High-strength ceiling material and preparation method thereof

A ceiling and high-strength technology, which is applied in the field of high-strength ceiling materials and its preparation, can solve the problems of easy powdery fracture resistance and other problems, and achieve the goals of improving friability, improving comprehensive performance, improving strength and corrosion resistance Effect

Inactive Publication Date: 2018-10-09
合肥永泰新型建材有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the gypsum ceiling also has the disadvantages of easy powdery cracking and poor bending resistance after reprocessing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A high-strength ceiling material, comprising the following raw materials in parts by weight:

[0026] 35 parts of modified phenolic resin, 8 parts of polytetrafluoroethylene, 8 parts of silica fume powder, 6 parts of hollow glass microspheres, 6 parts of sepiolite fiber, 3 parts of tourmaline powder, 3 parts of zinc borate, 2 parts of nano zinc oxide, 4 parts of expanded graphite, 6 parts of diatomaceous earth, 20 parts of coconut shell powder, 5 parts of bamboo charcoal powder, 4 parts of barley green pigment, 3 parts of nano-titanium dioxide, 4 parts of carbon nanotubes, 1.5 parts of silane coupling agent, 1.2 parts of antioxidant and 1.8 parts of flame retardant;

[0027] The preparation of modified phenolic resin comprises the following steps:

[0028] Stir and mix the phenolic resin and N-(4-hydroxyphenyl)maleimide corresponding to 5% of its weight evenly, heat up to 90 degrees Celsius, and react with stirring at a speed of 600 rpm for 20 minutes, slowly equivalen...

Embodiment 2

[0041] A high-strength ceiling material, comprising the following raw materials in parts by weight:

[0042] 45 parts of modified phenolic resin, 15 parts of polytetrafluoroethylene, 15 parts of silica fume powder, 12 parts of hollow glass microspheres, 12 parts of sepiolite fiber, 6 parts of tourmaline powder, 6 parts of zinc borate, 4 parts of nano zinc oxide, 8 parts of expanded graphite, 12 parts of diatomaceous earth, 30 parts of coconut shell powder, 10 parts of bamboo charcoal powder, 8 parts of barley green pigment, 7 parts of nano-titanium dioxide, 8 parts of carbon nanotubes, 3.2 parts of silane coupling agent, 2.5 parts of antioxidant and 3.6 parts of flame retardant;

[0043] The preparation of described modified phenolic resin comprises the following steps:

[0044] Stir and mix the phenolic resin and N-(4-hydroxyphenyl)maleimide corresponding to 5% of its weight evenly, heat up to 110 degrees Celsius, and react with stirring at a speed of 1000 rpm for 30 minutes...

Embodiment 3

[0057] A high-strength ceiling material, comprising the following raw materials in parts by weight:

[0058] 40 parts of modified phenolic resin, 12 parts of polytetrafluoroethylene, 12 parts of silica fume powder, 10 parts of hollow glass microspheres, 10 parts of sepiolite fiber, 4.5 parts of tourmaline powder, 4.5 parts of zinc borate, 3 parts of nano zinc oxide, 6 parts of expanded graphite, 10 parts of diatomaceous earth, 25 parts of coconut shell powder, 8 parts of bamboo charcoal powder, 6 parts of barley green pigment, 5 parts of nano-titanium dioxide, 6 parts of carbon nanotubes, 2.6 parts of silane coupling agent, 1.8 parts of antioxidant And 2.8 parts of flame retardant.

[0059] The preparation of modified phenolic resin comprises the following steps:

[0060] Stir and mix the phenolic resin and N-(4-hydroxyphenyl)maleimide corresponding to 5% of its weight evenly, heat up to 100 degrees Celsius, and react with stirring at a speed of 800 rpm for 25 minutes. 30% h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-strength ceiling material and a preparation method thereof. The high-strength ceiling material comprises the following raw materials in parts by weight: 35-45 parts of modified phenolic resin, 8-15 parts of polytetrafluoroethylene, 8-15 parts of silica fume, 6-12 parts of hollow glass beads, 6-12 parts of sepiolite fibers, 3-6 parts of tourmaline powder, 3-6 parts ofzinc borate, 2-4 parts of nano-zinc oxide, 4-8 parts of expanded graphite, 6-12 parts of diatomite, 20-30 parts of coconut shell flour, 5-10 parts of bamboo charcoal powder, 4-8 parts of barley green, 3-7 parts of nano-titania, 4-8 parts of carbon nano tubes, 1.5-3.2 parts of a silane coupling agent, 1.2-2.5 parts of an antioxidant and 1.8-3.6 parts of a flame retardant. According to reasonable ratio synergism of the raw materials, the ceiling material disclosed by the invention has excellent bending strength and pressure resistance, is high in strength, easy to process, green and environmental-friendly, and has an effect of refreshing air.

Description

technical field [0001] The invention relates to the field of ceiling materials, in particular to a high-strength ceiling material and a preparation method thereof. Background technique [0002] Ceilings are used as interior roof decoration materials. In the past, straw mats, reed mats, and wooden boards were used as the main materials in traditional houses. With the advancement of technology, more building materials have been applied. The ceilings commonly used in the prior art are mainly gypsum ceilings. The gypsum ceilings have the advantages of light weight, sound absorption and non-combustibility, and the materials are cheap and the decoration is elegant. However, the gypsum ceiling has the disadvantages of easy powdery cracking and poor bending resistance after reprocessing. Contents of the invention [0003] Aiming at the problems existing in the prior art, the present invention provides a high-strength ceiling material and its preparation method. The ceiling materi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L61/14C08L27/18C08L97/02C08K13/06C08K9/06C08K3/34C08K7/24C08K7/26C08K3/04C08K7/28C08K7/10C08K3/38C08K3/22C08G8/32
CPCC08L61/14C08G8/32C08K2003/2296C08K2003/387C08K2201/011C08K2201/014C08L2205/03C08L27/18C08L97/02C08K13/06C08K9/06C08K3/34C08K7/24C08K7/26C08K3/04C08K7/28C08K7/10C08K3/38C08K3/22C08K3/041
Inventor 伍志远
Owner 合肥永泰新型建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More