Waterborne wood paint with high weather resistance and production method of waterborne wood paint

A water-based wood lacquer and production method technology, applied in the direction of biocide-containing paint, antifouling/underwater paint, coating, etc., can solve the problems of difficult to meet outdoor use, poor weather resistance, loss of gloss, etc., and achieve excellent performance , excellent weather resistance, low pollution effect

Inactive Publication Date: 2018-09-28
东莞市家美环保涂料有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, when common water-based wood paints are used in outdoor environments, under the comprehensive damage caused by light, wind and rain, bacteria, etc., they are prone to loss of light, fading, yellowing, chalking, etc., that is, their weather resistance Poor, difficult to meet outdoor use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Each raw material is weighed so that the parts by weight of each raw material are as follows: 30 parts of water-based acrylic resin, 15 parts of water-based polyurethane resin, 0.3 part of defoamer, 0.2 part of substrate wetting agent, 2 parts of dipropylene glycol butyl ether, dipropylene glycol 2 parts of methyl ether, 1 part of dodecyl alcohol ester, 0.5 part of Casson antifungal agent, 0.3 part of wetting agent, 1 part of water repellent agent, 1 part of water repellent, 1 part of dry film antifungal agent, polysiloxane 0.1 part, 0.2 part of leveling agent, 0.3 part of hindered amine light stabilizer, 0.5 part of ultraviolet absorber, 0.2 part of polyurethane tackifier, 0.3 part of acrylic tackifier, 10 parts of deionized water.

[0030] The preparation method of the water-based wood paint with high weather resistance comprises the following steps:

[0031] Step a, add deionized water, dipropylene glycol butyl ether, dipropylene glycol methyl ether, dodecyl alcohol ...

Embodiment 2

[0042] Each raw material is weighed so that the parts by weight of each raw material are as follows: 40 parts of water-based acrylic resin, 25 parts of water-based polyurethane resin, 0.7 part of defoamer, 1 part of substrate wetting agent, 5 parts of dipropylene glycol butyl ether, dipropylene glycol 4 parts of methyl ether, 3 parts of dodecyl alcohol ester, 1 part of Casson antifungal agent, 0.6 parts of wetting agent, 2 parts of water repellent agent, 3 parts of water repellent, 3 parts of dry film antifungal agent, polysiloxane 0.5 parts, 0.5 parts of leveling agent, 0.8 parts of hindered amine light stabilizer, 1 part of ultraviolet absorber, 0.5 parts of polyurethane tackifier, 0.8 parts of acrylic tackifier, 20 parts of deionized water.

[0043] The preparation method of the water-based wood paint with high weather resistance comprises the following steps:

[0044] Step a, add deionized water, dipropylene glycol butyl ether, dipropylene glycol methyl ether, dodecyl alco...

Embodiment 3

[0055] Each raw material is weighed so that the parts by weight of each raw material are as follows: 35 parts of water-based acrylic resin, 20 parts of water-based polyurethane resin, 0.5 part of defoamer, 0.6 part of substrate wetting agent, 3 parts of dipropylene glycol butyl ether, dipropylene glycol 3 parts of methyl ether, 2 parts of dodecyl alcohol ester, 0.8 parts of Casson antifungal agent, 0.5 parts of wetting agent, 1.5 parts of water repellent agent, 2 parts of water repellent, 2 parts of dry film antifungal agent, polysiloxane 0.3 parts, 0.4 parts of leveling agent, 0.6 parts of hindered amine light stabilizer, 0.7 parts of ultraviolet absorber, 0.3 parts of polyurethane tackifier, 0.5 parts of acrylic tackifier, 15 parts of deionized water.

[0056] The preparation method of the water-based wood paint with high weather resistance comprises the following steps:

[0057] Step a, add deionized water, dipropylene glycol butyl ether, dipropylene glycol methyl ether, do...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a waterborne wood paint with high weather resistance and a production method of the waterborne wood paint. The waterborne wood paint with high weather resistance comprises thefollowing raw materials in parts by weight: 30-40 parts of waterborne acrylic resin, 15-25 parts of waterborne polyurethane resin, 0.3-0.7 part of defoaming agent, 0.2-1 part of substrate wetting agent, 2-5 parts of dipropylene glycol monobutyl ether, 2-4 parts of dipropylene glycol methyl ether, 1-3 parts of 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate, 0.5-1 part of kathon mildewcide, 0.3-0.6part of wetting agent, 1-2 parts of water repellent, 1-3 parts of waterproof agent, 1-3 parts of dry film mildewcide, 0.1-0.5 part of polysiloxane, 0.2-0.5 part of flatting agent, 0.3-0.8 part of hindered amine light stabilizer, 0.5-1 part of ultraviolet light absorber, 0.2-0.5 part of polyurethane tackifier, 0.3-0.8 part of acrylic tackifier and 10-20 parts of deionized water.

Description

technical field [0001] The invention relates to the field of wood lacquer design, in particular to a water-based wood varnish with high weather resistance. Background technique [0002] Wood paint refers to a type of resin paint used on wood products, including polyester and polyurethane paints. In the past, most of the wood lacquers were oil-based wood lacquers, but oil-based wood lacquers required the use of organic solvents, such as "thinna water" or "banana water", which caused serious environmental pollution and easily caused great damage to users, and were easy to burn. In order to solve the above-mentioned problems of oil-based wood lacquers, there are currently many water-based wood lacquers on the market that use water as a solvent. Because water-based wood lacquers are non-toxic, environmentally friendly, odorless, have very little volatile matter, and are non-flammable and non-explosive. High safety With the enhancement of people's awareness of environmental pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D5/14C09D7/63C09D7/65C08J3/00
CPCC09D133/00C08J3/005C08J2333/00C08J2475/04C08J2483/04C08L2201/08C08L2205/025C08L2205/035C09D5/14C09D7/63C09D7/65C08L75/04C08L83/04C08L91/06C08K5/47C08K5/053
Inventor 张词典
Owner 东莞市家美环保涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com