Antiskid paint

A technology of anti-slip coating and silicone, applied in the direction of coating, etc., can solve the problems of low service life, general light and heat aging resistance, etc., and achieve the effects of reducing wear, improving comprehensive mechanical properties, and uniform stress distribution

Inactive Publication Date: 2018-09-04
枞阳县三金颜料有限责任公司
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although it has a certain anti-skid effect, its light and heat aging resistance is average, and its service life is low when used outdoors.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A kind of non-slip coating, comprises the following steps to make:

[0021] (1) Preparation of modified silicone resin: After mixing the hyperbranched polymer and silicone resin in a mass ratio of 3.5:80, add a coupling agent of 0.12% by mass of the silicone resin, heat to 150°C, and heat at 2000r / min Stir at a rotating speed for 2 hours, then air-cool to room temperature to obtain;

[0022] (2) Filler: use sericite powder doped with 0.3wt% aminated graphene oxide;

[0023] (3) Finished product: uniformly mix the modified silicone resin 100 in step (1), filler 25 in step (2), dispersant 1, leveling agent 0.2, defoamer 0.5, and toluene 60 in parts by weight Together, stir at a speed of 3000r / min for 2 hours, and then grind for 40 minutes to obtain.

[0024] Further, the hyperbranched polymer in the step (1) is acrylated hyperbranched polyester (HBPA).

[0025] Further, the coupling agent in the step (1) is a titanate coupling agent.

[0026] Further, the air cooling ...

Embodiment 2

[0032] A kind of non-slip coating, comprises the following steps to make:

[0033] (1) Preparation of modified silicone resin: mix the hyperbranched polymer and silicone resin in a mass ratio of 3.5-3.8:80, then add a coupling agent of 0.12% of the mass of the silicone resin, heat to 150-160°C, Stir at 2000-2500r / min for 2-3 hours, then air-cool to room temperature to obtain;

[0034] (2) Filler: use sericite powder doped with 0.3-3.5wt% aminated graphene oxide;

[0035] (3) Finished product: 100-105 modified silicone resin in step (1), 25-30 filler in step (2), 1-3 dispersant, 0.2-1.5 leveling agent, defoaming agent in parts by weight 0.5-1.0 of the agent and 60-100 of toluene are evenly mixed together, stirred at 3000r / min for 2 hours, and then ground for 40 minutes to obtain the product.

[0036] Further, the hyperbranched polymer in the step (1) is acrylated hyperbranched polyester (HBPA).

[0037] Further, the coupling agent in the step (1) is a titanate coupling agent...

Embodiment 3

[0044] A kind of non-slip coating, comprises the following steps to make:

[0045] (1) Preparation of modified silicone resin: After mixing the hyperbranched polymer and silicone resin in a mass ratio of 3.6:80, add a coupling agent of 0.12% by mass of the silicone resin, heat to 155°C, and heat at 2200r / min Stir at a rotating speed for 2.5 hours, then air-cool to room temperature to obtain;

[0046] (2) Filler: use sericite powder doped with 1.5wt% aminated graphene oxide;

[0047](3) Finished product: uniformly mix the modified silicone resin 103 in step (1), filler 28 in step (2), dispersant 2, leveling agent 1.2, defoamer 0.8, and toluene 80 to Together, stir at a speed of 3000r / min for 2 hours, and then grind for 40 minutes to obtain.

[0048] Further, the hyperbranched polymer in the step (1) is acrylated hyperbranched polyester (HBPA).

[0049] Further, the coupling agent in the step (1) is a titanate coupling agent.

[0050] Further, the air cooling is air cooling ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an antiskid paint, which relates to the technical field of a paint. A preparation method of the paint comprises the following steps: 1) preparing modified organic silicone resin; 2) filling a material; and 3) obtaining a finished product. The antiskid performance of the paint can be guaranteed, and the adhesive force, weatherability, wear resistance and high temperature resistance of the paint can be greatly guaranteed.

Description

technical field [0001] The invention belongs to the technical field of coatings, and in particular relates to an anti-slip coating. Background technique [0002] Anti-slip coatings are mostly used in various public places, ship decks, workshop floors, homes, gardens, etc. to prevent slipping while walking. Its advantages are good adhesion, rough and effective anti-skid, and can be adapted to different places and different objects. Different anti-skid building materials are used. The disadvantage is that some anti-skid materials have poor environmental performance, are not friendly to the environment and affect the appearance of the building. Commonly used categories are phenolic, perchlorethylene, chlorinated rubber, epoxy, polyurethane, acrylic and the latest green environmental protection product - CPC anti-slip agent, etc., when using, add wear-resistant aggregates (river sand, corundum, cement and rubber) in proportion Plastic particles, etc.) can improve the anti-skid...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D183/10C09D7/62C09D7/61C08G77/445
CPCC08G77/445C08L2205/025C08L2205/035C09D7/61C09D7/62C09D183/10C08L83/04C08K13/06C08K9/04C08K3/042C08K3/34
Inventor 周艺桃
Owner 枞阳县三金颜料有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com