Jianzhan porcelain reduction bar as well as preparation method and Jianzhan porcelain firing method thereof

A technology of roasting and rosinic acid, which is applied to clay products, other household utensils, solid fuels, etc., can solve the problems that affect the quality stability of Jianzhan finished products, the composition of pine wood cannot be guaranteed to be consistent, and the combustion conditions are different, etc., to achieve glass Good chemical effect, good flammability, and high yield

Active Publication Date: 2018-09-28
谢松青
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since pine wood is mined naturally, its components are unstable, and the content of pine wood, turpentine and other components is uncertain. The same weight of pine wood cannot guarantee that its components are consistent, or even have a large difference.
In this way, when the pine wood is put into the kiln, under the same furnace temperature, the combustion conditions are different, which is likely to cause fluctuations in the reducing atmosphere and affect the stability of the quality of the finished product.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Jianzhan reducing stick is made from the following components in parts by weight: 40 parts of turpentine, 10 parts of rosinic acid, 10 parts of turpentine, 20 parts of pine wood powder, 5 parts of wild loquat root powder, 5 parts of red stone sticky powder, 5 parts of elm bark powder, 5 parts of corn starch, 10 parts of charcoal powder, 20 parts of water.

[0034] Described pine resin, rosinic acid are in powder form, and the mesh number of described rosin, rosinic acid, wild loquat root powder, red stone sticky powder, elm bark powder, cornstarch, charcoal powder is 100 orders; The mesh number of described pine wood powder The number is 80 mesh.

[0035] The preparation method of the above-mentioned Jianzhan reducing rod comprises the following steps:

[0036] (1) Mix rosinic acid, pine wood powder, wild loquat root powder, red stone sticky powder, elm bark powder, corn starch, and charcoal powder, add to the mixer and stir at 40 rpm for 2 hours;

[0037] (2) Pine re...

Embodiment 2

[0049] Jianzhan reducing stick is made from the following components in parts by weight: 42 parts of turpentine, 12 parts of rosinic acid, 8 parts of turpentine, 22 parts of pine wood powder, 6 parts of wild loquat root powder, 4 parts of red stone sticky powder, 6 parts of elm bark powder, 4 parts of cornstarch, 13 parts of charcoal powder, 22 parts of water.

[0050] The rosin and rosinic acid are in powder form, and the mesh number of the rosin, rosinic acid, wild loquat root powder, red stone sticky powder, elm bark powder, cornstarch, and charcoal powder is 90 mesh; the mesh of the pine wood powder The number is 75 mesh.

[0051] The preparation method of the above-mentioned Jianzhan reducing rod comprises the following steps:

[0052] (1) Mix rosinic acid, pine wood powder, wild loquat root powder, red stone sticky powder, elm bark powder, corn starch, and charcoal powder, add to the mixer and stir at 50rpm for 1.8h;

[0053](2) Pine resin and water are mixed and refin...

Embodiment 3

[0065] Jianzhan reducing stick is made by including the following components in parts by weight: 38 parts of turpentine, 7 parts of rosinic acid, 12 parts of turpentine, 17 parts of pine wood powder, 4 parts of wild loquat root powder, 6 parts of red stone sticky powder, 4 parts of elm bark powder, 6 parts of cornstarch, 8 parts of charcoal powder, 18 parts of water.

[0066] Described pine resin, rosinic acid are in powder form, and the mesh number of described rosin, rosinic acid, wild loquat root powder, red stone sticky powder, elm bark powder, cornstarch, charcoal powder is 110 orders; The mesh number of described pine wood powder The number is 90 mesh.

[0067] The preparation method of the above-mentioned Jianzhan reducing rod comprises the following steps:

[0068] (1) Mix rosinic acid, pine wood powder, wild loquat root powder, red stone sticky powder, elm bark powder, corn starch, and charcoal powder, add to the mixer and stir at 45 rpm for 2.3 hours;

[0069] (2) ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
weightaaaaaaaaaa
Login to view more

Abstract

The invention discloses a Jianzhan porcelain reduction bar as well as a preparation method and a Jianzhan porcelain firing method thereof. The Jianzhan porcelain reduction bar is prepared from the following components in parts by weight: 38-42 parts of rosin, 7-13 parts of abietic acid, 8-12 parts of oil of turpentine, 17-23 parts of pine wood flour, 4-6 parts of wild loquat root powder, 4-6 partsof red-stone sticky powder, 5-7 parts of elm bark powder, 4-7 parts of corn starch, 8-13 parts of charcoal dust and 18-22 parts of water. The Jianzhan porcelain reduction bar disclosed by the invention is stable in component and excellent in combustibility. A certain amount of Jianzhan porcelain reduction bar is added in a Jianzhan porcelain firing process according to needs, combustion conditions and a reducing atmosphere in a kiln can be accurately controlled, the quality stability of the finished Jianzhan porcelain is greatly improved, and hare's fur or oil drop Jianzhan porcelain with beautiful stripes can be conveniently fired.

Description

technical field [0001] The invention relates to a firing process of porcelain, in particular to a firing method of Jianzhan. Background technique [0002] China is the hometown of porcelain, and porcelain is an important creation of the Chinese working people. Jianzhan is a typical representative of black-glazed porcelain. Black-glazed porcelain has been fired very early in my country. It can be traced back to the Eastern Han Dynasty, and Jianzhan reached its peak in the Song Dynasty. Jianzhan is produced in Shuiji Town, Jianyang District, Nanping City, Fujian Province. Jianzhan occupies a place in Chinese porcelain because of its simple shape, unpredictable and colorful glaze color, which fully displays the magic and depth of black porcelain. [0003] There are many processes in the manufacture of Jianzhan, mainly including body and glaze preparation, casting, trimming, biscuit firing, glazing and roasting. Among them, the most important step is roasting. The quality of t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C10L5/44C04B33/04C03C8/00C04B41/86
CPCC03C8/00C03C2204/04C04B33/04C04B41/009C04B41/5022C04B41/86C10L5/44C10L5/442Y02E50/10Y02E50/30
Inventor 谢松青廖坤
Owner 谢松青
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap