PVC wood-plastic low-foaming particle material

A granular material and low-foaming technology, applied in the field of PVC wood-plastic low-foaming granular materials, can solve the problems of short service life, high maintenance costs, poor application effects, etc., achieve high weather resistance, reduce comprehensive cost, and formula cost low effect

Inactive Publication Date: 2018-09-04
GUILIN QUANZHOU LIAOYUAN SCI & TECH
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the main disadvantages of plastic wood products used outdoors are: easy to fade and whiten after long-term exposure to sunlight and rain, poor weather resistance; short service life, poor application effect, regular painting protection is required, and high maintenance costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A PVC wood-plastic low-foaming granular material, which is composed of the following components in parts by weight: 120 parts of polyvinyl chloride, 60 parts of bamboo powder, 10 parts of dispersant, 5 parts of initiator, 3 parts of buffering agent, foaming agent 1 part, 0.3 part of triallyl cyanurate, 4 parts of flame retardant, 0.1 part of coloring agent;

[0035] The preparation steps are as follows: (1) Take the raw materials according to the weight, put them into a high-speed mixer for mixing, and perform a pre-reaction at 100° C. to obtain the mixture;

[0036] (2) Import the mixture whose temperature reaches 100°C into the cooling mixer for further mixing and cooling; cool to 50°C;

[0037] (3) Input the mixture cooled to 50°C into the wood molding granulator for plasticization, and the plasticization temperature is controlled at 155°C;

[0038] (4) Extrude the plasticized wood-plastic mixed melt from a template with 20 to hundreds of through holes, and cut the ...

Embodiment 2

[0041] A PVC wood-plastic low-foaming granular material, which is composed of the following components in parts by weight: 130 parts of polyvinyl chloride, 65 parts of bamboo powder, 15 parts of dispersant, 8 parts of initiator, 5 parts of buffering agent, foaming agent 3 parts, 0.5 part of triallyl cyanurate, 6 parts of flame retardant, 0.3 part of coloring agent;

[0042] The preparation steps are as follows: (1) Take the raw materials according to the weight, put them into a high-speed mixer for mixing, and perform a pre-reaction at 100° C. to obtain the mixture;

[0043] (2) Import the mixture whose temperature reaches 100°C into the cooling mixer for further mixing and cooling; cool to 50°C;

[0044] (3) Input the mixture cooled to 50°C into the wood molding granulator for plasticization, and the plasticization temperature is controlled at 155°C;

[0045] (4) Extrude the plasticized wood-plastic mixed melt from a template with 20 to hundreds of through holes, and cut the...

Embodiment 3

[0048] A PVC wood-plastic low-foaming granular material, which is composed of the following components in parts by weight: 125 parts of polyvinyl chloride, 63 parts of bamboo powder, 11 parts of dispersant, 7 parts of initiator, 4 parts of buffering agent, foaming agent 2 parts, 0.4 part of triallyl cyanurate, 5 parts of flame retardant, 0.2 part of coloring agent;

[0049] The preparation steps are as follows: (1) Take the raw materials according to the weight, put them into a high-speed mixer for mixing, and perform a pre-reaction at 100° C. to obtain the mixture;

[0050] (2) Import the mixture whose temperature reaches 100°C into the cooling mixer for further mixing and cooling; cool to 50°C;

[0051] (3) Input the mixture cooled to 50°C into the wood molding granulator for plasticization, and the plasticization temperature is controlled at 155°C;

[0052] (4) Extrude the plasticized wood-plastic mixed melt from a template with 20 to hundreds of through holes, and cut the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a PVC wood-plastic low-foaming particle material which has the characteristics of light mass, high specific strength, water resistance, corrosion resistance and heat insulation and the characteristics of nailing, sawing and planing processing of wood. The PVC wood-plastic low-foaming particle material has very high weatherability and can be widely used for outdoors productmarkets such as exterior decoration of buildings, garden landscape, fences and walkways. The PVC wood-plastic low-foaming particle material has the significant characteristics of low formula cost andlow material density; and the comprehensive manufacturing cost of a product can be greatly lowered.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a PVC wood-plastic low-foaming granular material. Background technique [0002] PVC wood-plastic composite material is a new type of composite material that has been booming at home and abroad in recent years. It refers to the use of polyvinyl chloride, mixed with bamboo powder, rice husk, bamboo powder and other plant fibers to form new wood materials, and is prepared by mixing and granulating. composite particles. After extrusion, molding, injection molding and other plastic processing techniques, the plates or profiles are produced. PVC wood-plastic foaming materials are used as interior decoration materials, which have high requirements for flame retardancy and smoke suppression, in order to avoid fires, or minimize the personal and property losses caused by fire emergencies. At present, the main disadvantages of plastic wood products used outdoors are: easy to f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L97/02C08J9/04
CPCC08J9/04C08J2327/06C08J2497/02
Inventor 徐乐
Owner GUILIN QUANZHOU LIAOYUAN SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com