylolpropane 11g, pentaerythritol 2g, maleic anhydride 2g, isophthalic acid ...

Embodiment 2

[0072] 1. Waterborne acrylic modified alkyd resin products

[0073] Prepare 35g of linolenic acid, 5g of benzoic acid, 12g of trimethylolpropane, 4g of pentaerythritol, 1.5g of maleic anhydride, 8g of isophthalic acid, 18g of ethylene glycol monobutyl ether, and 19g of butanol into basic alkyd Resin; In this basic alkyd resin 50g, add styrene 8g, methyl methacrylate 9g, butyl acrylate 11g, acrylic acid 8g, vinyltriisopropoxysilane 1.5g, benzoyl peroxide 1.1g, 0.11 g of tert-butyl hydroperoxide, 1.7 g of ethylene glycol monobutyl ether, 10 g of dimethylethanolamine, and 5 g of sodium metasilicate were prepared to obtain a water-based acrylic modified alkyd resin.

[0074] Two, the preparation method of waterborne acrylic acid modified alkyd resin:

[0075] Step A, preparation of basic alkyd resin:

[0076] The base alkyd resin is prepared from raw materials of the following qualities: linolenic acid 35g, benzoic acid 5g, trimethylolpropane 12g, pentaerythritol 4g, maleic anhy...

Embodiment 3

[0091] 1. Waterborne acrylic modified alkyd resin products

[0092] 33g of soy oil, 4g of benzoic acid, 10g of trimethylolpropane, 3g of pentaerythritol, 1g of maleic anhydride, 10g of isophthalic acid, 17g of ethylene glycol monobutyl ether, and 20g of butanol were prepared into a basic alkyd resin; 11 g of styrene, 7 g of methyl methacrylate, 8 g of butyl acrylate, 10 g of acrylic acid, 1.0 g of vinyltrimethoxysilane, 0.7 g of benzoyl peroxide, and 0.7 g of tert-butyl peroxide were added to 48 g of the basic alkyd resin. 0.1 g of hydrogen oxide, 1.9 g of ethylene glycol monobutyl ether, 8.5 g of dimethylethanolamine, and 1.5 g of sodium metasilicate were used to prepare a water-based acrylic modified alkyd resin.

[0093] Two, the preparation method of waterborne acrylic acid modified alkyd resin:

[0094] Step A, preparation of basic alkyd resin:

[0095] The basic alkyd resin is prepared from the following quality raw materials: 33g soy oil, 4g benzoic acid, 10g trimethy...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses aqueous acrylic acid-modified alkyd resin and a preparation method thereof. Basic alkyd resin of the aqueous acrylic acid-modified alkyd resin is prepared from an unsaturated fatty acid, benzoic acid, trimethylolpropane, pentaerythritol, maleic anhydride, isophthalic acid, ethylene glycol monobutyl ether and butanol. The aqueous acrylic acid-modified alkyd resin is prepared by adding styrene, methyl methacrylate, butyl acrylate, acrylic acid, a silane coupling agent, benzoyl peroxide, tert-butyl hydroperoxide, ethylene glycol monobutyl ether and a mixing neutralizer into the basic alkyd resin. According to the aqueous acrylic acid-modified alkyd resin and the preparation method thereof, the advantages of alkyd resin and acrylic resin are integrated, and a product has high gloss retention, color retention and weather resistance; a production process is simple, the raw materials are readily available, and the production cost is low; a paint production process is simple, water is used as a diluting agent, and safety and convenience in construction are ensured.

Description

technical field [0001] The invention relates to the field of synthesis of acrylic acid modified alkyd resin, in particular to a preparation method of waterborne acrylic acid modified alkyd resin. Background technique [0002] With the continuous advancement of science and technology and the continuous enhancement of people's awareness of environmental protection, systems that contain no or less volatile organic compounds (VOC) and no harmful air pollutants (HAP) have become the development direction of new materials. Solvent-based systems are gradually being replaced by water-based systems, and the promotion of water-based environmentally friendly materials has become an inevitable trend. Therefore, the development of water-based resins has been paid more and more attention by people. At present, the most successfully developed varieties mainly include: water-based acrylic resins, water-based epoxy ester resins, and water-based alkyd resins. [0003] Alkyd resin coatings ha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F283/01C08F212/08C08F220/14C08F220/18C08F220/06C08F230/08C08F8/44C08F8/42C08G63/49C08G63/91C09D151/08
Inventor 肖菲魏瑞平贾雪艳杨敬霞许玉霞李华明
Owner 西北永新涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com